Comparison of mechanical behavior between bulk and ribbon Cu-based metallic glasses
|
|
- Andrea Sparks
- 5 years ago
- Views:
Transcription
1 Materials Science and Engineering A 430 (2006) Short communication Comparison of mechanical behavior between bulk and ribbon Cu-based metallic glasses W.H. Jiang a,, F.X. Liu a, Y.D. Wang a,b, H.F. Zhang c, H. Choo a,d, P.K. Liaw a a Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN 37996, USA b School of Materials and Metallurgy, Northeastern University, Shenyang , China c Shenyang National Laboratory for Materials Science, Institute of Metals Research, Chinese Academy of Sciences, Shenyang , China d Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831, USA Received 10 April 2006; received in revised form 11 May 2006; accepted 14 May 2006 Abstract As-cast bulk and as-spun ribbon Cu 60 Zr 30 Ti 10 metallic glasses were characterized using differential-scanning calorimetry and instrumented nanoindentation. Two alloys show a significant difference in the amount of free volume, which is attributed to the difference in a cooling rate, while exhibiting a similar serrated plastic flow. Atomic-force-microscopy observations demonstrate the pile-ups containing shear bands around the indents in both alloys. The as-cast bulk alloy has higher hardness and elastic modulus than the as-spun ribbon alloy. The difference in the strengths of two alloys may be related to the different amount of free volume. The strength seems to be more sensitive to a cooling rate during solidification than the plastic-flow behavior in the Cu 60 Zr 30 Ti Elsevier B.V. All rights reserved. Keywords: Metallic glasses; Nanoindentation; Plastic deformation; Hardness; Free volume 1. Introduction Over the last decade, significant progress has been made in searching alloy compositions with sluggish crystallization kinetics, resulting in the development of numerous bulk-metallic glasses (BMGs) that include Zr-, Ni-, Ti-, Mg-, Cu-, Pt-, Fe-, Laand Pd-based alloy systems. As their critical cooling rates are as low as 100 K/s, the BMGs can be produced using conventional casting techniques and their size is as large as millimeters or even centimeters [1]. This progress makes the applications of metallic glasses, particularly as structural materials, close to realization [1]. The BMGs have outstanding mechanical properties, such as high strength of up to 5 GPa [2], large elastic-deformation limit of around 2% [1], as well as good fatigue properties [3 6]. The cooling rate is one of the most important factors affecting structures and properties of the metallic glasses. Conventionally, the metallic glasses are synthesized by a rapid solidification process, typically melt spinning, which gives a cooling rate of about 10 6 K/s. The resulting products are in the form of ribbons with Corresponding author. Tel.: ; fax: address: wjiang5@utk.edu (W.H. Jiang). a thickness of tens of micrometers [7]. The rapidly solidified ribbons must be different in structures and properties from the BMG ingots produced at a much lower cooling rate, generally less than 10 2 K/s. Illekováetal.[8] observed a substantial difference in the structural relaxation kinetics between the bulk and ribbon Zr 55 Ni 25 Al 20 metallic glasses and the different degrees of the short-range order. Bobrov et al. [9] found that the density of the bulk Zr 52.5 Ti 5 Cu 17.9 Ni 14.6 Al 10 glass is higher than that of the ribbon counterpart, indicating that the amount of free volume in a metallic glass is related to the cooling rate. Understanding the difference in the mechanical behavior between the rapidly solidified ribbons and BMG ingots is of both practical significance and fundamental interest. However, small thicknesses of as-spun ribbons (i.e., tens of micrometers) inhibit an investigation through the conventional mechanical testing, such as tension, compression or microhardness tests. An instrumented nanoindentation is a useful probe for studying the mechanical response of various materials to the microto nano-scale loads. This technique has been applied widely to the study of mechanical behavior of metallic glasses as recently reviewed by Schuh and Nieh [10]. In this paper, an instrumented nanoindenter is utilized to study the mechanical properties of the bulk and ribbon Cu 60 Zr 30 Ti /$ see front matter 2006 Elsevier B.V. All rights reserved. doi: /j.msea
2 (at.%) metallic glasses. It is expected that this work can provide insight to the effect of cooling rates on the mechanical properties of metallic glasses. 2. Experimental W.H. Jiang et al. / Materials Science and Engineering A 430 (2006) The bulk Cu 60 Zr 30 Ti 10 metallic glass was prepared by arcmelting a mixture of the constituent elements in a purified argon atmosphere. In order to obtain the homogeneity, the alloy ingots were remelted several times before cast into a water-cooled copper mold using an in situ suction-casting facility. The resulting cylindrical BMG rods have a dimension of 3 mm in diameter and 30 mm in length. For the ribbon specimens, the master alloy with the nominal composition of Cu 60 Zr 30 Ti 10 was first synthesized by arc-melting a mixture of the constituent elements in a purified argon atmosphere. Then, the amorphous ribbons (2 mm 0.06 mm) were prepared from the master-alloy ingots using a single-roller melt-spinning apparatus with a copper wheel in a purified argon atmosphere. The amorphous structure of both bulk and ribbon alloys was examined by X-ray diffraction with Cu K radiation using Philips X pert Diffractometer. Differential-scanning calorimetry (DSC, Perkin-Elmer DSC7) was used to characterize their thermal properties. DSC was run two times for each specimen from 50 to 600 C at a heating rate of 20 C/min in an argon atmosphere. Taking the second scan as a base line, any thermal effect from the structural evolution during heating was investigated. The surfaces of the bulk and ribbon alloys were electropolished using a twin-jet thinning electropolisher for nanoindentation tests. For the ribbon alloy, the wheel side was subjected to polishing. Polishing was performed in a solution of 25% nitric acid and 75% methanol (vol.%) at 243 K and a voltage of 10 V. Nanoinstruments Nanoindenter II with a Berkovich diamond indenter was used to characterize their mechanical properties. At least 10 indents were made on each sample with the separation between adjacent indents of 20 m. The loading phase of the indentation was carried out under a displacement control at a loading rate of 10 nm/s to a maximum displacement of 350 nm. At 90% unloading, a dwell period of 100 s was imposed to correct for any thermal drift in the system, which was less than 0.5 nm/s. The load displacement curves, hardness and elastic modulus were obtained from indentation experiments. The atomic-force-microscopy (AFM) observation on the indents was conducted, using a Digital Instruments Nanoscope IIIa in the contact mode. Fig. 1. X-ray diffraction patterns of the bulk and ribbon Cu 60 Zr 30 Ti 10. DSC curves, the typical thermal properties were determined, as shown in Table 1. The bulk and ribbon alloys exhibit a similar thermal behavior. There are two exothermic peaks for the crystallization and an obvious endothermic peak for a glass transition for both alloys. The exothermic heats of the crystallization, H x ( H x = H 1 + H 2, where H 1 and H 2 are the exothermic heats of the first and the second crystallization, respectively.) are 41.7 and 45.5 J/g for the bulk and ribbon alloys, respectively. The crystallization peaks correspond to the precipitation of Cu 8 Zr 3 and Cu 10 Zr 7, respectively [11]. The 3. Results Fig. 1 shows the X-ray diffraction patterns of both bulk and ribbon Cu 60 Zr 30 Ti 10 metallic glasses. The broad diffraction maxima demonstrate the amorphous structure of the bulk and ribbon alloys. It has been observed that Cu 60 Zr 30 Ti 10 alloy has a good glass-forming ability, and the BMG rod with the maximum diameter of 4 mm has been reported [11]. Fig. 2 presents the DSC thermograms for the bulk and ribbon alloys that were normalized using the base lines. From the Fig. 2. (a) DSC traces of the bulk and ribbon Cu 60 Zr 30 Ti 10 at a heating rate of 20 min/s and (b) an enlarged portion of the dashed-line box in (a) showing an exothermic heat of the structural relaxation. The arrows in (b) indicate T g.
