TOOLS NEWS HSS milling shank drills SE High Precision Drill Series 216.1 Update SEPDS/SEPDM B212G DS n P E S ditio Ad New HSS drill with newly developed proprietary D-STH surface treatment. Excellent for a wide range of work materials, wear resistant, lubricity and sharp cutting edge.
HSS milling shank drills SEPDS/SEPDM SE High Precision Drill Series Excellent wear resistance Adopted proprietary D-STH surface treatment with evolved nitriding and oxidation. D-STH treatment realizes the same level of sharpness as non-coating and excellent wear resistant like coating. Tool surface Hardening layer Hardening region Drilling of Carbon Steel S5C Number of holes 5 45 4 35 3 25 2 15 1 5 SEPDM Conventional A (TiN coating products) Conventional B (TiN coating products) Substrate < Conditions> Work material : JIS S5C/DIN-C5/AISI-149 Tool : SEPDMD3 (ø3mm) : 265min-1 : 25m/min : 398mm/min :.15mm/rev Hole depth : 8mm (Through hole) mode : Emulsion Continuous feed machining Machine tools : Gantry type M/C (BT4) The dark color, * the higher hardness Drilling of Stainless Steel SUS34 Number of holes 5 45 4 35 3 25 2 15 1 5 SEPDM Conventional (TiN coating products) < Conditions> Work material : JIS SUS34/DIN-X5CrNi181/ASTM-S34 Tool : SEPDMD3 (ø3mm) : 159min-1 : 25m/min : 398mm/min :.5mm/rev Hole depth : 7mm (Blind hole) mode : Emulsion Continuous feed machining Machine tools : Gantry type M/C (BT4) High-accuracy drill diameter JIS h6 Achieving the unprecedented highest accuracy with the new surface treatment. Diameter.5<DC 3 Tolerance.6 3<DC 4.8 1
Small burr in the feed direction Having sharp cutting edge compared to coating drills. Comparison of burr SEPDM < Conditions> Work material : JIS S5C/DIN-C5/AISI-149 Tool : SEPDMD4 (ø4mm) Speed : 35m/min :.15mm/rev Hole depth : 13mm (Through hole) mode : Emulsion Continuous feed machining Conventional (Coated product) Excellent welding resistance and smooth chip discharge Minute holes on a tool surface helps coolant penetrate into the holes, which result in the superior lubricity. The lubricity provides excellent welding resistance and chip disposal. Weld resistance SEPDM Conventional(Coated product) Welding of Aluminum: Small Welding of Aluminum: Large < Conditions> Work material : JIS AC4B/DIN-G-AISi9Cu3/ASTM-356. Tool : SEPDMD3 (ø3mm) Speed : 35m/min :.13mm/rev Hole depth : 9mm (Blind hole) mode : Emulsion Continuous feed machining 2
HSS MILLING SHANK DRILLS SEPDS SE High Precision Drill (S) NEW P M K N S H CO HSS D-STH 135 Thinning.5<DC<3 3.1<DC<4.6.8 PL LF DC LCF OAL DCON(h7) aunique D-STH process dramatically improves sharpness and welding resistance and smooth chip discharge. Unit : mm Order Number DC LCF OAL LF PL DCON Stock Order Number DC LCF OAL LF PL DCON Stock SEPDSD5.5 3.1 5.1 5.1 3 a SEPDSD55.55 3.11 5.11 5.11 3 a SEPDSD6.6 5.12 5.12 5.12 3 a SEPDSD65.65 5.13 5.13 5.13 3 a SEPDSD7.7 5.14 5.14 5.14 3 a SEPDSD75.75 5.16 5.16 5.16 3 a SEPDSD8.8 5.17 5.17 5.17 3 a SEPDSD85.85 5.18 5.18 5.18 3 a SEPDSD9.9 6.19 5.19 5.19 3 a SEPDSD95.95 6.2 5.2 5.2 3 a SEPDSD1 1 6.2 5.2 5.2 3 a SEPDSD11 1.1 8.2 55.2 55.2 3 a SEPDSD12 1.2 8.3 55.3 55.3 3 a SEPDSD13 1.3 9.3 55.3 55.3 3 a SEPDSD14 1.4 9.3 55.3 55.3 3 a SEPDSD15 1.5 9.3 55.3 55.3 3 a SEPDSD16 1.6 11.3 55.3 55.3 3 a SEPDSD17 1.7 11.4 55.4 55.4 3 a SEPDSD18 1.8 11.4 55.4 55.4 3 a SEPDSD19 1.9 12.4 55.4 55.4 3 a SEPDSD2 2 12.4 6.4 6.4 3 a SEPDSD21 2.1 12.4 6.4 6.4 3 a SEPDSD22 2.2 12.5 6.5 6.5 3 a SEPDSD23 2.3 13.5 6.5 6.5 3 a SEPDSD24 2.4 13.5 6.5 6.5 3 a SEPDSD25 2.5 13.5 6.5 6.5 3 a SEPDSD26 2.6 15.5 6.5 6.5 3 a SEPDSD27 2.7 15.6 6.6 6.6 3 a SEPDSD28 2.8 15.6 6.6 6.6 3 a SEPDSD29 2.9 15.6 6.6 6.6 3 a SEPDSD3 3 15.6 6.6 6.6 3 a SEPDSD31 3.1 17.6 7.6 7.6 4 a SEPDSD32 3.2 17.7 7.7 7.7 4 a SEPDSD33 3.3 19.7 7.7 7.7 4 a SEPDSD34 3.4 19.7 7.7 7.7 4 a SEPDSD35 3.5 19.7 7.7 7.7 4 a SEPDSD36 3.6 21.8 7.8 7.8 4 a SEPDSD37 3.7 21.8 7.8 7.8 4 a SEPDSD38 3.8 21.8 7.8 7.8 4 a SEPDSD39 3.9 21.8 7.8 7.8 4 a SEPDSD4 4 21.8 7.8 7.8 4 a 3 a : Inventory maintained in Japan.
