DONIT 4AS Specialy designed anti-stick coating A CLEVER CHOICE GRAFILIT IQ

DONIT 4AS Specialy designed anti-stick coating A CLEVER CHOICE GRAFILIT IQ

/ DONIT A clever choice A special engineered high quality sheet made of expanded natural graphite foil and reinforced by an expanded stainless (316L) steel insert with outstanding anti-stick performance. Excellent leakage performance min ] Leak rate [ml 1,2 - Long Term High Temperature Leakage test 1 Flange: EN 192-1 DN4 PN4 Gasket: 92 x 49 x 1.mm,8 Surface stress: 3MPa Medium: N2 Pressure: 4bars Temperature: 3 C,6 Time: 7h Leak rate Temperature,4 36 3 24 18 12,2 6 1 2 3 4 6 7 Time [h] Leak rate [mg/s/m] - High Temperature Lekage Test,12 Gasket size: 92 x 49 x 1.mm Surface stress: 3MPa,1 Medium: N2 Pressure: 4bars,8 36 3 24,6 Leak rate [mg/s/m] 18,4 12 Composition: expanded natural graphite; (> 99%) laminated by a special process to an expanded chromium nickel-steel (1.444-AISI316L) insert Advantages Superior anti-stick performance Easy handling Excellent load distribution Excellent adaptability to irregularities or scratches on the flange surface No hardening or ageing due to absence of binders High pressure and temperature resistance even under cycling conditions Complies to Lowest Fugitive Emission regulations Complies to Fire Safe Test DVGW VP 41 and API 67,2 2 4 6 8 1 12 14 16 18 Time [s] Complies to Low Fugitive Emission regulation (TA-Luft VDI244) Leak rate [mbar l/s/m] 3,E-4 2,E-4 2,E-4 1,E-4 1,E-4,E-, Leak rate VDI 244 Initial Surface Pressure : 4 MPa Joint Temperature : 3 C Residual Surface Pressure: 32 MPa Achieved Leak Rate: 9.4 1^- mbar l/s/m,e+ 1 1 2 Excellent thermo mechanical performance 1 1 Deformation - MPa/2 C 8 7 6 Surface Preessure [MPa] 1 1 Grafilit EM Hot Compression Test - MPa / 3 C Stress [MPa] 6 Time [ h ] 8 7 6 Surface Pressure [MPa] 2 4 2 4 3 3 σ [MPa] 3 2 3 1 4 1 2 3 4 6 Time [min] σ Vo/Bo - DIN 289-2 1 14 3 2 3 Standard Quality 1 Surface Stress 4 4 8 12 16 2 24 28 32 36 4 Temperature [ C] Standard quality 13 12 11 1 9 8 1 1 2 3 3 4 4

A clever choice DONIT DIN 289-2: Creep-compression test Outstanding anti-stick properties Deformation at 2 C 1 2 3 4 ; Surface Pressure [MPa] Deformation at 3 C/MPa/16h 3 3 Standard Quality ε ksw = 29.2 % ε ksw = 33 % ε krw = 4.3 % ε krw = 4.8 % 2 wsw wsw ε = 3.8 % ε = 1.7 % ε wrw = 2. % ε wrw = 2.8 % R =.4 mm R =.38 mm 1 1 1 Standard Quality 2 Temperature Surface Pressure 3 4 The unique composition of results in outstanding antistick properties. Removing a stuck gasket from the flange surface can be a tedious and labour intensive task that can end up damaging the flange surfaces. The amount of time spent on cleaning flanges can be significant, and in many services, the plant must remain off-line longer while the gaskets are removed, resulting in a loss of production. 2 4 6 8 1 12 14 14 114 214 314 414 14 614 714 814 914 114 Time [min] Time [min] FIRE SAFE PRODUCT Complies to Fire Safe Test DVGW VP 41 By using we enable you to optimize your resources and shorten your maintenance duration. The state of the gasket after opening the joint also shows the superb thermo mechanical properties and fire safety of. These same properties make it suitable even for the most demanding applications. 3 Leak rate Leak rate [ l/h ] Leak raate [l/h] 2 1 1, 1 1, 2 2, 3 3, 4 4, Time [ min ] Leak rate - cold 3 2 1 1 Pass criteria is leak rate under 3l/h. The average leak rate of the seal was. l/h. The leak rate was of average l/h after cooling down. Without anti-stick,2,4,6,8 1 1,2 1,4 Time [ min ] Complies to Fire Safe Test API 67 FIRESAFE API 67 with outstanding anti stick performance Made in Eu