3 352 W.H. Jiang et al. / Materials Science and Engineering A 430 (2006) Table 1 Thermal properties of the bulk and ribbon Cu 60 Zr 30 Ti 10 measured from DSC Alloys T g ( C) T x1 ( C) T x2 ( C) T x ( C) H o (J/g) H 1 (J/g) H 2 (J/g) H 1 + H 2 (J/g) Bulk Ribbon T g denotes the glass-transition temperature, T x1 and T x2 the first and the second crystallization temperatures, T x the supercooled liquid region, H o the structuralrelaxation exothermic heat, and H 1 and H 2 the exothermic heats of the first and the second crystallization. glass-transition temperatures, T g, and the supercooled liquid regions, T x ( T x = T x1 T g, where T x1 is the onset temperature of the first crystallization), are and 37.0 C, and and 40.4 C for the bulk and ribbon alloys, respectively. This trend shows that the supercooled liquid regions of the bulk and ribbon alloys are quite similar. But, the supercooled liquid region of the bulk alloy is shifted upward by about 20 C compared to that of the ribbon alloy. Fig. 2(b) exhibits the enlarged DSC scanning curves at low temperatures. The exothermic reaction manifesting structural relaxation for both bulk and ribbon alloys are clearly observed just below the T g. The structural relaxation exothermic heat ( H o ) of the bulk alloy (8.9 J/g) is much smaller than that of the ribbon alloy (24.0 J/g). This trend can be related to the large difference in the amount of the free volume between the bulk and ribbon alloys; that is, the amount of the free volume of the bulk alloy is smaller than that of the ribbon alloy. Table 2 shows the values of hardness and elastic modulus of the bulk and ribbon alloys obtained from the nanoindentation tests. A correction was applied, using the actual contact area of indents observed by AFM to account for the pile-ups. It is important to mention that the hardness was obtained from the nanoindentation with a maximum displacement of 350 nm and a loading rate of 10 nm/s. Due to an indentation-size effect, hardness values for amorphous alloys, derived from the nanoindentation, are higher than those obtained from macro- or microhardness testers [12,13]. Thus, the numbers we present here are only used for the comparison between the current two alloys. It can be seen that the bulk alloy has a higher hardness and elastic modulus than the ribbon alloy. Fig. 3(a) displays the typical load displacement curves for the bulk and ribbon alloys. The obvious serrations are observed for both alloys. From the nanoindentation data in Fig. 3(a), the strain rates, ε = (1/h)(dh/dt), where h is the indenter displacement during loading, were calculated. The values change with the depth, as shown in Fig. 3(b). The strain rates for both alloys show the same decreasing trend with increasing the depth. However, the curves are not smooth, and there are obvious serrations. These curves highlight the serration behavior observed in the load displacement curves (Fig. 3(a)) and demonstrate that there is little difference in the serrations between the bulk and ribbon alloys. Table 2 Hardness (H) and elastic modulus (E) of the bulk and ribbon Cu 60 Zr 30 Ti 10 Alloys H (GPa) E (GPa) Bulk 7.61 ± ± 1.70 Ribbon 6.94 ± ± 0.92 Fig. 3. (a) The load displacement curves for the bulk and ribbon Cu 60 Zr 30 Ti 10 during nanoindentation and (b) the corresponding strain rate vs. displacement curves during loading. In order to avoid overlapping, the curves were shifted along the displacement in (a) and the strain rate in (b), respectively. AFM observations of the indents on the bulk and ribbon alloys show that the indents were rather regular in shape and caused no cracking. Typical images are shown in Fig. 4(a and c). There are obvious pile-ups containing shear bands around the indents in both bulk and ribbon samples (Fig. 4(b and d)). The pile-ups have the height of about 22 and 34% of the indent depth for the bulk and ribbon alloys, respectively. 4. Discussion Amorphous materials contain a significant amount of the free volume that is frozen during cooling. The free volume is one of the most important structural features in amorphous materials, which significantly affects the mechanical, physical and chemical properties. DSC is one of the effective methods to characterize the structural relaxation that is closely related to the free volume in amorphous materials. In a DSC thermogram, the exothermic reaction just below the T g is a result of the annihi-
4 W.H. Jiang et al. / Materials Science and Engineering A 430 (2006) Fig. 4. AFM images (a and c) and corresponding height profiles (b and d) of the indents formed at a maximum displacement of 350 nm in the bulk alloy (a and b) and ribbon alloy (c and d). The lines in the AFM images indicate the traces where height profiles were taken. lation of free volume and structural relaxation. The exothermic heat is proportional to the amount of the escaping free volume [14]. The present work demonstrates that the exothermic heat in the bulk Cu 60 Zr 30 Ti 10 is significantly less than that in the ribbon Cu 60 Zr 30 Ti 10 (Fig. 2(b) and Table 1), indicating that the bulk alloy contains less free volume than the ribbon alloy. A high cooling rate used in the process of the ribbon suppresses the escape of free volume during cooling. By measuring the density, Bobrov et al. [9] demonstrated that the bulk Zr 52.5 Ti 5 Cu 17.9 Ni 14.6 Al 10 has a higher density than the as-spun ribbon by about 1.3%. Using the positron annihilation, Nagel et al. [15] also observed that in Zr 46.7 Ti 8.5 Cu 7.5 Ni 10 Be 27.5, the rapid solidification froze in more free volumes. Even though the quantitative distinction in free volume between the bulk and ribbon alloys cannot be made here, a qualitative (or semi-quantitative) difference is clearly observed, which resulted from the large