Twinjection Technology Improves Hot Metal Desulphurisation at Corus Scunthorpe Works

Similar documents
ThyssenKrupp Industrial Solutions. Our new name is. Metallurgical Injection Technology.

Over the past few decades the demand for steel

THE LEADING HOT METAL DESULFURIZATION METHODS: A COMPARISON BETWEEN KR, MMI AND CO-INJECTION*

Sulphur Problem. AkMB Rashid Professor, Department of MME BUET, Dhaka. Today s Topics

Efficient, Economical & Ecological Hot Metal Desulphurisation Solution for Iron and Steel Industries

Part III: Slag Practices and Oxygen/Carbon Injection when Melting Direct Reduced Iron

DEPHOSPHORIZATION AND DESULFURIZATION OF MOLTEN DUCTILE IRON AND ITS EFFECT ON DUCTILITY

Secondary Steelmaking 1 Synthetic slag practice, injection ladle metallurgy, deoxidation

Phosphorous Problem. AkMB Rashid Professor, Department of MME BUET, Dhaka

Lecture 17 Alternative Charge Materials in EAF

A.K. LAHIRI. Thermodynamics of refining in electric furnace steelmaking

RECENT PROGRESS. INTERNAL HOT METAL DESULPHURIZATION BY MULTI-INJECTION AT THYSSENKRUPP STAHL AG s (TKS) STEELWORKS

Lecture 23: Injection ladle metallurgy

Lecture 14 Modern trends in BOF steelmaking

Reduce Furnace Energy Consumption Using Calumite

Improvement of Flux Reaction Efficiency in Steel Refining

On-line Sulphur Immersion Sensor Improves Hot Metal Desulphurization Process

The steel plant of today is exposed to an ever-growing

Pyrometallurgy of iron is still the most important pyrometallurgical process economically.

REFINING STEELS PRODUCED IN ELECTRIC ARC FURNACE

SECONDARY STEELMAKING

Lecture 12 Converter Steelmaking Practice & combined blowing. Key words: Top blown steelmaking, combined blowing, bottom stirring, hot metal refining

Lecture 25: Principles of degassing

EAF Technology and process

AN OVERVIEW OF TREATMENT OF STEEL- MAKING SLAG FOR RECOVERY OF LIME AND PHOSPHORUS VALUES

Thermodynamic database of P 2 O 5 -containing oxide system for De-P process in steelmaking

Metallurgy and lining life in basic oxygen converters

Briquette Smelting in Electric Arc Furnace to Recycle Wastes from Stainless Steel Production

RECYCLING PRACTICES OF SPENT MgO-C REFRACTORIES

Steel Making Prof. Deepak Mazumdar Prof. S. C. Koria Department of Materials Science and Engineering

THE EFFECT OF QUALITY OF FERROUS BURDEN MATERIALS ON THE QUALITY OF PIG IRON

MGO-C REFRACTORY SELECTION AND EVALUATION FOR STEELMAKING VESSELS. J Terblanche Arcelormittal

Ferrochromium in Converter Practice

Advanced vision systems to control ladle slag carry-over

Effect of B 2 O 3 on Melting Temperature, Viscosity and Desulfurization Capacity of CaO based Refining Flux

Carbide Capacity of CaO SiO 2 CaF 2 ( Na 2 O) Slags at K

Custom-Designed Fluxes for Refining Nickel Alloys

Services to the Steel Industry - Independent research, consultancy, technical support, pilot and up-scaling services to the steel industry worldwide.

Improvement in Blast Furnace Reaction Efficiency Through the Use of Catalyst-doped Highly Reactive Coke

PYROMETALLURGY OF IRON

In conjunction with MJAC Midland Joint Advisory Council for Environmental Protection. Present. Advanced Module IV

Oxidation of Iron, Silicon and Manganese

REFINING OF FERRO-SILICON

Steel Making Prof. Deepak Mazumdar Prof. S. C. Koria Department of Materials Science and Engineering

Thermodynamic determination of low melting area in CaO-Al 2 O 3 -SiO 2 -MgO-MnO system inclusion and its control in spring steel

Characterization of Metal Droplets in Slag after Desulfurization of Hot Metal

IRON AND STEEL INDUSTRY DEVELOPMENT AND TECHNOLOGICAL INNOVATION IN CHINA

Lecture 21: Evolution of ladle Treatment and Requirements

Topic 2.7 EXTRACTION OF METALS. Extraction of Iron Extraction of Aluminium Extraction of Titanium Recycling

