Considerations in Developing High Energy ZnO MOV Blocks RAMÓN PUYANÉ

Transcription

1 Considerations in Developing High Energy ZnO MOV Blocks RAMÓN PUYANÉ

2 R. Puyané Advanced Varistor Consulting Limited Caraban House Caraban Ravensdale Dundalk IRELAND

3 MOV blocks are the working component in a surge arrester. The two major demands on high energy ZnO MOV blocks are: - Protect equipment and networks - Survive overvoltage transients

4 - System protection: Good voltage clamp: V 10kA, 20kA / V 5mA as close to 1 as possible To achieve it, it is required to have: Good intrinsic conductivity at high current (10 ka; 20 ka) Proper doping of ZnO grains. Main donors: Al 3+ ; Sb 3+ ; F + Caution: incorrect doping can increase leakage at COV.

5 Electrical impulses: Duty cycle impulses (Square waves: long duration low current) Lightning impulses (Short duration high currents) Long life under load Reliable: improves with time Moisture attack Critical issue for arrester manufacturer. This presentation will focus on survival under electrical impulses.

6 Electrical impulse failures: Crack mode failure due to fast generation of thermally induced mechanical stresses. Puncture mode failure due to current concentration at a non-uniform spot with lower threshold voltage.

7 MOV block crack failures under electrical impulses are due to brittle fracture. A brittle fracture in a MOV block originates at a very precise weak spot acting as the crack initiator, such as: Micro flaws Voids Inhomogeneities How can these weak spots be eliminated or minimized? By implementing the proper ceramic manufacturing procedures.

8 ZnO MOV manufacturing process flow: Process step Critical requirements Raw materials - Metal oxides - Water quality (purity) - Organic additives - Trace contaminants Powder (Spray dried) - Most critical step Compaction - Pressure profile Firing - Temperature profile and atmosphere Surfacing, glazing and metallizing - Proper handling Block mechanical control - Micro cracks detection (Ultrasonics) Electrical testing - Weed out weak blocks

9 MOV Raw materials Metal oxides: ZnO,Bi 2 O 3, Co 3 O 4, Sb 2 O 3, MnO, NiO, Critical spec. parameters - Part. Size Distr.; Spec. Surf. Area - Trace contaminants (Clamp) Organic additives Deflocculant, Binder, Antifoaming agent, Plasticizer, - Low ash content - Easy burn off - No gelling

10 Varistor powder oxide formulation Electrical requirements: Better peak pulse stability Low current power losses Improved energy handling capability Reduced residual voltage by enhanced doping Better control of ceramic crystalline microstructure: Enhanced grain uniformity to reduce residual voltage and leakage at low voltages Physical and mechanical aspects of the ceramic body: Higher mechanical strength for better energy handling capability

11 Varistor powder organic formulation: The organic additive system requires: Binder plasticity - Organic system formulation: It is critical for good compaction Powder compactability - Specified density Solid body lubricity - No compaction defects Mechanical strength of green discs

12 ZnO MOV ceramic powder: Spray dried agglomerates: Powder requirements: - Fully homogenized powder. - No segregation. - Well controlled Part. Size Distr. Single Spray Dry - Good flowability (small flow time) (Class 1 and 2) - High flow and tap density - Spherical solid particles Double Spray Dry with calcination (No doughnuts, no egg-shells) (Class 3, 4 and 5) - Solid lubrication present - No foreign contamination (Particles, fibres, aggregates, etc.)

13 ZnO MOV ceramic powder: SEM pictures Spray dried agglomerates: Close-up:

14 ZnO MOV ceramic powder: SEM pictures Contaminant fibres:

15 ZnO MOV ceramic powder: SEM pictures Organic contaminant particle: Close-up:

16 ZnO MOV ceramic powder: SEM pictures Organic contaminant particle IR spectrum:

17 ZnO MOV ceramic powder: SEM pictures Organic contaminant particle IR spectrum:

18 Block compaction methods: Floating die Fixed die and opposing rams compaction (Preferred method) Better control of body neutral plane Improved mechanical consistency of the green body (critical for HE MOV blocks) Requirements - Optimize compaction pressure profile. - Reduce spring-back effect - Minimized pressure gradients in blocks. - Tooling material and design. - Neutral plane at half way of height. - Avoid generation of edge micro flaws, cracks, laminations, end cap, etc.

19 Parameters affecting block compaction: Powder character.: Particle shape, size and distrib.; Spec. Surf. Area; flow time; hardness. Body geometry: Height; density, (Aspect ratio). Compact properties: Specified density; minimized density gradient; green strength; (min. defects). Organic system: Binder type and qty.; plasticizer; defloculant; lubricant. Compaction technique: Die filling, pressing profile (ramps and dwells) ; maximum force; ejection procedure.

20 MOV block compaction defect: Radial crack visualized on a sintered block.

21 ZnO MOV firing profile: The temperature profile and the firing atmosphere must be controlled. With proper control, watt loss at low voltage and residual voltage at high current will improve: Binder Burn Off (BBO): to be tailored for binder system and disc type Uniform densification: (Porosity elimination, LPS Bi 2 O 3 compounds) Temperature BBO Shrinkage Peak temperature crystal growth Cooling off : Natural or forced convection High Temp. dwell: Homogeneous crystal growth (narrow and uniform) Time

22 ZnO MOV firing: BBO is a critical step: Most mechanical defects are generated at this stage: Voids, cracks, microfisures Uniform densification: Avoid thermal gradients; atmosphere control HT sintering: Optimize t and T to promote homogeneous crystal growth.

23 ZnO MOV firing bulk defects: Micro-fissures / voids Close - up

24 ZnO MOV firing bulk defects: Void / Larger grain size - Mechanically weak spot - Larger grain size reduces threshold voltage

25 ZnO MOV firing bulk defects: Micro-fissures / voids Failure at 100 ka / 4 / 10 µs: fracture surface Close up Fracture origin

26 ZnO MOV firing bulk defects: Micro-fissures / voids Failure at 100 ka / 4 / 10 µs: fracture surface XRD spot analysis Close up Fracture origin

27 Flat surface grinding: Lapping Grinding (Preferred) Flat parallel surface Intense US washing, rinsing and degreasing. Flat surface specs: No scratches No edge chips Surface suitable for molten metal adhesion.

28 Testing of black MOV block before metallizing and passivation: Visual inspection Ultrasonic testing (Internal cracks, other defects)

29 Metallisation process: Flame spray Arc spray (Preferred) Masking procedure (Critical for edge definition) Accurately defined margin geometry for every block Passivation coating: Air spray of a glass powder suspension. Lead glass (Environm. Issue) Leadless glass (Cost issue) Glass coating thickness can be an issue for HASD test (Distr., class 1 and 2).

30 Final electrical testing: The only possible outcome is to weed out weak blocks that are non performing under energy impulses.

31 Conclusions and recommendations: More homogeneous blocks will show better survival performance under temporary over-voltages. MOV blocks with higher mechanical strength will have a higher probability of survival under energy impulses. Stronger MOV material will make it possible some reduction of block size. Smaller blocks with similar energy characteristics can make it possible to reduce the size of the arresters. However, block over heating must be considered when reducing MOV block size. A block size reduction can have an impact on costs for the block and arrester manufacturers as well as for the arrester user since a smaller and lighter arrester will be cheaper to install and to replace.

32 Thank you for your attention! Ramón Puyané ADVANCED VARISTOR CONSULTING LIMITED Dundalk, Co. Louth & Montpellier, L Hérault Ireland France