difference (about four orders of magnitude) in a cooling rate between two alloys [1,7]. Nanoindentation indicates that the bulk alloy has an appreciably higher hardness and elastic modulus than the ribbon alloy (Table 2). Their difference in mechanical strength may be closely related to the amount of the free volume in the metallic glasses. Evidently, an increase in free volume may increase the average atomic distance that affects the material stiffness, i.e., the elastic modulus. On the other hand, the free volume also influences the resistance to the plastic deformation. The increase in free volume results in the lower resistance to the plastic deformation. Jiang and Atzmon [16] also observed the decreases in the hardness values in the order of the as-relaxed, as-spun, and as-rolled states of the amorphous Al 86.8 Ni 3.7 Y 9.5, while the free volume in these states is expected to increase in the opposite order. In fact, it is widely observed that the relaxation annealing causes an increase in hardness/strength in metallic glasses [16 20]. The relatively high values of hardness and elastic modulus of the bulk alloy may be attributed to the smaller amount of free volume in its matrix, which was caused by the lower cooling rate. In the nanoindentation, the load displacement curves (Fig. 3(a)) of both bulk and ribbon alloys display obvious serrations. The serrated plastic flow has been observed extensively in metallic glasses [10,21 23]. At low temperatures (e.g., room temperature) and high strain rates, metallic glasses exhibit an inhomogeneous plastic deformation, and the deformation is confined to highly localized narrow regions, i.e., shear bands. The shear bands observed around the indents in both alloys indicate that the plastic deformation of both alloys is inhomogeneous. Wright et al. suggested that the serrated plastic flow is caused by the formation of individual shear bands [23]. Using an infrared camera, Jiang et al. recently observed in situ dynamic shearbanding processes during the uniaxial compression of a Zr-based BMG and demonstrated that the serrations in the plastic flow correspond to individual shear-banding events [24]. No appreciable distinction in serrations between the bulk and ribbon alloys can be made in the strain rate versus displacement curves (Fig. 3(b)). Therefore, the effect of free volume on the inhomogeneous plastic flow cannot be identified in the present study. 5. Conclusions The as-cast bulk and as-spun ribbon Cu 60 Zr 30 Ti 10 metallic glasses were characterized for the thermal and mechanical behaviors. The main results can be summarized as follows. (1) The as-cast bulk Cu 60 Zr 30 Ti 10 alloy has less free volume than the ribbon alloy, which is attributed to the relatively slower cooling rate. (2) The bulk alloy has a higher hardness and elastic modulus than the ribbon alloy. The difference in strength may be related to the different amount of free volume in the amorphous matrix. (3) The bulk and ribbon alloys exhibit a similar serrated plastic flow during the nanoindentation test. The pile-ups around the indents are observed in both alloys. (4) The hardness and modulus seem to be more sensitive to a cooling rate during solidification than the plastic-flow behavior in the Cu 60 Zr 30 Ti 10. Acknowledgements This work was supported by the National Science Foundation [NSF] International Materials Institutes [IMI] Program [DMR ], the Combined Research and Curriculum Development [CRCD] Program [EEC ] and the Integrative Graduate Education and Research Training [IGERT] Program [DGE ] with Dr. C. Huber, Ms. M. Poats, Dr. C. J. Van Hartesveldt, Dr. D. Dutta, Dr. L. Clesceri, Dr. W. Jennings and Dr. L. Goldberg as the Program Directors. References [1] W.L. Johnson, MRS Bull. 24 (1999) [2] A. Inoue, B.L. Shen, H. Koshiba, H. Kato, A.R. Yavari, Nat. Mater. 2 (2003)
5 354 W.H. Jiang et al. / Materials Science and Engineering A 430 (2006) [3] W.H. Peter, P.K. Liaw, R.A. Buchanan, C.T. Liu, C.R. Brooks, J.A. Horton, C.A. Carmichael, J.L. Wright, Intermetallics 10 (2002) [4] W.H. Peter, R.A. Buchanan, C.T. Liu, P.K. Liaw, J. Non-Cryst. Solids 317 (2003) [5] G.Y. Wang, P.K. Liaw, A. Peker, B. Yang, M.L. Benson, W. Yuan, W.H. Peter, L. Huang, A. Freels, R.A. Buchanan, C.T. Liu, C.R. Brooks, Intermetallics 13 (2005) [6] G.Y. Wang, P.K. Liaw, W.H. Peter, B. Yang, M. Freels, Y. Yokoyama, M.L. Benson, B.A. Green, T.A. Saleh, R.L. McDaniels, R.V. Steward, R.A. Buchanan, C.T. Liu, C.R. Brooks, Intermetallics 12 (2004) [7] H.H. Liebermann, in: F.E. Luborsky (Ed.), Amorphous Metallic Alloys, Butterworths, London, 1983, pp [8] E. Illeková, M. Jergel, P. Duhaj, A. Inoue, Mater. Sci. Eng. A (1997) [9] O.P. Bobrov, V.A. Khonik, K. Kitagawa, S.N. Laptev, J. Non-Cryst. Solids 342 (2004) [10] C.A. Schuh, T.G. Nieh, J. Mater. Res. 19 (2004) [11] A. Inoue, W. Zhang, T. Zhang, K. Kurosaka, Mater. Trans. 42 (2001) [12] D.C.C. Lam, A.C.M. Chong, Mater. Sci. Eng. A. 318 (2001) [13] M.J. Mayo, R.W. Siegel, A. Narayanasami, W.D. Nix, J. Mater. Res. 5 (1990) [14] A. Slipenyuk, J. Eckert, Scr. Mater. 50 (2004) [15] C. Nagel, K. Rätzke, E. Schmidke, J. Wolf, U. Geyer, F. Faupel, Phys. Rev. B. 57 (1998) [16] W.H. Jiang, M. Atzmon, Acta Mater. 53 (2005) [17] A. Concustell, G. Alcalá, S. Mato, T.G. Woodcock, A. Gebert, J. Eckert, M.D. Baró, Intermetallics 13 (2005) [18] Z.H. Zhang, J.X. Xie, Mater. Sci. Eng. A. 407 (2005) [19] U. Ramamurty, M.L. Lee, J. Basu, Y. Li, Scr. Mater. 47 (2002) [20] P. Murah, U. Ramamurty, Acta Mater. 53 (2005) [21] W.H. Jiang, M. Atzmon, J. Mater. Res. 18 (2003) [22] W.J. Wright, R. Saha, W.D. Nix, Mater. Trans. JIM 42 (2001) [23] W.J. Wright, R.B. Schwarz, W.D. Nix, Mater. Sci. Eng. A (2001) [24] W.H. Jiang, G.J. Fan, F.X. Liu, G.Y. Wang, H. Choo, P.K. Liaw, J. Mater. Res., in press.
