SCHOTT is an international technology group with more than 5 years of experience in the areas of specialty glasses, materials and advanced technologies. With our high-qualitity products and intelligent solutions, we contribute to our customers success and make SCHOTT part of everyone s life. With a production capacity of more than 0,000 tons and production sites in Europe, South America and Asia, SCHOTT Tubing is one of the world s leading manufacturers of glass tubes, rods and profiles. Approximately 60 glass types are produced in large external diameters and a variety of lengths based on site-overlapping strategies in development, production and quality assurance. SCHOTT Tubing provides customized products and services for international growth markets such as pharmaceuticals and electronics as well as industrial and environmental engineering.
3 Contents 5 6 6 7 8 5 DURAN Customer Service and Technical Consulting 6 6 Product Range 7 8 Physical and Chemical Properties Tips on Processing Packing
DURAN Borosilicate Glass 3.3 Gives you an advantage in both quality and service DURAN in the Laboratory Highly resistant to thermal shock and heat Resistant to water, strong acids, alkali and saline solutions Fulfills all major standards (e. g. DIN ISO 85 and ASTM E38 Type I, Class A) Established brand for glassblowing items in the laboratory sector DURAN for Lighting High optical and cosmetic quality, therefore no unwanted reflections or refractions Tight geometric tolerances allow for stable manufacturing processes and easy assembly Especially low thermal expansion, high resistance to thermal shock and high chemical resistance make it optimally suited for use in adverse conditions Can be tempered upon request (DURATAN ) DURAN for Engineered Systems and Plants A wide range of dimensions and variable lengths helps to reduce and/or eliminate the need for subsequent dilation or part assembly High geometrical accuracy and excellent optical properties allow easy assembly, high functionality in service and low levels of maintenance Exceptionally corrosion resistant, chemically inert and will not burn Longstanding glass know-how for engineered systems and plants (heat exchangers, ozone generators, chemical plant engineering)
5 Scientific Services The Scientific Services department of SCHOTT is available to customers for all questions concerning glass properties, processing and the various applications of DURAN tubing, rod and capillary. Equipped with its own chemical and physics laboratories this team of qualified experts is optimally suited to handle any question. This means that our customers do not just get innovative solutions regarding the glass itself but we can also provide valuable input and knowledge to help solve problems within existing manufacturing processes. All you have to do is ask! Scientific