Can Fluorspar be replaced in steelmaking? Eugene Pretorius Baker Refractories

2.7 EXTRA QUESTIONS MS. heat or C (1) 2 (b) electrolysis (1) molten or with cryolite (1) 2 [4]

TUNDISH METALLURGICAL PRACTICES FOR SLAB PRODUCTION IN BOKARO STEEL

Module - 02 Lecture - 06 Limitation of Primary Steelmaking & Importance of secondary Refining

Advanced Master Course Process Technology of Metals

Integrated Pollution Prevention and Control (IPPC) Reference Document on Best Available Techniques in the Cement and Lime Manufacturing Industries

Trial of capillary refining by porous CaO with molten slag

Fundamental Study of Sn Removal from Hot Metal by NH 3 Gas Blowing

Analysis of parameters affecting end blow manganese content at oxygen steelmaking

Investigating the Effect of Coal Mineral Matter on Blast Furnace Coal Injection

Sulphur bonding in solidified ladle slags

The HIsarna Ironmaking Process

Unique functions of slags in steelmaking

Hot Rolled Products Analyst Site Visit Port Kembla

The necessity of hot metal desiliconization process

Influence of hydrogen in weld joints

Lecture 36 CHEMICAL REACTION IN WELDS II

EFFECT OF CHROME ORE QUALITY ON FERROCHROME PRODUCTION EFFICIENCY

THE INFLUENCE OF BRIQUETTED SYNTHETIC SLAGS ON STEEL REFINING IN LADLE

The economics of electric arc furnace (EAF) technology

Experimental and mathematical modeling studies on primary hot metal desulfurization

Study on reduction behavior of molybdenum trioxide in molten steel

Innovations in Iron and Steel at JSW Steel Ltd

Control of sulphur and minimisation of centre line segregation for Rail Steel

Summary of findings from HYBRIT Pre-Feasibility Study

Effect of MgO and Al 2 O 3 variations in oxygen steelmaking (BOF) slag on slag morphology and phosphorus distribution

Volume Issue 3 POSSIBILITIES FOR THE UTILISATION OF STEELMAKING SLAGS FOR THE PRODUCTION OF SLAG-FORMING MATERIALS

Use of DRI in EAF s. Gregory L. Dressel Dressel Technologies Pawleys Island, SC. Part II: Feeding and Melting of Direct Reduced Iron.

Technology Improving Your Meltshop Performance

Lecture 42: Self Assessment questions. 1a) Explain the role of a basic oxidising slag in steelmaking. (04)

Effect of Silicon Carbide on Reactions between Molten Steel and Fused Magnesia Silicon Carbide Composite Refractory

Reduction in Charge Requirements of Hismeltiron-Making Process in Indian Context

Electric Arc Furnace Simulation User Guide Version 1

GENERAL PRINCIPLES AND PROCE ISOLATION ISOL ELEMENTS

not to be republished NCERT GENERAL PRINCIPLES AND PROCE ISOLATION ISOL ELEMENTS Unit I. Multiple Choice Questions (Type-I)

Shaun Moss Mars Society Australia June 2006

Acta Metallurgica Slovaca - Conference, Vol. 4, 2014, p Acta Metall. Slovaca Conf. 138

Trial on the Applicaton of Capillary Phenomenon of Solid CaO to Desulfurization of Liquid Fe

REDUCTION OF IRON ORE PELLETS BY STATISTICAL DESIGN OF EXPERIMENTS

Oxygen Technologies: Reduce Melting Cost and Emissions. * Air Products GmbH, Germany, ** Air Products plc, UK.

REDUCING REFRACTORY COST USING NEW ASCC BRICKS FOR HOT IRON TRANSPORT

PILOT PLANT PRODUCTION OF FERRONICKEL FROM NICKEL OXIDE ORES AND DUSTS IN A DC ARC FURNACE. Abstract

Conversion of CO 2 Gas to CO Gas by the Utilization of Decarburization Reaction during Steelmaking Process

Peter Zonneveld, MD Danieli Corus. Innovative Technologies in Modern Sustainable Steel Making

Stainless Steelmaking

Slags in Production of Manganese Alloys

Functions of Mg and Mg-CaO mixtures in hot metal desulfurization

Reduction of FeO in Molten Slags by Solid Carbon in. the Electric Arc Furnace Operation*

The Recycling of Materials Containing Iron and Zinc in the OxyCup Process

< > The Experience of ArcelorMittal Lázaro Cardenas Flat Carbon. By R. Lule 1), F.Lopez 2), J. Espinoza 3) R. Torres 4) & R.D.