New Cu-based Bulk Metallic Glasses with High Strength of 2000 MPa
Materials Science Forum Online: 2004-03-15 ISSN: 1662-9752, Vols. 449-452, pp 945-948 doi:10.4028/www.scientific.net/msf.449-452.945 2004 Trans Tech Publications, Switzerland New Cu-based Bulk Metallic
More informationQ. S. Zhang 1, W. Zhang 1; *, X. M. Wang 1, Y. Yokoyama 1, K. Yubuta 1 and A. Inoue 2
Materials Transactions, Vol. 49, No. 9 (2008) pp. 2141 to 2146 #2008 The Japan Institute of Metals EXPRESS REGULAR ARTICLE Structure, Thermal Stability and Mechanical Properties of Zr 65 Al 7:5 Ni 10 Cu
More informationCompression-Compression Fatigue and Fracture Behaviors of Zr 50 Al 10 Cu 37 Pd 3 Bulk-Metallic Glass
Materials Transactions, Vol. 48, No. 7 (2007) pp. 1828 to 1833 Special Issue on Bulk Metallic Glasses Selected Papers from the Fifth International Conference on Bulk Metallic Glasses (BMGV) #2007 The Japan
More informationFe-B-Si-Nb Bulk Metallic Glasses with High Strength above 4000 MPa and Distinct Plastic Elongation
Materials Transactions, Vol. 45, No. 4 (2004) pp. 1214 to 1218 Special Issue on Bulk Amorphous, Nano-Crystalline and Nano-Quasicrystalline Alloys-V #2004 The Japan Institute of Metals Fe-B-Si-Nb Bulk Metallic
More informationFormation and Soft Magnetic Properties of Co Fe Si B Nb Bulk Glassy Alloys
Materials Transactions, Vol. 43, No. 5 (2002) pp. 1230 to 1234 c 2002 The Japan Institute of Metals EXPRESS REGULAR ARTICLE Formation and Soft Magnetic Properties of Co Fe Si B Nb Bulk Glassy Alloys Akihisa
More informationCompression stress induced flow temperature reduction in a bulk Zr 41:2 Ti 13:8 Cu 12:5 Ni 10:0 Be 22:5 metallic glass
Scripta Materialia 47 (2002) 787 791 www.actamat-journals.com Compression stress induced flow temperature reduction in a bulk Zr 41:2 Ti 13:8 Cu 12:5 Ni 10:0 Be 22:5 metallic glass H.J. Jin, X.J. Gu, F.
More informationEffects of silicon and chromium additions on glass forming ability and microhardness of Co-based bulk metallic glasses
Indian Journal of Engineering & Materials Sciences Vol. 21, February 2014, pp. 111-115 Effects of silicon and chromium additions on glass forming ability and microhardness of Co-based bulk metallic glasses
More informationTHERMAL AND ELASTIC PROPERTIES OF CU-ZR-BE BULK-METALLIC-GLASS FORMING ALLOYS
Chapter 5 THERMAL AND ELASTIC PROPERTIES OF CU-ZR-BE BULK-METALLIC-GLASS FORMING ALLOYS The compositional dependence of thermal and elastic properties of Cu-Zr-Be ternary bulk-metallic-glass forming alloys
More informationMechanical Properties of Bulk Metallic Glasses and composites
Mechanical Properties of Bulk Metallic Glasses and composites M.L. Lee 1 *, Y. Li 1, 2, Y. Zhong 1, C.W. Carter 1, 3 1. Advanced Materials for Micro- and Nano- Systems Programmes, Singapore-MIT Alliance,
More informationEffect of Nb content on the microstructure and mechanical properties of Zr Cu Ni Al Nb glass forming alloys
Journal of Alloys and Compounds 403 (2005) 239 244 Effect of Nb content on the microstructure and mechanical properties of Zr Cu Ni Al Nb glass forming alloys Y.F. Sun a, C.H. Shek b,, B.C. Wei c, W.H.
More informationCrack initiation and fracture features of Fe Co B Si Nb bulk metallic glass during compression
Focussed on Crack Paths Crack initiation and fracture features of Fe Co B Si Nb bulk metallic glass during compression S. Lesz, A. Januszka, S. Griner, R. Nowosielski Silesian University of Technology,
More informationIn Situ Thermographic Imaging of Shear Bands During Tensile Testing. of a Bulk Metallic Glass. and R.V. Leon 3
In Situ Thermographic Imaging of Shear Bands During Tensile Testing of a Bulk Metallic Glass M.L. Morrison 1*, B. Yang 1, C.T. Liu 2, P.K. Liaw 1, R.A. Buchanan 1, C.A. Carmichael 2, and R.V. Leon 3 1.
More informationChapter 1. Institute of Technology in 1960 [1]. The first metallic glass system, Au 75 Si 25, was found
Chapter 1 Introduction The first metallic glass was reported by Klement and Duwez at the California Institute of Technology in 1960 [1]. The first metallic glass system, Au 75 Si 25, was found during an
More informationSoft Magnetic Properties of Nanocystalline Fe Si B Nb Cu Rod Alloys Obtained by Crystallization of Cast Amorphous Phase
Materials Transactions, Vol. 43, No. 9 (2002) pp. 2337 to 2341 c 2002 The Japan Institute of Metals EXPRESS REGULAR ARTICLE Soft Magnetic Properties of Nanocystalline Fe Si B Nb Cu Rod Alloys Obtained
More informationSupporting Online Material for
www.sciencemag.org/cgi/content/full/315/5817/1385/dc1 Supporting Online Material for Super Plastic Bulk Metallic Glasses at Room Temperature Yan Hui Liu, Gang Wang, Ru Ju Wang, De Qian Zhao, Ming Xiang
More informationState Key Laboratory for Powder Metallurgy, Central South University, Changsha , China
Advances in Materials Science and Engineering, Article ID 21593, 5 pages http://dx.doi.org/1.1155/214/21593 Research Article Investigation of Mechanical Properties and Plastic Deformation Behavior of (Ti
More informationChapter 1 1 CHAPTER 1. INTRODUCTION Historical background and development of bulk metallic glasses
Chapter 1 1 CHAPTER 1. INTRODUCTION 1.1. Historical background and development of bulk metallic glasses Glass is any material that can be cooled from a liquid to a solid without crystallizing. Most metals
More informationSynthesis of Ti-Based Bulk Metallic Glass Composites Containing WC Particles
Materials Transactions, Vol. 46, No. 12 (2005) pp. 2963 to 2967 Special Issue on Materials Science of Bulk Metallic Glasses #2005 The Japan Institute of Metals Synthesis of Ti-Based Bulk Metallic Glass
More informationFabrication and investigation of intermetallic compound-glassy phase composites having tensile ductility
Fabrication and investigation of intermetallic compound-glassy phase composites having tensile ductility The purpose The purpose of the proposed study was to produce in-situ ductile crystalline intermetallic
More informationFormation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability
Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability YANG Ying-jun( 杨英俊 ) 1, 2, KANG Fu-wei( 康福伟 ) 1, XING Da-wei( 邢大伟 ) 1, SUN Jian-fei( 孙剑飞 ) 1, SHEN
More informationRotation mechanism of shear fracture induced by high plasticity in Ti-based nano-structured composites containing ductile dendrites
Scripta Materialia 52 (2005) 945 949 www.actamat-journals.com Rotation mechanism of shear fracture induced by high plasticity in Ti-based nano-structured composites containing ductile dendrites Z.F. Zhang
More informationCharacteristics of Shear Bands and Fracture Surfaces of Zr 65 Al 7:5 Ni 10 Pd 17:5 Bulk Metallic Glass
Materials Transactions, Vol. 46, No. 12 (2005) pp. 2870 to 2874 Special Issue on Materials Science of Bulk Metallic Glasses #2005 The Japan Institute of Metals Characteristics of Shear Bands and Fracture
More informationCentimeter-scale-diameter Co-based bulk metallic glasses with fracture strength exceeding 5000 MPa
Article SPECIAL ISSUE Bulk Metallic Glasses December 011 Vol.56 No.36: 3973977 doi: 10.1007/s11434-011-4765-8 Centimeter-scale-diameter Co-based bulk metallic glasses with fracture strength exceeding 5000
More informationION IRRADIATION-INDUCED NANO-CRYSTALLIZATION METALLIC GLASSES (AMORPHOUS METAL)
ION IRRADIATION-INDUCED NANO-CRYSTALLIZATION METALLIC GLASSES (AMORPHOUS METAL) A Senior Scholars Thesis by MINH HONG TRAN Submitted to Honors and Undergraduate Research Texas A&M University in partial
More informationKeywords. Aluminium-based amorphous alloys; melt spinning; crystallization behaviour; microhardness.