SEPDM SE High Precision Drill (M) P M K N S H CO HSS D-STH 118 135 DC<4 DC=4 Thinning.5<DC<3 3.1<DC<4.6.8 PL LF DC LCF OAL DCON(h7) aunique D-STH process dramatically improves sharpness and welding resistance and smooth chip discharge. Unit : mm Order Number DC LCF OAL LF PL DCON Stock Order Number DC LCF OAL LF PL DCON Stock SEPDMD5.5 6.15 5.15 5.15 3 a SEPDMD55.55 6.17 5.17 5.17 3 a SEPDMD6.6 8.18 5.18 5.18 3 a SEPDMD65.65 8.2 5.2 5.2 3 a SEPDMD7.7 1.21 5.21 5.21 3 a SEPDMD75.75 1.23 5.23 5.23 3 a SEPDMD8.8 1.24 5.24 5.24 3 a SEPDMD85.85 1.26 5.26 5.26 3 a SEPDMD9.9 12.27 5.27 5.27 3 a SEPDMD95.95 12.29 5.29 5.29 3 a SEPDMD1 1. 12.3 6.3 6.3 3 a SEPDMD11 1.1 16.3 6.3 6.3 3 a SEPDMD12 1.2 16.4 6.4 6.4 3 a SEPDMD13 1.3 16.4 6.4 6.4 3 a SEPDMD14 1.4 18.4 6.4 6.4 3 a SEPDMD15 1.5 18.5 6.5 6.5 3 a SEPDMD16 1.6 2.5 6.5 6.5 3 a SEPDMD17 1.7 2.5 6.5 6.5 3 a SEPDMD18 1.8 22.5 6.5 6.5 3 a SEPDMD19 1.9 22.6 6.6 6.6 3 a SEPDMD2 2. 23.6 7.6 7.6 3 a SEPDMD21 2.1 23.6 7.6 7.6 3 a SEPDMD22 2.2 26.7 7.7 7.7 3 a SEPDMD23 2.3 26.7 7.7 7.7 3 a SEPDMD24 2.4 29.7 7.7 7.7 3 a SEPDMD25 2.5 29.8 7.8 7.8 3 a SEPDMD26 2.6 29.8 7.8 7.8 3 a SEPDMD27 2.7 32.8 7.8 7.8 3 a SEPDMD28 2.8 32.8 7.8 7.8 3 a SEPDMD29 2.9 32.9 7.9 7.9 3 a SEPDMD3 3. 32.9 7.9 7.9 3 a SEPDMD31 3.1 35.9 85.9 85.9 4 a SEPDMD32 3.2 36. 86. 85 1. 4 a SEPDMD33 3.3 36. 86. 85 1. 4 a SEPDMD34 3.4 39. 86. 85 1. 4 a SEPDMD35 3.5 39.1 86.1 85 1.1 4 a SEPDMD36 3.6 39.1 86.1 85 1.1 4 a SEPDMD37 3.7 39.1 86.1 85 1.1 4 a SEPDMD38 3.8 43.1 86.1 85 1.1 4 a SEPDMD39 3.9 43.2 86.2 85 1.2 4 a SEPDMD4 4. 42.8 85.8 85.8 4 a 4
HSS MILLING SHANK DRILLS RECOMMENDED CUTTING CONDITIONS Work material Mild Steel ( 18HB), Aluminum Alloy (Si<5%) SS4, S1C, A661, A775 etc Carbon Steel, Alloy Steel (18 28HB), Gray Cast Iron ( 35MPa), Copper, Copper Alloys S45C, SCM44, FC3 etc Alloy Steel, Tool Steel ( 25HB) Ferritic and Martensitic Stainless Steel ( 2HB) SKD11, SUS41, SUS43 etc Drill Dia. (mm).5 24 15.2 3 18 1125.1 11 13 8.1 8.65 28 137.3 41 22 17.2 21 14 68.2 135.8 33 131.4 52 27 17.3 32 14 55.3 165 1. 38 12.5 6 31 1.5 5 16 5.5 25 1.2 38 1.6 6 31 82.6 49 17 45.5 225 1.6 4 8.8 64 33 65.8 52 18 35.6 21 2. 4 64.9 575 35 55.9 495 18 29.6 17 2.5 4 51.11 56 35 44.11 48 18 23.8 18 3.2 4 4.13 52 34 34.13 44 18 18.9 16 4. 4 32.15 48 35 28.15 42 18 14.1 14 Work material Austenitic Stainless Steel ( 2HB) SUS34, SUS316 etc Alloy Steel, Tool Steel ( 3HRC) SKD61, SKT4 etc Drill Dia. (mm).5 1 66.1 65 1 66.1 65.65 11 53.12 6 11 53.12 6.8 11 43.15 6 11 43.15 6 1. 12 38.2 75 12 38.2 75 1.2 12 31.25 75 12 31.23 7 1.6 14 27.3 8 14 27.3 8 2. 15 24.4 95 15 24.4 95 2.5 15 19.5 95 15 19.4 75 3.2 15 15.7 15 15 15.5 75 4. 15 12.9 15 15 12.7 8 1) Please reduce the revolution and feed rate depending on the drilling situation when the installation of workpiece or machine lacks rigidity. 2) Please use a collet type drill chuck or a milling chuck. 