Transcription:

Twinjection Technology Improves Hot Metal Desulphurisation at Corus Scunthorpe Works Dr. Robert Robey, Process Metallurgist, Mark Whitehead, Manager - Technical Sales, SMS Mevac UK Limited, Winsford, UK; Gareth Parker, Process Technologist, Helen Thomson, Process Technologist, Corus Construction & Industrial, Scunthorpe, UK (Published in MPT International, 2009, Issue 5, pp24-28) Abstract Powder injection times for hot metal desulphurisation have been dramatically cut by up to 50% at Corus Scunthorpe by the modernisation of the plant using Twinjection technology. Twinjection technology introduces two powder streams into the hot metal down a single refractory lance. Lower sulphur levels can now be achieved using co-injection of lime and magnesium in a fraction of the previous injection times. This allows Corus to increase the proportion of low sulphur steels that can be made through the plant and makes it possible, should the need arise, to cope with higher incoming hot metal sulphur levels without reducing production rates. Introduction The Scunthorpe works of Corus has recently upgraded its hot metal desulphurisation facilities using the Twinjection technology of SMS Mevac. Desulphurisation of molten iron was first achieved at Scunthorpe, in 1973, by the injection of calcium carbide (CaC 2 ) into the torpedoes delivered from the blast furnaces. The efficiency of the process was improved in 1979 when desulphurisation was carried out in the iron transfer ladle, still using CaC 2. Then, in 1982, the process was further improved by moving to the deep injection of a magnesium based premixed powder, containing approximately 80% magnesium as well as some Al 2 O 3 and MgO. The injection of the magnesium powder was achieved by carrying the Mg in a stream of nitrogen gas down a channel in a refractory lance that was inserted into the molten iron with the tip located at about three quarters of the depth of the melt. After a refinement to reduce over injection of the reagent in 1989, the plant served the needs of Corus for hot metal desulphurisation to the present day with a typical injection time of 20 minutes, but with much longer times being required to achieve a final hot metal sulphur level of 0.002%. At Corus Scunthorpe Works, the rated liquid steel production is 4.8 million tonnes per annum (Mtpa), but traditionally output has fallen significantly short of this rated capacity due to the type of products that are being produced at the plant [1]. The product mix that is produced can significantly affect the tonnage leaving the BOS plant [2] and as the demand for low sulphur products increases, the desulphurisation process was identified as a potential bottleneck for the plant. The primary reason for investment in the desulphurisation facilities was to give consistent high throughput of hot metal at low final sulphur levels. A further benefit was to achieve a dust emission reduction to the local atmosphere by upgrading the fume extraction system at the same time. SMS Mevac was selected to design, install and commission the modernised desulphurisation facility. Hot Metal Desulphurisation It has long been recognised that desulphurisation of liquid iron before the primary steelmaking stage is the most cost effective method to produce low sulphur steels. It can also make the 1