PRAMANA c Indian Academy of Sciences Vol. 65, No. 4 journal of October 2005 physics pp. 745 751 Effect of rare-earth elements on nanophase evolution, crystallization behaviour and mechanical properties
More informationEffects of Glass-Forming Metallic Film on the Fatigue Behavior of C-2000 Ni-Based Alloy
Mater. Res. Soc. Symp. Proc. Vol. 903E 2006 Materials Research Society 0903-Z14-13.1 Effects of Glass-Forming Metallic Film on the Fatigue Behavior of C-2000 Ni-Based Alloy F. X. Liu 1, C. L. Chiang 1,2,
More informationViscous flow behavior and thermal properties of bulk amorphous Mg 58 Cu 31 Y 11 alloy
Intermetallics 15 (2007) 1303e1308 www.elsevier.com/locate/intermet Viscous flow behavior and thermal properties of bulk amorphous Mg 58 Cu 31 Y 11 alloy Y.C. Chang a, T.H. Hung a, H.M. Chen a, J.C. Huang
More informationDifference in compressive and tensile fracture mechanisms of Zr 59 Cu 20 Al 10 Ni 8 Ti 3 bulk metallic glass
Acta Materialia 51 (2003) 1167 1179 www.actamat-journals.com Difference in compressive and tensile fracture mechanisms of Zr 59 Cu 20 Al 10 Ni 8 Ti 3 bulk metallic glass Z.F. Zhang, J. Eckert, L. Schultz
More informationA new Ti Zr Hf Cu Ni Si Sn bulk amorphous alloy with high glass-forming ability
Journal of Alloys and Compounds 427 (2007) 171 175 A new Ti Zr Hf Cu Ni Si Sn bulk amorphous alloy with high glass-forming ability Y.J. Huang a, J. Shen a,, J.F. Sun a, X.B. Yu b, a School of Materials
More informationInstitute of Experimental Physics, Slovak Academy of Sciences, Košice, Slovakia 2)
Acta Metall. Slovaca Conf. 191 FRACTURE SURFACE MORPHOLOGY OF Pd 40 Cu 30 Ni 10 P 20 AMORPHOUS ALLOY Alena Juríková 1)*, Jozef Miškuf 1), Kornel Csach 1), Elena Tabachnikova 2), Vladimír Bengus 2) 1) Institute
More informationConsolidation of [(Fe 0:5 Co 0:5 ) 0:75 Si 0:05 B 0:2 ] 96 Nb 4 Metallic Glassy Powder by SPS Method* 1
Materials Transactions, Vol. 50, No. 9 (2009) pp. 2264 to 2269 #2009 The Japan Institute of Metals Consolidation of [(Fe 0:5 Co 0:5 ) 0:75 Si 0:05 B 0:2 ] 96 Nb 4 Metallic Glassy Powder by SPS Method*
More informationLocal microstructure evolution at shear bands in metallic glasses with nanoscale phase separation
Supplementary Information Local microstructure evolution at shear bands in metallic glasses with nanoscale phase separation Jie He 1,2, Ivan Kaban 2,3, Norbert Mattern 2, Kaikai Song 2, Baoan Sun 2, Jiuzhou
More informationGlass-Forming Ability and Competitive Crystalline Phases for Lightweight Ti-Be Based Alloys
Glass-Forming Ability and Competitive Crystalline Phases for Lightweight Ti-Be Based Alloys Y. ZHANG, W.G. ZHANG, J.P. LIN, G.J. HAO, G.L. CHEN, and P.K. LIAW The glass-forming ability (GFA) for the Ti-Be
More informationCrystallization behavior of the Zr 63 Al 7.5 Cu 17.5 Ni 10 B 2 amorphous alloy during isothermal annealing
Intermetallics 13 (2005) 907 911 www.elsevier.com/locate/intermet Short communication Crystallization behavior of the Zr 63 Al 7.5 Cu 17.5 Ni 10 B 2 amorphous alloy during isothermal annealing J.S.C. Jang
More informationCo-based soft magnetic bulk glassy alloys optimized for glass-forming ability and plasticity
Bull. Mater. Sci., Vol. 39, No. 3, June 2016, pp. 691 695. DOI 10.1007/s12034-016-1207-x c Indian Academy of Sciences. Co-based soft magnetic bulk glassy alloys optimized for glass-forming ability and
More informationVariation of Hardness and Modulus across the Thickness of Zr-Cu-Al Metallic Glass Ribbons
Mater. Res. Soc. Symp. Proc. Vol. 1520 2012 Materials Research Society DOI: 10.1557/opl.2012. 1690 Variation of Hardness and Modulus across the Thickness of Zr-Cu-Al Metallic Glass Ribbons Z. Humberto
More informationTwin-Roll Strip Casting of Iron-Base Amorphous Alloys
Materials Transactions, Vol. 48, No. 7 (2007) pp. 1584 to 1588 Special Issue on Bulk Metallic Glasses Selected Papers from the Fifth International Conference on Bulk Metallic Glasses (BMGV) #2007 The Japan
More informationSynthesis and Fundamental Properties of Cu-Based Bulk Glassy Alloys in Binary and Multi-component Systems
Materials Transactions, Vol. 45, No. 4 (2004) pp. 1153 to 1162 Special Issue on Bulk Amorphous, Nano-Crystalline and Nano-Quasicrystalline Alloys-V #2004 The Japan Institute of Metals OVERVIEW Synthesis
More informationGlass-forming ability of melt-spun multicomponent (Ti, Zr, Hf) (Cu, Ni, Co) Al alloys with equiatomic substitution
Journal of Non-Crystalline Solids 347 (2004) 166 172 www.elsevier.com/locate/jnoncrysol Glass-forming ability of melt-spun multicomponent (Ti, Zr, Hf) (Cu, Ni, Co) Al alloys with equiatomic substitution
More informationTitle containing nano-crystalline. Author(s) Matsumoto, Naoki; Matsumoto, Ryosuk. Citation Journal of Non-Crystalline Solids (
Title Estimation of shear-banding containing nano-crystalline resista particl Author(s) Matsumoto, Naoki; Matsumoto, Ryosuk Citation Journal of Non-Crystalline Solids ( Issue Date 2009-01 URL http://hdl.handle.net/2433/88965
More informationDual phase bulk metallic glasses fabricated by hot pressing using two different types of glassy alloy powder
JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS Vol. 17, No. 7-8, July August 2015, p. 1026-1031 Dual phase bulk metallic glasses fabricated by hot pressing using two different types of glassy alloy
More informationMechanical and Magnetic Properties of New (Fe,Co,Ni) B Si Ta Bulk Glassy Alloys
Acta Metall. Sin. (Engl. Lett.), 2017, 30(7), 659 664 DOI 10.1007/s40195-017-0576-5 Mechanical and Magnetic Properties of New (Fe,Co,Ni) B Si Ta Bulk Glassy Alloys Yao-Xiang Geng 1 Xin Lin 2 Yu-Xin Wang
More informationMicrostructure evolution and mechanical properties of Cu 46 Zr 47 Al 7 bulk metallic glass composite containing CuZr crystallizing phases