Services Our services at a glance: Problem solving analysis for manufacturing processes Technical Advice for specific applications Know-how transfer available through workshops and lectures Do you have a new product idea? We have the know-how! Contact us! Direct contact: Mr. Dr. Andre Petershans andre.petershans@schott.com Ordering around the clock DURAN can be conveniently and easily ordered online around the clock. The comprehensive and secure login functions at www.schott.com/tubing/ecom make ordering easy. Stock of inventory, price transparency and anticipated delivery date are only some of the helpful functions available. Further information and individual login data are available by phone + (0) 633/80-00 or by email at customerservice.tubing@schott.com. All dimensions shown in this brochure can be ordered online: www.schott.com/tubing/ecom
6 DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons 3 ±0. 0.7 ±0.0 7 6.0 7 3.0 ±0. 0.8 ±0.0 7 555 36 50.0 5 ±0. 0.8 ±0.0 33.0 5 50.0 6 ±0..0.5 ±0.0 53 7 5 3.0 36 36 68.0 50.0 7 ±0..0.5 ±0.0 63 87 0 7.0 5 36 50.0 50.0 8 ±0..0.5 ±0.0 7 0 7.0 5 36 50.0
7 DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons ±0..0.5 ±0.0 8 8.0 5 36 50.0 50.0 0 ±0..0.5. ±0.0 ±0. 5 3 80 5 0 56.0.0 5 5 5 0 50.0 50.0 ±0.8.0.5. ±0.0 ±0. 05 50 3 86 73.0.0 8.5 5 5 5 0 38.5 ±0.8.0.5. ±0.0 ±0. 6 65 6 30 67.0.5 5 5 5 7.5 3 ±0.8.0.5. ±0.0 ±0. 6 8 50 55 36.0 5 5 5 50.0 0 ±0.8.0.5. ±0.0 ±0. 37 7 73 0 6 30.0 8. 5 5 5 0 36.0 5 ±0.8..8.5 ±0.05 ±0.0 ±0.3 7 50 38 86 56 5.0 8. 5 5 0.0 36.0 6 ±0.8..8.5 ±0.05 ±0.0 ±0.3 87 68 8 5 3. 8.8 5 5 58.5 36.0 7 ±0.8..8.5 ±0.05 ±0.0 ±0.3 87 38 75 5.0.5 5 5 0.0 7.5 8 ±0.8..8.5 ±0.05 ±0.0 ±0.3 306 07 66.0 8. 5 0.0 5 36.5 ±0.8..8.5 ±0.05 ±0.0 ±0.3 35 33 63 36.0 3.7 5.6 0.0 7.5 56.0 ±0.5..8.5 ±0.05 ±0.5 37 3 60 55 36 3.0.. 5 5 3.0.0
8 DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons ±0.5..8.5 ±0.05 ±0.5 6 38 5 30 30.0.5 5. 38 0.5 53.0 ±0.5..8.5 ±0.05 ±0.5 87 565 36 5 5 0.3 0.5.0 5 360.5 367.5 0.0 6 ±0.5..0.8 ±0.05 ±0.5 36 50 68 30 5 0..6 3.6 38.5.0 76.0 8 ±0.5..0.8 ±0.05 ±0.5 3 56 7 5.8.0.8 33.0 38 58.0 30 ±0...0.8 ±0.5 588 800 36 6 6 5...8 30.0 3.0 8.0 3 ±0...0.8 ±0.5 50 630 85 5 6 6.3 0. 3.8 6.0 3.5 83.0 33 ±0..0 65 5 6. 3.0 3 ±0...0.8 ±0.5 7 67 8 5 6 6. 0.8.8.0 378.0 58.0 36 ±0.0..0.8 ±0.5 50 7 76 5 5.6 8.0.7 5.0 360.0 0.5 38 ±0.0..0.8 ±0.5 538 756 0 0.8. 6.0 300.0 3.0 0 ±0.55.6.3 3. ±0. ±0. ±0.0 65 37 838 6 6 0..6. 6.5 8.0.0 3.0 6.0 ±0.55.6.3 3. ±0. ±0. 67 5 30 6 6 0. 5.3.7 8.0 306.0 0.5
DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons ±0.55.6.3 3. ±0. ±0. 73 007 37 6 6. 6.0. 8.0 3.0 3.0 5 ±0.65 ±0.0 0 8. 8 5. 6 ±0.65.6.3 3. ±0. ±0. 76 056 3 6..5 3.0 38.0 33.5 5 8 ±0.65.6.3 3. ±0. ±0. 780 0 506 6 6 6. 7.6.0 8.0.0 3