iron-making stage more economic in that the sulphur limit imposed on blast furnace operations can be more relaxed. Various reagents have been adopted throughout the world to effect sulphur removal from liquid iron. The most common reagents have included soda ash (Na 2 CO 3 ), calcium carbide (CaC 2 ), lime (CaO) and magnesium (Mg). These reagents can be used on their own or, more often, in combination. The use of soda ash, as a desulphurising agent, is very much reduced in modern steelmaking due to the decomposition products that were produced in contact with liquid iron and the water soluble slag products that could cause environmental management difficulties. Modern steelmakers now use Na 2 CO 3 sparingly, such as in combination with other reagents as a slag flux to help reduce iron losses during deslagging operations at the end of desulphurisation. For the other reagents, the extent of desulphurisation depends on the following reactions: Mg + S MgS 2CaO + 2S + Si 2CaS + SiO 2 CaC 2 + S CaS + C CaO + Mg + S CaS + MgO Deep injection of reagents into liquid iron was developed by injecting a powder of that reagent, with a suitable grain size for conveyance by pneumatic means, near to the bottom of a ladle. Typically an inert gas, usually nitrogen, is used as the transport media for the powder. A refractory coated lance is brought towards the surface of the molten iron and the transport gas flow is established. Prior to entering the liquid iron, the powder flow is established from a fluidised dispenser along a channel inside a refractory coated lance. Once the powder flow is established the lance can then be inserted into the liquid iron and lowered to a pre-defined height in the ladle. Once at the pre-defined height the powder flow rate can be increased to the flow rate appropriate for that powder and a combination of powder and inert gas is injected into the iron. The carrier gas acts as a stirring media as the bubbles expand and rise to the surface. In addition to the active desulphurising reagent, other compounds may be added to aid the stirring of the melt. For the case of CaC 2, small amounts of volatile additions may be made to improve the reaction rate of the reagent. Magnesium needs no additional stirring agents, since the melting point of Mg (at around 650 C) and the boiling point (at 1107 C) are both below the temperature of liquid iron. In fact, Mg rapidly melts and gasifies, producing a vigorous stirring effect in liquid iron. For this reason the rate at which Mg can be added to liquid iron tends to be limited to between 8 and 12 kg per minute. Once the required amounts of reagent are added, the lance is withdrawn with the reagent still flowing until the lance leaves the surface of the melt. Then the powder flow can be discontinued and the carrier gas turned off when the lance is clear of the melt. After the injection process is finished the slag on the top of the iron will now be rich in sulphur. In order to prevent the sulphur from the slag reverting back into the iron, much of the slag must be removed by raking the slag from the surface of the iron using a steel boom and refractory coated rake. This process is known as de-slagging. The grain size of the injected reagent must be carefully controlled by the supplier. For a high reaction coefficient the grain size should be as small as possible, to present a large surface area for the chemical reactions to take place. On the other hand, if the grain size is too small, then the material is difficult to convey pneumatically. Each powder will have an optimum grain size distribution that allows its use for deep injection for iron desulphurisation. 2

Each of the reagents listed above have some drawbacks that should be pointed out. Magnesium powder is obviously highly flammable and magnesium powder for injection into liquid iron is treated with a passive coating to prevent easy oxidation. Lime is easily hydrated, and once hydrated can no longer be conveyed pneumatically and may even set hard in the equipment. Therefore, lime must be kept dry, best achieved by storing under a dry inert gas and kept fluidised. Similarly CaC 2 must be stored under a dry inert gas, with a constant flow of gas percolating through the storage vessel. However, the reason for keeping CaC 2 dry is that it reacts readily with moisture to form acetylene gas, which is highly flammable. Treated correctly, safe storage of the reagents is readily achievable. Efficiency of Desulphurisation Reagents The best reagent to use is very much dependent upon both the initial and final sulphur levels anticipated, the temperature of the hot metal and the price and availability of the reagents. The cheapest but least efficient of the reagents is lime. Mono-injection of lime is time consuming and results in large quantities of slag to be removed. Due to the large time requirements for injection and deslagging when using lime temperature losses are the highest for this reagent. It may be used when little desulphurisation is required and a steelmaker has a very low cost lime available. The efficiency of magnesium as a desulphurising agent is strongly dependent on temperature. At lower temperatures the solubility product between magnesium and sulphur is reduced and less magnesium is dissolved in the iron, thus allowing more of the injected magnesium to react with the dissolved sulphur giving a lower final sulphur level [3]. Figure 1 shows that at a hot metal temperature of 1250 C, only 0.003% of Mg is dissolved, compared to 0.032% at 1350 C. Figure 1. Variation of Mg solubility in liquid iron with sulphur content and iron temperature When the amounts of Mg and CaC 2 are compared for removal of sulphur at various start sulphur levels, it can be seen that Mg is by far the more efficient reagent by a factor of 10 or more (Figure 2). A cost comparison reveals that despite the higher efficiency of Mg, the high cost of Mg means that per 0.001% of sulphur removed, the costs of the reagents used are much closer. At present, Mg remains a more cost effective option with Mg prices at seven times those of CaC 2. 3

Figure 2. Effectiveness of desulphurisation for lime and calcium carbide for a typical steel plant in 1989 Desulphurisation by Co-injection The development of co-injection for hot metal desulphurisation in the late 1970s brought reductions in treatment time and large reductions in reagent consumption per tonne of treated metal [4]. Co-injection is the simultaneous injection of two or more powders through a single channel. Most commonly, the powders are used in combination with Mg and are usually based on either CaO or CaC 2. Because the powders are controlled independently, the cheaper powder is used to establish powder flow and the more expensive Mg is not added until the lance is in the lowest position in the iron ladle. The main injection period then consists of injection of Mg and another powder and the efficiency of the Mg is improved by fully utilising the Mg for desulphurisation, none is lost by oxidation in the atmosphere. At the end of the coinjection period, CaO or CaC 2 can be continued for a short while to ensure all the Mg is mixed into the steel and fully used. Then the lance can be withdrawn as for mono-injection. Recent examinations of the sulphur compounds present in desulphurised hot metal and in the slag layer indicate that when Mg is injected with calcium bearing reagents, MgS is readily produced in the liquid metal but only MgO and CaS are detected in the slag [5,6]. This is explained by the fact that the free energy of formation of CaS is much lower than that of MgS [5], but that the reaction between gaseous Mg and sulphur in the hot metal is much more rapid than the rate of reaction between the solids CaO or CaC 2 and sulphur. This is the reason why co-injection results in much better desulphurisation performance than mono-injection. 4