Materials Science and Engineering A 467 (2007) 139 145 Microstructure evolution and mechanical properties of Cu 46 Zr 47 Al 7 bulk metallic glass composite containing CuZr crystallizing phases F. Jiang
More informationStructure and magnetic properties of Fe 36 Co 36 B 19 Si 5 Nb 4 bulk metallic glasses
of Achievements in Materials and Manufacturing Engineering VOLUME 30 ISSUE 2 October 2008 Structure and magnetic properties of Fe 36 Co 36 B 19 Si 5 Nb 4 bulk metallic glasses R. Nowosielski, R. Babilas*
More informationStudy of glass transition of metallic glasses by temperature-modulated differential scanning calorimetry (MDSC)
Thermochimica Acta 357±358 (2000) 65±69 Study of glass transition of metallic glasses by temperature-modulated differential scanning calorimetry (MDSC) Z.P. Lu a,y.li a,*, S.C. Ng b, Y.P. Feng b a Department
More informationSTUDYING AMORPHOUS-CRYSTALLINE TRANSITIONS IN POWDERS CAUSED BY BALL-MILLING
STUDYING AMORPHOUS-CRYSTALLINE TRANSITIONS IN POWDERS CAUSED BY BALL-MILLING K. Tomolya 1, D. Janovszky 2, A. Sycheva 3, A. Roósz 4 1 Ph.D. Research fellow, 2 Ph.D. Senior research fellow, 3 Ph.D. Research
More informationDefense Technical Information Center Compilation Part Notice
UNCLASSIFIED Defense Technical Information Center Compilation Part Notice ADP014286 TITLE: Formation, Mechanical and Electrical Properties of Ni-based Amorphous Alloys and their Nanocrystalline Structure
More informationLaser Shock Peening of Bulk Metallic Glasses
Final Report Laser Shock Peening of Bulk Metallic Glasses MSE 516: Mechanical Metallurgy Spring 2008 Submitted on April 24 th, 2008 Deepak Rajput Graduate Research Assistant Center for Laser Applications
More informationCorrosion Behavior of Cu Zr Ti Nb Bulk Glassy Alloys
Materials Transactions, Vol. 44, No. 4 (3 pp. 749 to 753 #3 The Japan Institute of Metals Corrosion Behavior of Cu Bulk Glassy Alloys Chunling Qin 1; *, Katsuhiko Asami 1, Tao Zhang 1, Wei Zhang 2 and
More informationFabrication of Mg-based bulk metallic glasses by pressure die casting method
Indian Journal of Engineering & Materials Sciences Vol. 21, June 2014, pp. 259-264 Fabrication of Mg-based bulk metallic glasses by pressure die casting method A Borowski*, A Guwer, A Gawlas-Mucha, R Babilas
More informationProperties of the Ti 40 Zr 10 Cu 36 Pd 14 BMG Modified by Sn and Nb Additions Anna Sypien, Mihail Stoica, and Tomasz Czeppe
JMEPEG (2016) 25:800 808 The Author(s). This article is published with open access at Springerlink.com DOI: 10.1007/s11665-016-1898-6 1059-9495/$19.00 Properties of the Ti 40 Zr 10 Cu 36 Pd 14 BMG Modified
More informationMechanical properties of Ti-based glassy and nanocomposite alloys. J. Sort Departament de Física Universitat Autònoma de Barcelona
Mechanical properties of Ti-based glassy and nanocomposite alloys J. Sort Departament de Física Universitat Autònoma de Barcelona 1 Collaborators Universitat Autònoma de Barcelona, Spain A. Hynowska, J.
More informationNucleation and Growth in Undercooled Melts of Bulk-Metallic-Glass Forming Zr 60 Ni 25 Al 15 Alloy
Materials Transactions, Vol. 46, No. 12 (2005) pp. 2762 to 2767 Special Issue on Materials Science of Bulk Metallic Glasses #2005 The Japan Institute of Metals Nucleation and Growth in Undercooled Melts
More informationELEVATED-TEMPERATURE CREEP-FATIGUE CRACK-GROWTH BEHAVIOR OF NICKEL- BASED HAYNES R-41, HAYNES 230 and HASTELLOY X AllOYS
ELEVATED-TEMPERATURE CREEP-FATIGUE CRACK-GROWTH BEHAVIOR OF NICKEL- BASED HAYNES R-41, HAYNES 230 and HASTELLOY X AllOYS S.Y. Lee 1, P.K. Liaw 1, Y.L. Lu 1, D. Fielden 1, L.M. Pike 2 and D.L. Klarstrom
More informationPorous Bulk Metallic Glass Fabricated by Powder Consolidation
Journal of Minerals & Materials Characterization & Engineering, Vol. 7, No.2, pp 97-104, 2008 jmmce.org Printed in the USA. All rights reserved Porous Bulk Metallic Glass Fabricated by Powder Consolidation
More informationChapter 2 9 CHAPTER 2. MACHINING OF THE BMG. Bulk metallic glass (BMG) alloys are metal alloys with no long-range atomic
Chapter 2 9 CHAPTER 2. MACHINING OF THE BMG 2.1. Introduction Bulk metallic glass (BMG) alloys are metal alloys with no long-range atomic order. A variety of rapid solidification techniques are used to
More informationHahn-Meitner-Institut Berlin, Glienicker Str. 100, D-14109, Berlin, Germany
Journal of Metastable and Nanocrystalline Materials Vols. 20-21 (2004) pp. 35-40 online at http://www.scientific.net (2004) Trans Tech Publications, Switzerland Crystallization of Pd 40 Cu 30 Ni 10 P 20
More informationmetallic glasses (amorphous alloys)
A brief introduction to metallic glasses (amorphous alloys) Sheng Guo Assistant Professor Materials and Manufacturing Technology Department E-mail: sheng.guo@chalmers.se Outline What are metallic glasses
More informationHydrogen Permeation of Ni-Nb-Zr Metallic Glasses in a Supercooled Liquid State
Materials Transactions, Vol. 47, No. 12 (2006) pp. 2991 to 2996 #2006 The Japan Institute of Metals Hydrogen Permeation of Ni-Nb-Zr Metallic Glasses in a Supercooled Liquid State Shin-ichi Yamaura, Shuhei
More informationResearch Article A Centimeter-Sized Quaternary Ti-Zr-Be-Ag Bulk Metallic Glass
Advances in Materials Science and Engineering, Article ID 192187, 5 pages http://dx.doi.org/10.1155/2014/192187 Research Article A Centimeter-Sized Quaternary Ti-Zr-Be-Ag Bulk Metallic Glass S. F. Zhao,
More informationFATIGUE-INDUCED PHASE FORMATION AND ITS DEFORMATION BEHAVIOR IN A COBALT-BASED SUPERALLOY
Copyright JCPDS - International Centre for Diffraction Data 2005, Advances in X-ray Analysis, Volume 48. 123 FATIGUE-INDUCED PHASE FORMATION AND ITS DEFORMATION BEHAVIOR IN A COBALT-BASED SUPERALLOY M.