0 DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons 50 ±0.70.8.5 3.5.0 ±0. ±0.5 ±0.5 ±0.30 ±0.65 7 70 363 3 6 3 876 6 6 6 0..5..0 3. 8 8.0 300.0 3.5 53.0 87. 5 ±0.70.8.5 3.5 ±0. ±0.8 ±0.5 300 783 8.5.7 6.0 70.0 3.0 3.0 5 ±0.70.8.5 3.5 ±0. ±0.8 ±0.5 87 856 8.. 6.7 78.0.0 33.0 55 ±0.70 ±0. 66 0.5 367.5 56 ±0.70.8.5 3.5 ±0. ±0.8 ±0.5 05 05 30..6 7.5 8.0 5.0 0.0 58 ±0.70.8.5 3.5 ±0. ±0.8 ±0.5 063 57 00.6 3. 8.0.0 6.0 360.0
DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons 60 ±0.80. 3...0 ±0.8 ±0. ±0.30 ±0. ±0.65 336 0 6 888 3 87 8.0 7.,8.5 5.6.3 8 0.0 3.0 33.0 0.5 56.0 50. 65 ±0.80. 3.. ±0.8 ±0. ±0.30 ±0. 5 077 68 3 5 8.7 8,3 0.7.6 3.0 0.5 37.5.0 70 ±0.0. 3...0 ±0.8 ±0. ±0.30 ±0. ±0.65 567 5 03 3 63 5 766 8.5.0.6 3.6 8.5 3. 5 87.5 3 06.0 76.0 67.5 85. 75 ±0.0. 3.. ±0.8 ±0. ±0.30 ±0. 68 3 3 3 3 676 8 3.5.7.5.7 5.5.0 50.0.0 80 ±..5 3.5.0 ±0.8 ±0.5 ±0.0 ±0.70 0 8 3 3 6 7 8..3 5.8 6.8 6.0 6.0 36.0 536.0 85 ±..5 3.5 ±0.8 ±0.5 ±0.0 66 6 8.7.0 6.8 0.0 336.0 0 ±..5 3.5.0 ±0.8 ±0.5 ±0.0 ±0.70 8 3 80 6 6 0 7 657 3 3..7 7. 8.3 3.0 5 5 8.0 8.0 7.5 3 5 ±.0.5 3.5 ±0.8 ±0.5 ±0.0 3 36 76.7 3. 8..0 68.0 378.0
DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons 00 ±.0.5 3.0 3.5.0 ±0.8 ±0. ±0.5 ±0.0 ±0.70 560 3 056 3 57 8 6 838 8 60 3 3 3 3 0.3. 0.7.5 5.8 6.0 08. 8. 80.0 6.0 30.6 05 ±.50 3.0 ±0. ±0.0 3 5 5 3 3.6 5.8 5. 8.6 0 ±.50 3.0 ±0.30 ±0.70 3 37 5 5 7 573 3 3 3 0. 6.5.7. 8.0 7. 5 ±.50 3.0 ±0.30 ±0.70 3 5 5 777 7 0..6 5. 5 5 6. 38.5 ±.50 3.0.0 ±0.30 ±0.70 ±0.0 3 687 6 03 8 308 0 3.7. 6.6.0 5 5 5 3.3 8.5.0 3 5 ±.50.0 ±0.0 6 30 0 65.6. 5 5 8.0 38.5 30 ±.60 3.0.0 ±0.30 ±0.70 ±0.0 00 6 565 03 38 6.0 3. 8.. 5 5 5.0 6.5 7.5 33.5 ±.60 ±0.70 6 87 3.7 8.8 5 5 5.5 8.0 0 ±.70 3.0 ±0.30 ±0.70 37 7 00 77 7.3..6 5 5 55.7 3.0.0 5 ±.70 7.7 5.5
3 DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons 50 ±.80 3.0.0 ±0.30 ±0.70 ±0.0 63 7 65 0 5 3 3.3 5..0 6.7.6 8. 5.0 3. 55 ±.80 7 877 5.8 8.6 60 ±.80 ±0.80 8 0 6.3.5 5.6 70.0 65 ±.80 ±0.80 8 03 67 6.8 3..6 78. 70 ±.80.0 ±0.80 ±.00 8 665 8 5 7.3.0 5. 7.6 88.0 30.0 80 ±.00.0 ±0.80 ±.0 0 7 6 65..7 6. 8.0 3.0
DURAN Tubing Outside Diameter Wall Thickness per Tube Length approx. 500 mm Carton Contents Pallet Load mm mm g Number of Tubes Number of cartons 0 ±.0 ±0.80 76 3 55.7 3.5.0 70.0 0 ±.0.0 ±0.80 ±.00 ±. 0 0 8 055 0.. 8..0 8.0 36.0 5 ±.50.0 ±.0 ±. 5 3 73 5.3.5 37.7 75.5 5 ±.70.0 ±.0 ±.30 6 08 8 6.0..0 83.6 0 ±.0.0 ±.30 836.8 6. 50 ±3.00.0 ±0.80 ±.0 ±.30 867 7 866 78. 7..8 6. 6. 5. 70 ±3.00.0 ±0.80 ±.0 ±.30 3 7 337 67 3..3.7 5. 73.7.3 300 ±3.80.0 ±0.80 ±. ±.0 5 5 7 508 5.5.5 7.5 3.5 3.5 7.5 35 ±3.0.0 ±. ±.0 65 8 6.6 8. 3. 60. 35 ±.00.0 ±.0 ±.0 87 33 085. 33.0.6 0 ±.00 ±0.80 8 8 8. 7. 365 ±.50 ±.0 6 3 6.3 05. 00 ±0 6.0 ±.50 8.8. 5 ±0 ±.50 7 30.0.0 ±0 ±.00 3 063 3. 7. Standard length: 500 mm Special lengths of tubing (depending on outside diameter and wall thickness) are available upon request between 000 and 0000 mm. Glass cut to a length of 0.3 mm and longer available on inquiry.
