UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT VEHICLE I.D SPECIFICATION AND GRADE PIPE CARBON SMLS STD PIPE API 5L-*44TH ED DTD OCT 2007 AND ISO 3183:2007 MOD PSL-2 GRADE B AND GRADE X42 R N OR Q ASTM A53-*12 ASTM A106-*11 GRADE B QUAD STENCIL SPECIAL OD TOLERANCE ASME SA53-*2010 EDITION ASME SA106-*2010 EDITION GRADE B BLK REG MILL COAT PE BEV 30 DEG MEETING ALL THE APPLICABLE REQUIREMENTS OF NACE STANDARD MR-01-75 *:ISO 15156-2 2009 ED AND MR-0103-2012_ED TYPE/ ORIENTATION COND. GAUGE WIDTH O.D.: WALL: YIELD EXT % TENSILE Y/T ELONG % in (mm) in (mm) TENSILE PSI.50 PSI 2" HRB PSI 42100 60200 66.0 2500 5 IN 71800 110200 0.93 28.0 99.5 MA4617 B353AA STRIP/L/B AR 1.500 53000.50 78500 0.67 41.5 B 81.7 2500 5 MA4621 B352AA STRIP/L/B AR 1.500 51000.50 79500 0.64 39.2 B 82.6 2500 5 (IN ) SCALE: HARDNESS MIN HYDRO DWELL(SEC) LEGEND: L - LONGITUDINAL U - UPSET TYPE T - TRANSVERSE NM - NORMALIZED QT - QUENCH & TEMPERED SR - STRESS RELIEVED AR - AS ROLLED B - BODY W - WELD TR - THERMOMECHANICAL ROLLED C MN P S SI CU NI CR MO AL N V B TI CB CO C.E.* MA4617 HEAT 20 105 012 001 22 12 04 06 02 026 03 0004 002 002.41 MA4617 B353AA PROD 20 104 015 001 23 12 04 07 02 023 04 0001 001 001.41 MA4617 B353AA PROD 19 103 016 002 23 11 04 07 02 022 04 0002 002 002.40 MA4621 HEAT 20 105 010 001 24 10 05 06 02 029 04 0004 002 002.41 MA4621 B352AA PROD 20 104 014 001 24 10 04 06 02 024 04 0002 002 001.41 MA4621 B352AA PROD 19 103 014 002 25 10 04 06 02 026 04 0001 001 003.40 MAX.43 *C.E. IS BASED ON THE FOLLOWING EQUATION(S): CE=C+MN/6+(CR+MO+V)/5+(NI+CU)/15 DECIMAL POSITIONS FOR ELEMENTS ARE INDICATED BY THE LEFT MARGIN, VERTICAL DOTTED LINE OR DECIMAL POINT. ELEMENTS REPORTED IN MASS FRACTION (%) PAGE 1 OF 8
UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT FLAT BEND GRAIN SIZE MIN COLLAPSE O.D.: in (mm) WALL: in (mm) DIR LOC. TEMP SIZE CHARPY V-NOTCH IMPACT ING FT-LBS % SHEAR COND. 1 2 3 AVG 1 2 3 AVG DEG F MA4617 B353AA OK T B + 32 3/4 AR 85 104 107 98 70 100 100 90 MA4621 B352AA OK T B + 32 3/4 AR 82 79 85 82 40 50 70 53 LEGEND L - LONGITUDINAL T - TRANSVERSE B - BODY W - WELD HAZ - HEAT AFFECTED ZONE ING / INSPECTION INFORMATION FULL LENGTH VISUAL FULL LENGTH EMI FULL LENGTH MPI FULL LENGTH UT END AREA INSPECTION (PLAIN END) SPECIAL END AREA (SEA) INSP FULL LENGTH DRIFT / INSPECTION YES RESULTS / COMMENTS X OD OD/ID L L/T X X ID OD/ID L L/T DRIFT MANDREL SIZE: ADDITIONAL NOTES/COMMENTS MELTED AND MANUFACTURED IN THE USA, NO REPAIRS BY WELDING, NO MERCURY COMPOUNDS ARE ADDED TO THE STEEL AND ALL MERCURY BEARING EQUIPMENT IS PROTECTED BY A DOUBLE BOUNDARY OF CONTAINMENT. MANUFACTURED IN AN ISO 9001 CERTIFIED FACILITY - CERTIFICATE #32022. WAS HOT ROLLED AND HOT FINISHED THIS IS TO CERTIFY THAT THE DESCRIBED HEREIN WAS MANUFACTURED, SAMPLED, ED AND/OR INSPECTED IN ACCORDANCE WITH THE SPECIFICATION AND FULFILLS THE REQUIREMENTS IN SUCH RESPECTS. PAGE 2 OF 8 **
UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT VEHICLE I.D SPECIFICATION AND GRADE PIPE CARBON SMLS STD PIPE API 5L-*44TH ED DTD OCT 2007 AND ISO 3183:2007 MOD PSL-2 GRADE B AND GRADE X42 R N OR Q ASTM A53-*12 ASTM A106-*11 GRADE B QUAD STENCIL SPECIAL OD TOLERANCE ASME SA53-*2010 EDITION ASME SA106-*2010 EDITION GRADE B BLK REG MILL COAT PE BEV 30 DEG MEETING ALL THE APPLICABLE REQUIREMENTS OF NACE STANDARD MR-01-75 *:ISO 15156-2 2009 ED AND MR-0103-2012_ED TYPE/ ORIENTATION COND. GAUGE WIDTH O.D.: WALL: YIELD EXT % TENSILE Y/T ELONG % in (mm) in (mm) TENSILE PSI.50 PSI 2" HRB PSI 42100 60200 66.0 2500 5 IN 71800 110200 0.93 28.0 99.5 MA4673 B355AA STRIP/L/B AR 1.500 59000.50 78500 0.75 42.6 B 83.1 2500 5 MA4674 B354AA STRIP/L/B AR 1.500 48900.50 77500 0.63 40.2 B 83.2 2500 5 (IN ) SCALE: HARDNESS MIN HYDRO DWELL(SEC) LEGEND: L - LONGITUDINAL U - UPSET TYPE T - TRANSVERSE NM - NORMALIZED QT - QUENCH & TEMPERED SR - STRESS RELIEVED AR - AS ROLLED B - BODY W - WELD TR - THERMOMECHANICAL ROLLED C MN P S SI CU NI CR MO AL N V B TI CB CO C.E.* MA4673 HEAT 20 105 013 003 24 11 04 08 02 026 03 0003 002 002.41 MA4673 B355AA PROD 20 105 014 004 24 10 04 07 01 023 04 0001 001 001.41 MA4673 B355AA PROD 19 105 014 004 24 11 04 08 01 024 04 0001 001 001.40 MA4674 HEAT 20 104 011 001 24 09 04 07 02 025 03 0003 002 002.41 MA4674 B354AA PROD 20 104 012 002 24 10 04 07 01 023 04 0002 002 001.40 MA4674 B354AA PROD 20 102 012 002 26 10 04 07 02 026 04 0002 002 001.41 MAX.43 *C.E. IS BASED ON THE FOLLOWING EQUATION(S): CE=C+MN/6+(CR+MO+V)/5+(NI+CU)/15 DECIMAL POSITIONS FOR ELEMENTS ARE INDICATED BY THE LEFT MARGIN, VERTICAL DOTTED LINE OR DECIMAL POINT. ELEMENTS REPORTED IN MASS FRACTION (%) PAGE 3 OF 8
UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT FLAT BEND GRAIN SIZE MIN COLLAPSE O.D.: in (mm) WALL: in (mm) DIR LOC. TEMP SIZE CHARPY V-NOTCH IMPACT ING FT-LBS % SHEAR COND. 1 2 3 AVG 1 2 3 AVG DEG F MA4673 B355AA OK T B + 32 3/4 AR 84 83 79 82 100 100 100 100 MA4674 B354AA OK T B + 32 3/4 AR 119 85 87 97 100 50 50 66 LEGEND L - LONGITUDINAL T - TRANSVERSE B - BODY W - WELD HAZ - HEAT AFFECTED ZONE ING / INSPECTION INFORMATION FULL LENGTH VISUAL FULL LENGTH EMI FULL LENGTH MPI FULL LENGTH UT END AREA INSPECTION (PLAIN END) SPECIAL END AREA (SEA) INSP FULL LENGTH DRIFT / INSPECTION YES RESULTS / COMMENTS X OD OD/ID L L/T X X ID OD/ID L L/T DRIFT MANDREL SIZE: ADDITIONAL NOTES/COMMENTS MELTED AND MANUFACTURED IN THE USA, NO REPAIRS BY WELDING, NO MERCURY COMPOUNDS ARE ADDED TO THE STEEL AND ALL MERCURY BEARING EQUIPMENT IS PROTECTED BY A DOUBLE BOUNDARY OF CONTAINMENT. MANUFACTURED IN AN ISO 9001 CERTIFIED FACILITY - CERTIFICATE #32022. WAS HOT ROLLED AND HOT FINISHED THIS IS TO CERTIFY THAT THE DESCRIBED HEREIN WAS MANUFACTURED, SAMPLED, ED AND/OR INSPECTED IN ACCORDANCE WITH THE SPECIFICATION AND FULFILLS THE REQUIREMENTS IN SUCH RESPECTS. PAGE 4 OF 8 **
UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT SPECIFICATION AND GRADE PIPE CARBON SMLS STD PIPE API 5L-*44TH ED DTD OCT 2007 AND ISO 3183:2007 MOD PSL-2 GRADE B AND GRADE X42 R N OR Q ASTM A53-*12 ASTM A106-*11 GRADE B QUAD STENCIL SPECIAL OD TOLERANCE ASME SA53-*2010 EDITION ASME SA106-*2010 EDITION GRADE B BLK REG MILL COAT PE BEV 30 DEG MEETING ALL THE APPLICABLE REQUIREMENTS OF NACE STANDARD MR-01-75 *:ISO 15156-2 2009 ED AND MR-0103-2012_ED TYPE/ ORIENTATION COND. GAUGE WIDTH O.D.: WALL: YIELD EXT % TENSILE Y/T ELONG % in (mm) in (mm) TENSILE PSI.50 PSI 2" HRB PSI 42100 60200 66.0 2500 5 IN 71800 110200 0.93 28.0 99.5 MA4675 B351AA STRIP/L/B AR 1.500 52500.50 77500 0.68 40.7 B 83.3 2500 5 MA4676 B350AA STRIP/L/B AR 1.500 49900.50 76000 0.66 41.3 B 81.9 2500 5 (IN ) SCALE: HARDNESS MIN HYDRO DWELL(SEC) LEGEND: L - LONGITUDINAL U - UPSET TYPE T - TRANSVERSE NM - NORMALIZED QT - QUENCH & TEMPERED SR - STRESS RELIEVED AR - AS ROLLED B - BODY W - WELD TR - THERMOMECHANICAL ROLLED C MN P S SI CU NI CR MO AL N V B TI CB CO C.E.* MA4675 HEAT 20 105 010 000 24 11 04 06 02 027 03 0003 002 001.41 MA4675 B351AA PROD 20 104 011 001 25 11 05 06 02 028 04 0003 001 002.41 MA4675 B351AA PROD 20 104 012 002 25 10 04 07 01 025 04 0002 002 001.40 MA4676 HEAT 20 103 009 002 24 09 04 07 02 027 03 0003 002 001.40 MA4676 B350AA PROD 20 103 010 002 24 10 04 07 01 026 04 0001 003 001.40 MA4676 B350AA PROD 20 103 011 002 24 10 04 07 01 025 04 0002 002 001.40 MAX.43 *C.E. IS BASED ON THE FOLLOWING EQUATION(S): CE=C+MN/6+(CR+MO+V)/5+(NI+CU)/15 DECIMAL POSITIONS FOR ELEMENTS ARE INDICATED BY THE LEFT MARGIN, VERTICAL DOTTED LINE OR DECIMAL POINT. ELEMENTS REPORTED IN MASS FRACTION (%) PAGE 5 OF 8
UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT FLAT BEND GRAIN SIZE MIN COLLAPSE O.D.: in (mm) WALL: in (mm) DIR LOC. TEMP SIZE CHARPY V-NOTCH IMPACT ING FT-LBS % SHEAR COND. 1 2 3 AVG 1 2 3 AVG DEG F MA4675 B351AA OK T B + 32 3/4 AR 116 111 120 115 100 100 100 100 MA4676 B350AA OK T B + 32 3/4 AR 82 73 77 77 60 50 60 56 LEGEND L - LONGITUDINAL T - TRANSVERSE B - BODY W - WELD HAZ - HEAT AFFECTED ZONE ING / INSPECTION INFORMATION FULL LENGTH VISUAL FULL LENGTH EMI FULL LENGTH MPI FULL LENGTH UT END AREA INSPECTION (PLAIN END) SPECIAL END AREA (SEA) INSP FULL LENGTH DRIFT / INSPECTION YES RESULTS / COMMENTS X OD OD/ID L L/T X X ID OD/ID L L/T DRIFT MANDREL SIZE: ADDITIONAL NOTES/COMMENTS MELTED AND MANUFACTURED IN THE USA, NO REPAIRS BY WELDING, NO MERCURY COMPOUNDS ARE ADDED TO THE STEEL AND ALL MERCURY BEARING EQUIPMENT IS PROTECTED BY A DOUBLE BOUNDARY OF CONTAINMENT. MANUFACTURED IN AN ISO 9001 CERTIFIED FACILITY - CERTIFICATE #32022. WAS HOT ROLLED AND HOT FINISHED THIS IS TO CERTIFY THAT THE DESCRIBED HEREIN WAS MANUFACTURED, SAMPLED, ED AND/OR INSPECTED IN ACCORDANCE WITH THE SPECIFICATION AND FULFILLS THE REQUIREMENTS IN SUCH RESPECTS. PAGE 6 OF 8 **
UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT VEHICLE I.D SPECIFICATION AND GRADE PIPE CARBON SMLS STD PIPE API 5L-*44TH ED DTD OCT 2007 AND ISO 3183:2007 MOD PSL-2 GRADE B AND GRADE X42 R N OR Q ASTM A53-*12 ASTM A106-*11 GRADE B QUAD STENCIL SPECIAL OD TOLERANCE ASME SA53-*2010 EDITION ASME SA106-*2010 EDITION GRADE B BLK REG MILL COAT PE BEV 30 DEG MEETING ALL THE APPLICABLE REQUIREMENTS OF NACE STANDARD MR-01-75 *:ISO 15156-2 2009 ED AND MR-0103-2012_ED TYPE/ ORIENTATION COND. GAUGE WIDTH O.D.: WALL: YIELD EXT % TENSILE Y/T ELONG % in (mm) in (mm) TENSILE PSI.50 PSI 2" HRB PSI 42100 60200 66.0 2500 5 IN 71800 110200 0.93 28.0 99.5 WA4047 B360AA STRIP/L/B AR 1.500 58500.50 76000 0.77 40.8 B 85.0 2500 5 WA4118 B361AA STRIP/L/B AR 1.500 55000.50 74500 0.74 38.9 B 84.2 2500 5 (IN ) SCALE: HARDNESS MIN HYDRO DWELL(SEC) LEGEND: L - LONGITUDINAL U - UPSET TYPE T - TRANSVERSE NM - NORMALIZED QT - QUENCH & TEMPERED SR - STRESS RELIEVED AR - AS ROLLED B - BODY W - WELD TR - THERMOMECHANICAL ROLLED C MN P S SI CU NI CR MO AL N V B TI CB CO C.E.* WA4047 HEAT 19 100 006 001 22 14 13 11 05 025 03 0002 000 002.41 WA4047 B360AA PROD 19 106 008 001 24 11 14 11 05 016 03 0001 001 001.43 WA4047 B360AA PROD 20 106 009 001 24 11 14 11 05 016 03 0002 001 001.43 WA4118 HEAT 20 101 011 001 22 11 05 09 04 021 03 0003 000 002.41 WA4118 B361AA PROD 19 108 011 001 23 08 06 09 05 019 04 0001 001 001.42 WA4118 B361AA PROD 22 105 012 002 27 08 05 08 03 018 03 0000 001 001.43 MAX.43 *C.E. IS BASED ON THE FOLLOWING EQUATION(S): CE=C+MN/6+(CR+MO+V)/5+(NI+CU)/15 DECIMAL POSITIONS FOR ELEMENTS ARE INDICATED BY THE LEFT MARGIN, VERTICAL DOTTED LINE OR DECIMAL POINT. ELEMENTS REPORTED IN MASS FRACTION (%) PAGE 7 OF 8
UNITED STATES STEEL TUBULAR S TIME: 09:07:07 CERTIFIED REPORT FLAT BEND GRAIN SIZE MIN COLLAPSE O.D.: in (mm) WALL: in (mm) DIR LOC. TEMP SIZE CHARPY V-NOTCH IMPACT ING FT-LBS % SHEAR COND. 1 2 3 AVG 1 2 3 AVG DEG F WA4047 B360AA OK T B + 32 3/4 AR 186 184 190 186 100 100 100 100 WA4118 B361AA OK T B + 32 3/4 AR 81 72 80 77 80 70 80 76 LEGEND L - LONGITUDINAL T - TRANSVERSE B - BODY W - WELD HAZ - HEAT AFFECTED ZONE ING / INSPECTION INFORMATION FULL LENGTH VISUAL FULL LENGTH EMI FULL LENGTH MPI FULL LENGTH UT END AREA INSPECTION (PLAIN END) SPECIAL END AREA (SEA) INSP FULL LENGTH DRIFT / INSPECTION YES RESULTS / COMMENTS X OD OD/ID L L/T X X ID OD/ID L L/T DRIFT MANDREL SIZE: ADDITIONAL NOTES/COMMENTS MELTED AND MANUFACTURED IN THE USA, NO REPAIRS BY WELDING, NO MERCURY COMPOUNDS ARE ADDED TO THE STEEL AND ALL MERCURY BEARING EQUIPMENT IS PROTECTED BY A DOUBLE BOUNDARY OF CONTAINMENT. MANUFACTURED IN AN ISO 9001 CERTIFIED FACILITY - CERTIFICATE #32022. WAS HOT ROLLED AND HOT FINISHED THIS IS TO CERTIFY THAT THE DESCRIBED HEREIN WAS MANUFACTURED, SAMPLED, ED AND/OR INSPECTED IN ACCORDANCE WITH THE SPECIFICATION AND FULFILLS THE REQUIREMENTS IN SUCH RESPECTS. PAGE 8 OF 8 **