More informationChinese Academy of Sciences, Shenyang, China. Baltimore, MD 21218, USA. First Published: May 2008 PLEASE SCROLL DOWN FOR ARTICLE
This article was downloaded by:[national Institute for Materials Science] On: 21 May 2008 Access Details: [subscription number 776099147] Publisher: Taylor & Francis Informa Ltd Registered in England and
More informationDEFORMATION BEHAVIOR AND FRACTOGRAPHIC FEATURES OF DUCTILE Cu 47
Deformation Rev.Adv.Mater.Sci. behavior 18(2008) and fractographic 527-533 features of ductile Cu 47 bulk metallic glass 527 DEFORMATION BEHAVIOR AND FRACTOGRAPHIC FEATURES OF DUCTILE Cu 47 BULK METALLIC
More informationFillability and Imprintability of High-strength Ni-based Bulk Metallic Glass Prepared by the Precision Die-casting Technique
Materials Transactions, Vol. 45, No. 4 (2004) pp. 1239 to 1244 Special Issue on Bulk Amorphous, Nano-Crystalline and Nano-Quasicrystalline Alloys-V #2004 The Japan Institute of Metals Fillability and Imprintability
More informationBulk Metallic Glasses - Characteristics and Possibilities
Downloaded from orbit.dtu.dk on: Apr 03, 2019 Bulk Metallic Glasses - Characteristics and Possibilities Eldrup, Morten Mostgaard; Byrne, Cormac Publication date: 2009 Document Version Publisher's PDF,
More informationResearch Article Nanocrystalline Phase Formation inside Shear Bands of Pd-Cu-Si Metallic Glass
Advances in Materials Science and Engineering, Article ID 490181, 4 pages http://dx.doi.org/10.1155/2014/490181 Research Article Nanocrystalline Phase Formation inside Shear Bands of Pd-Cu-Si Metallic
More informationMechanical properties of Ti-based glassy and nanocomposite alloys. J. Sort Departament de Física Universitat Autònoma de Barcelona
Mechanical properties of Ti-based glassy and nanocomposite alloys J. Sort Departament de Física Universitat Autònoma de Barcelona 1 Collaborators Universitat Autònoma de Barcelona, Spain A. Hynowska, J.
More informationEffect of Cu and P on the Crystallization Behavior of Fe-Rich Hetero-Amorphous FeSiB Alloy
Materials Transactions, Vol. 50, No. 11 (2009) pp. 2515 to 2520 #2009 The Japan Institute of Metals Effect of Cu and P on the Crystallization Behavior of Fe-Rich Hetero-Amorphous FeSiB Alloy Liying Cui
More informationEnhancement of glass-forming ability of FeCoNiBSiNb bulk glassy alloys with superhigh strength and good soft-magnetic properties
JOURNAL OF APPLIED PHYSICS 102, 023515 2007 Enhancement of glass-forming ability of FeCoNiBSiNb bulk glassy alloys with superhigh strength and good soft-magnetic properties Baolong Shen a and Chuntao Chang
More information3.1. Chapter 3 - ZrTi Based Be Bearing Glasses Optimized for High Thermal Stability
3.1 Chapter 3 - ZrTi Based Be Bearing Glasses Optimized for High Thermal Stability and Thermoplastic Formability We flesh out the details of the alloy development story in this chapter with a thorough
More informationAlloy by Synchrotron Radiation
1 Analysis of Glass-forming Alloy by Synchrotron Radiation T. A. Başer /NIS Università degli Studi di Torino/ITALY European School-BMGs/ 13-1 Sept /Torino-ITALY Fe-based Bulk Metallic Glasses with Y Addition
More informationPhase transformation kinetics and microstructure of NiTi shape memory alloy: effect of hydrostatic pressure
Bull. Mater. Sci., Vol., No. 4, August 2017, pp. 799 803 DOI.07/s12034-017-1413-1 Indian Academy of Sciences Phase transformation kinetics and microstructure of NiTi shape memory alloy: effect of hydrostatic
More informationThis article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and
This article appeared in a journal published by Elsevier. The attached copy is furnished to the author for internal non-commercial research and education use, including for instruction at the authors institution
More informationBulk Metallic Glasses
2018 Spring Advanced Physical Metallurgy Bulk Metallic Glasses 03.28.2018 Eun Soo Park Office: 33 313 Telephone: 880 7221 Email: espark@snu.ac.kr Office hours: by appointment 1 * Development strategy of
More informationThermodynamics and kinetics of the Mg 65 Cu 25 Y 10 bulk metallic glass forming liquid
JOURNAL OF APPLIED PHYSICS VOLUME 83, NUMBER 8 15 APRIL 1998 Thermodynamics and kinetics of the Mg 65 Cu 25 Y 10 bulk metallic glass forming liquid R. Busch, a) W. Liu, and W. L. Johnson California Institute
More informationAmorphous Metallic Alloys. 1.General features 2.Structure 3.Producing 4. Properties
Amorphous Metallic Alloys 1.General features 2.Structure 3.Producing 4. Properties Amorphous metallic alloys or metallic glasses have emerged as a new class of engineering materials after vitrficationof
More informationThe Effect of SiC Whisker Addition on Bulk Amorphous Formation Abilities of La-Transition Metal-Al System
The Effect of SiC Whisker Addition on Bulk Amorphous Formation Abilities of La-Transition Metal-Al System Takahito KOJIMA 1, Shuji AZUMO 2 and Katsuhisa NAGAYAMA 3 1 Graduate Student, Shibaura Institute
More informationTexture and Microstructure of Ti-Ni Melt-Spun Shape Memory Alloy Ribbons
Materials Transactions, Vol. 45, No. 2 (2004) pp. 214 to 218 Special Issue on Materials and Devices for Intelligent/Smart Systems #2004 The Japan Institute of Metals Texture and Microstructure of Ti-Ni
More informationMICROSTRUCTURE AND PROPERTIES OD RAPID SOLIDIFIED AL-SI-FE AND AL-SI-FE-CR ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION. Filip PRŮŠA*, Dalibor VOJTĚCH
MICROSTRUCTURE AND PROPERTIES OD RAPID SOLIDIFIED AL-SI-FE AND AL-SI-FE-CR ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION Filip PRŮŠA*, Dalibor VOJTĚCH Department of Metals and Corrosion Engineering, Institute
More informationEnhanced Amorphization by Sn Substitution for Si and B in the Ball-milled Ti 50 Ni 22 Cu 18 Al 4 Si 4 B 2 Alloy. L.C. Zhang, Z.Q. Shen, J.