5 DURAN Capillary Outside Diameter Inside Diameter per Tube Length approx. 500 mm Carton Contents mm mm g Number of Tubes ±0.8 0.8 0 50 5 ±0.8 0. 0.6 0.8. 65 65 6 6 5 5 56 6 6 ±0.8 0. 0.8..7..7 3 87 8 75 0 08 0 5 33 7 ±0. 0.8..7..7 3.0 7 5 6 0 05 7 80 83 86 5 8 ±0. 0.8..7..7 3.0 66 6 60 55 60 6 63 65 67 6 ±0. 0.8..7..7 3.0 5 0 8 7 8 50 5 53 Quantity of capillaries per pallet: Number of cartons: 55 : ca. 550.0 kg Standard length: 500 mm
6 DURAN Rod Diameter / Length Length approx. 500 mm Carton Contents Pallet Load mm g Number of Rods Number of cartons 3 ±0. 5.5 550.0 ±0. 8.5 550.0 5 ±0. 66 83.0 58.0 6 ±0. 5 0 3. 580.8 7 ±0. 8.6 55. 8 ±0. 68 80 3. 58.6 ±0. 3 63 3. 58.6 0 ±0. 63 5.8 5. ±0. 378 3. 580.8 ±0.30 55. 55.6 6 ±0.30 67 3. 36 8. 8 ±0.0 85 7 ±0.0 050 6 6.8 7 53.6 ±0.5 7 5.3 36 550.8 ±0.5 5 8. 7. 6 ±0.55 775 6.0 7 3.0 8 ±0.80 05 8.5 7.5 30 ±0.80 363 6. 36 5. Standard length: 500 mm
7 DURAN Borosilicate Glass 3.3 Physical and Chemical Properties Physical Properties Coefficient of mean linear thermal expansion a ( C; 300 C) acc. to DIN ISO 7 3.3 0 6 K Transformation temperature T g 55 C Temperature of the glass at viscosity h in dpa s: 0 3 (annealing point) 0 7.6 (softening point) 0 (working point) 560 C 85 C 60 C Density r at 5 C.3 g cm 3 Modulus of elasticity E (Young s modulus) 63 0 3 N mm Poisson s ratio m 0. Thermal Conductivity l w at 0 C. W m K Temperature for the specific electrical resistance of 0 8 W cm (DIN 5 36) t k 00 50 C Logarithm of the electric volume resistivity (W cm) at 50 C at 0 C 8 6.5 Dielectric properties ( MHz, 5 C) Dielectric constant (permittivity) e Dielectric loss factor (dissipation factor) tan d.6 37 0 Refractive index (l = 587.6 nm) n d.73 Stress-optical coefficient (DIN 5 3) K.0 0 6 mm N Chemical Composition SiO B O 3 Na O + K O Al O 3 8 3 main components in approx. weight %
8 DURAN Borosilicate Glass 3.3 Physical and Chemical Properties Chemical Resistance Hydrolytic Class (DIN ISO 7) HGB Acid Class (DIN 6) Class S Alkali Class (DIN ISO 65) Class A Transmission Transmission (%) 00 0 80 70 60 50 0 30 0 0 0 300 00 500 600 800 000 00 3000 000 5000 6000 Wall Thickness mm mm 8 mm Wavelenght (nm) DURAN Borosilicate Glass 3.3 is highly resistant to water, neutral and acid solutions, concentrated acids and acid mixtures; as well as chlorine, bromine, iodine and organic substances. Hydrofluoric acid, hot phosphoric acid and alkaline solutions do attack the glass surface but this is dependent on their concentration and temperature. Therefore, with these chemicals the use of DURAN should be checked for each individual case.