3) Use suffi cient cutting fl uid. 4) VAPDS,VAPDM is recommended for the workpiece whose hardness is over 3HRC. 5) WSTAR drill(new, MWS) are recommended for Precipitation hardening stainless steel (JIS-SUS63/ISO-L-No58X5CrNiCuNb16-4/ ASTM-S174, JIS-SUS631/DIN-X7CrNiAl177/ASTM-S177) 6) When drilling holes greater than 4 x drill diameter hole depths, please use a peck feed. 7) The above-mentioned cutting condition is standard when using water-soluble cutting fl uid. Please reduce the revolution when using water-insoluble cutting fl uid. 8) For the spindle revolution of diameters not shown in the table, please adjust to the conditions of larger and closest diameter, or calculate from the cutting of the closest diameter. For the feed rate per revolution, please set up within the recommended feed rate of the closest diameter appropriately. 5
Technical Data What is D-STH treatment? Geometry of sharp cutting edge Proprietary D-STH surface treatment maintains sharp cutting edge even after drilling because D-STH treatment is a surface treatment that hardens the surface of tool substrate unlike a coating. Cross-section image of cutting edge treated with D-STH Cross-section image of coated cutting edge Rake face Small rounded Flank Excellent welding resistance and smooth chip disposal due to better condition of tool surface Minute holes on a tool surface helps coolant penetrate into the holes, which result in the superior lubricity. The lubricity provides excellent welding resistance and chip disposal. (The difference of welding resistance can be seen significantly when machining aluminum alloy) Meanwhile the coated product has small grains (macro particles) on the tool surface, and it leads to the problem of welding. The surface properties compared by SEM photos Surface treated with D-STH 1μm Surface of coated Minute holes Macro particles 6
Method of selection with coated drills (Drill diameter is set up ø4 or below) Please refer to the following table for recommendation of milling shank drill series (precision drill) Work material Burr Welding Chip disposal Wearing Fracture, Chipping Tool cost Mild Steel Carbon Steel SEPDo SEPDo SEPDo VAPD o VAPDoSUS VAPDo VAPDoSUS SEPD o Stainless Steel Austenitic, Martensite SEPDo SEPDo SEPDo VAPDoSUS VAPDoSUS SEPDo Aluminum Alloy SEPDo SEPDo SEPDo SEPDo SEPDo SEPDo Alloy Steel ( 3HRC) SEPD o SEPDo SEPDo VAPD o VAPD o SEPD o Alloy Steel (3 4HRC) VAPD o VAPDo VAPD o VAPD o VAPD o VAPD o For Your Safety adon't handle inserts and chips without gloves. aplease machine within the recommended application range and exchange expired tools with new ones in advance of breakage. aplease use safety covers and wear safety glasses. awhen using compounded cutting oils, please take fire precautions. awhen using rotating tools, please make a trial run to check run-out, vibration and abnormal sounds etc. agrinding or heating of cutting tools produces dust and mist. Inhaling large amount of dust or contacting with eyes and skins may harm your body. MITSUBISHI MATERIALS CORPORATION Overseas Sales Dept, Asian Region KFC bldg., 8F, 1-6-1 Yokoami, Sumida-ku, Tokyo 13-15, Japan TEL +81-3-5819-8771 FAX +81-3-5819-8774 Overseas Sales Dept, European & American Region KFC bldg., 8F, 1-6-1 Yokoami, Sumida-ku, Tokyo 13-15, Japan TEL +81-3-5819-8772 FAX +81-3-5819-8774 http://www.mitsubishicarbide.com/en/ (Tools specifications subject to change without notice.) EXP-13-E17 216.1.E( - )