Journal of Metastable and Nanocrystalline Materials Vols. 20-21 (2004) pp. 488-493 online at http://www.scientific.net Journal 2004 Citation Trans Tech (to Publications, be inserted by Switzerland the
More informationHypereutectic aluminium alloy tubes with graded distribution of Mg Si particles prepared by centrifugal casting
Ž. Materials and Design 1 000 149 153 Hypereutectic aluminium alloy tubes with graded distribution of Mg Si particles prepared by centrifugal casting Jian Zhang a,b,, Zhongyun Fan a, Yuqing Wang b, Benlian
More informationChapter 2. Metallic Glass Honeycombs. Introduction
8 Chapter 2 Metallic Glass Honeycombs Introduction Due to the fact that they undergo a glass transition and are stable as an undercooled liquid over a large range of temperatures for a significant amount
More informationA Study on the Formation of Magnetic Refrigerant La(Fe,Si) 13
A Study on the Formation of Magnetic Refrigerant La(Fe,Si Compounds by Spark Plasma Sintering H. Tsuji, A.T. Saito, T. Kobayashi, S. Sakurada Corporate Research & Development Center, Toshiba Corp. Kawasaki,
More informationThe effects of trace Sc and Zr on microstructure and internal friction of Zn Al eutectoid alloy
Materials Science and Engineering A 370 (2004) 172 176 The effects of trace Sc and Zr on microstructure and internal friction of Zn Al eutectoid alloy B.H. Luo, Z.H. Bai, Y.Q. Xie Department of Materials
More informationMachining of a Zr Ti Al Cu Ni metallic glass
Scripta Materialia 50 (2004) 583 588 www.actamat-journals.com Machining of a Zr Ti Al Cu Ni metallic glass Mustafa Bakkal a, Albert J. Shih b, Ronald O. Scattergood c, *, C.T. Liu d a Department of Mechanical
More informationDevitrification of rapidly quenched Al Cu Ti amorphous alloys
Bull. Mater. Sci., Vol. 26, No. 5, August 2003, pp. 553 558. Indian Academy of Sciences. Devitrification of rapidly quenched Al Cu Ti amorphous alloys D K MISRA, R S TIWARI and O N SRIVASTAVA* Department
More informationBulk Metallic Glasses, Synthesis, Thermal and Mechanical Characterizations.
Author manuscript, published in "Processing and Fabrication of Advanced Materials XIII, Singapore : Singapore (2004)" 1 Bulk Metallic Glasses, Synthesis, Thermal and Mechanical Characterizations. Jean-Louis
More informationArticle. Department of Physics, Jining University, Qufu, , China; 2
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 Article Effect of Niobium and Yttrium modified Ti-based bulk amorphous alloy
More informationType II twins and their deformation characteristics in 18R martensite in a Cu Zn Al alloy
March 1998 Materials Letters 34 1998 351 355 Type II twins and their deformation characteristics in 18R martensite in a Cu Zn Al alloy Jianxin Zhang a,), Wei Cai a, Yufeng Zheng a,b, Liancheng Zhao a a
More informationStrength asymmetry of ductile dendrites reinforced Zr- and Ti-based composites
Strength asymmetry of ductile dendrites reinforced Zr- and Ti-based composites F.F. Wu and Z.F. Zhang a) Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy
More informationBulk Metallic Glasses
2016 Spring Advanced Physical Metallurgy Bulk Metallic Glasses 03.16.2016 Eun Soo Park Office: 33 313 Telephone: 880 7221 Email: espark@snu.ac.kr Office hours: by appointment 1 * Development strategy of
More informationAnisotropic Mechanical Properties of Pr(Co,In) 5 -type Compounds and Their Relation to Texture Formation in Die-upset Magnets
Journal of Magnetics 16(3), 220-224 (2011) http://dx.doi.org/10.4283/jmag.2011.16.3.220 Anisotropic Mechanical Properties of Pr(Co,In) 5 -type Compounds and Their Relation to Texture Formation in Die-upset
More informationInstitute of Physics and Chemistry of Metals, University of Silesia, Bankowa 12, Katowice, Poland
J. Phys. IV France 11 (2001) Pr8-345 EDP Sciences, Les Ulis Structure of melt spun 2 5Ti 5 ocu 2 5 ribbons studied by X-ray diffraction T. Goryczka, M. Karolus, P. Ochin 1 and H. Morawiec Institute of
More informationBulk metallic glasses (BMGs) have shown unique. Spheroidization behavior of dendritic b.c.c. phase in Zr-based β-phase composite
Spheroidization behavior of dendritic b.c.c. phase in Zr-based β-phase composite *Sun Guoyuan 1, Li Ping 2, Chen Wei 3 and Song Xuding 4 1. School of Mechanical Engineering, North China University of Water
More informationSupplementary Information
Supplementary Information Title: Strong, ductile, and thermally stable Cu-based metal-intermetallic nanostructured composites Authors: Keith J. Dusoe, Sriram Vijayan, Thomas R. Bissell, Jie Chen, Jack
More informationCORRELATION BETWEEN INTERNAL STATES AND STRENGTH IN BULK METALLIC GLASS
CORRELATION BETWEEN INTERNAL STATES AND STRENGTH IN BULK METALLIC GLASS J. Tan 1, 2, 3,*, C.J. Li 1, 2, Y.H. Jiang 1, R. Zhou 1, J. Eckert 2, 3, 1 School of Materials Science and Engineering, Kunming University
More informationEffect of cyclic recovery heat treatment on surface recrystallization of a directionally solidified superalloy
Effect of cyclic recovery heat treatment on surface recrystallization of a directionally solidified superalloy Guang XIE 1, Jian ZHANG 1, 2, Lang-hong LOU 1 1. Superalloys Division, Institute of Metal
More informationWeight (%) Temperature ( C)
Weight (%) 100 80 60 40 20 0 0 100 200 300 400 500 600 Temperature ( C) Supplementary Figure 1. Thermal analysis of (UPyU) 3 TMP. Thermogravimetric analysis (TGA) curve of (UPyU) 3 TMP from 25 to 600 C.
More informationÓThe Author(s). This article is published with open access at Springerlink.com DOI: /s /$19.00
JMEPEG (2014) 23:2241 2246 ÓThe Author(s). This article is published with open access at Springerlink.com DOI: 10.1007/s11665-014-0972-1 1059-9495/$19.00 Structure, Properties, and Crystallization of Mg-Cu-Y-Zn
More informationMechanical Properties and Deformation Behavior of Bulk Metallic Glasses
Metals 2013, 3, 1-22; doi:10.3390/met3010001 Review OPEN ACCESS metals ISSN 2075-4701 www.mdpi.com/journal/metals/ Mechanical Properties and Deformation Behavior of Bulk Metallic Glasses Dmitri V. Louzguine-Luzgin
More information