Desulphurisation by Twinjection Technology The equipment installed at Scunthorpe offers a two-fold advantage over the previous monoinjection of the magnesium based pre-mix. Twinjection offers the improved efficiency of coinjection with the added benefit of doubling the Mg injection rate and therefore a reduction in the injection time. The equipment incorporates two sets of dispensers for co-injection through two separate channels down a single refractory coated lance as shown in Figure 3. Since there are now two separate streams, the vigorous stirring effect from the gasification of Mg can be doubled and the rate of reagent addition is effectively doubled too. Figure 3 Typical Twinjection layout for co-injection of two streams down a single refractory coated lance. At Corus Scunthorpe, Mg and CaO were selected as the desulphurising reagents. Recent experience at Corus IJmuiden Works had shown that for their particular combination of iron chemistry and temperature, Mg and CaO injection was a more cost effective option than Mg and CaC 2 [7]. The plant was commissioned in August 2008 and using a lime to magnesium injection ratio of 3:1, the consumption of Mg has been significantly reduced for all final sulphur levels. Figure 4 shows how the Twinjection plant has reduced the Mg consumption by a factor of more than two, for example, for a starting sulphur level of 0.024%. Similarly for the same data, the total cost of injected reagents has also decreased by more than 50% (figure 5). The cost benefit of moving to co-injection is very clear from figure 5. However, the significant benefit of Twinjection is realised in terms of the reduction in injection time as observed from Figure 6, particularly for low final sulphur levels. Preliminary tests for co-injected lime and magnesium showed that injection times for a final sulphur level of 0.002% were reduced from an average of 28 minutes to an average of 12 minutes. The use of Twinjection, therefore, allows Corus to increase the number of ladles that can be put through the plant by reducing the cycle time to achieve the same sulphur level. It also allows a greater tonnage of low sulphur grades that can be treated through the plant. Due to the higher throughput capability and lower reagent cost benefit, this gives the plant the flexibility to allow an increase in the sulphur level in the incoming iron or using lower quality (cheaper) scrap with higher residual sulphur levels in the primary steelmaking stage to produce steels of the same final sulphur level. 5

Figure 4. Reagent consumption comparison between former mono-injection equipment and new Twinjection co-injection. Figure 5. Comparison of the total cost of reagents for desulphurisation from 0.024% start sulphur. Figure 6. Comparison of injection times for a start sulphur level of 0.024% 6

Summary Corus Scunthorpe Works has upgraded their hot metal desulphurisation equipment from mono-injection of magnesium to a co-injection process using lime and magnesium through the use of the Twinjection technology supplied by SMS Mevac. Reagent costs for desulphurisation have been significantly reduced. Injection times have been reduced by more than 50% and the capacity of the hot metal desulphurisation equipment is no longer a bottleneck for the rated capacity of the steel plant. The reduction in injection times achieved now allows the plant to consistently treat 50% more ladles than was the case previously. References [1] D. J. Price, Ironmaking & Steelmaking, 2007, 34, (3), 200-205. [2] D. Briggs, Embedding Human Scheduling in a Steel Plant Simulation, Proceedings of the 2008 Winter Simulation Conference, 1959-1967. [3] N.A. Voronova, "Desulfurization of Hot Metal by Magnesium", (International Magnesium Association and Iron and Steel Society, 1983) [4] E. T. Turkdogan, Fundamentals of Steelmaking, (The Institute of Materials, London, 1996) [5] A. Ender, H van den Boom, H. Kwast, H.-U. Lindenberg, Steel Research Int., 2005, 76, 562-572. [6] H.-J. Visser et al, La Revue de Metallurgie-CIT, November 2006, 487-492. [7] H.-J. Visser, R. Boom, ISIJ International, 2006, 46, (12), 1771-77. 7