DURAN Borosilicate Glass 3.3 Tips on Processing The excellent properties of DURAN tubing, rod and capillary provide for good workability when forming and cutting the glass when using the normal techniques associated with technical glass. Stress-free Annealing To eliminate temporary stress as a result of the working process, the glass should be well heated to a maximum temperature of 550 C and kept at this level for a maximum of 30 minutes. For a thinner wall only a fraction of this period is necessary. The chart below states the recommended cooling rate for the subsequent annealing: Wall Thickness Temperature Range in mm 550 to 80 C 80 to 00 C 00 to C 3 ~ C/min ~ C/min up to ~ 80 C/min 6 ~ 3 C/min ~ 6 C/min up to ~ C/min ~ 0.8 C/min ~.6 C/min up to ~ 3 C/min If an article needs to be annealed several times, the sum of all annealing periods at 550 C should not exceed hours. Resistance to Thermal Shock According to DIN ISO 78, resistance to thermal shock is the difference in temperature between the hot test sample and the cold water bath (room temperature) at which 50 % of all test samples show a tendency to crack when quickly immersed. Listed below are some benchmarks to illustrate the resistance to thermal shock of tubing, rod and capillary made from DURAN Borosilicate glass 3.3. Tubes OD 50.5 / WT 0 mm: ~ C Rod Diameter.0 mm: ~ 0 C OD 33.0 / WT 0 mm: ~ 80 C OD.0 / WT 8.00 mm: ~ 80 C The resistance of tubing and rod to thermal shock depends on many different factors. Some of these are the wall thickness, shape and size of the chilled surface, the state of the surface, the stress already present in the glass, and the end finish. It is recommended not to exceed a temperature difference of C. OD = Outside Diameter, WT = Wall Thickness
DURAN Borosilicate Glass 3.3 Tips on Processing Pressure Resistance of Tubing made of DURAN Borosilicate Glass 3.3 The following formulas apply to stress-free tubing and cylindrical hollow bodies with a circular profile, uniform wall thickness with open ends, free from thermal load, under internal positive pressure and external negative pressure. Calculation of Pressure Resistance (p) p = WT OD WT K S Calculation of the Wall Thickness (WT) WT = OD p K + p S OD = Outside Diameter in mm WT = Wall Thickness in mm p = Pressure Resistance in bar K N = 7 S mm = permissible load according to standard DIN EN 55: Pressure Equipment made from Borosilicate Glass 3.3 General Rules for Design, Manufacture and Testing Other points to be considered: AD 00-leaflet N, edition 00-0: Pressure vessels made of glass, with encl., edition 00-0: Evaluation of faults in walls of glass pressure containers AD 00-leaflet B, edition 00-0: Cylindrical and spherical shells under internal pressure overload According to DIN EN 55 Pressure Equipment made from Borosilicate Glass 3.3 General Rules for Design, Manufacture and Testing, DURAN is an approved material and may be used for the construction of pressure equipment.
DURAN Borosilicate Glass 3.3 Packing Standard: Cartons Available upon request: DENSOPACK (up to Outside Diameter 50 mm) DENSOPACK Tightly packed and covered with shrink film = effective transport protection Technical Terms of Supply Detailed information on permissible faults, definition of faults, testing methods and testing units are available upon request. Reduced tolerances are also available upon request. In case of quality complaints the relevant Technical Terms of Supply for the application apply to all sales and are binding unless separate written agreements with respect to quality have been entered into. SCHOTT, DURATAN and DENSOPACK are registered trademarks of SCHOTT. DURAN is a registered trademark of the Duran Group GmbH. Subject to technical alterations. We thank our customers and partners for their kind assistance in providing product samples and photos.
Notes