GRAFILIT IQ GRAFILIT IQ is an engineered graphite-based composite material endowed with mechanical reinforcement and anti-stick property making it suitable for for high temperature applications. This heavy-duty material has improved surface load resistance (in particular for cycling operations) and blow-out resistance. PROPERTIES SUPERIOR EXCELENT MECHANICAL RESISTANCE THERMAL RESISTANCE SEALABILITY PERFORMANCE CHEMICAL RESISTANCE APPROPRIATE INDUSTRIES & APPLICATIONS GENERAL PURPOSE SHIPBUILDING STEAM SUPPLY POWER PLANT VERY GOOD GOOD MODERATE GAS SUPPLY CHEMICAL INDUSTRY PETROCHEMICAL INDUSTRY PAPER AND CELLULOSE INDUSTRY AUTOMOTIVE AND ENGINE BUILDING INDUSTRY REFRIGERATION AND COOLING HEATING SYSTEMS HIGH TEMP. APPLICATIONS COMPRESSORS AND PUMPS VALVES Composition Colour Approvals Expanded natural graphite (> 99%) laminated by a special process to an expanded chromium nickel-steel (1.444-AISI316L) insert Silver Fire Safe Test DVGW VP 41, API 67, TA-Luft TECHNICAL DATA Typical values for a thickness of 1. mm Density DIN 289-2 g/cm 3 1.4 Compressibility ASTM F36A % 34 Recovery ASTM F36A % Stress resistance DIN 2913 16 h, MPa, 3 C MPa >46 Tensile strength (longitudinal) ASTM F12 MPa Tensile strength (transversal) ASTM F12 MPa 9 Specific leak rate DIN 33-6 mg/(s.m) <. Thickness increase ASTM F146 Oil IRM 93, h, 1 C % 3. ASTM Fuel B, h, 23 C % 6. Compression modulus DIN 289-2 Cold compressibility: ε KSW % 28 Cold recovery: ε KRW % 4 Percentage creep relaxation DIN 289-2 Hot crepp: ε WSW/3 C % 2. Hot recovery: ε WRvW/3 C % 3. Leachable chloride content FSA NMG 22 ppm <2 Leachable fluoride content FSA NMG 23 ppm <2 Operating conditions Minimum temperature C/ F -2/-328 Continuous maximum temperature - oxidizing atmosphere C/ F /122 - reducing or inert atmosphere C/ F 7/1292 Maximum pressure bar/psi 2/14 P-T DIAGRAM EN 114-1, Type IBC, PN 4, DIN 2891-2 / 3.8, 1. mm PRESSURE [bar] 2 1 1 General suitability - Appropriate measures ensure maximum performance for joint design and gasket installation. Limited suitability - Technical consultation is mandatory. -2-1 -1-1 1 2 3 3 4 4 TEMPERATURE [ C]

Dimensions of standard sheets Sheet size (mm): 1 x 1 1 x 2 1 x 1 Thickness (mm): 1. 1. 2. 3. Other dimensions and thicknesses are available on request. Acetamide + Acetic acid, 1% + Acetic acid, 1% (Glacial)? Acetone + Acetonitrile + Acetylene (gas) + Acid chlorides? Acrylic acid + Acrylonitrile + Adipic acid + Air (gas) + Alcohols + Aldehydes + Alum? Aluminium acetate? Aluminium chlorate? Aluminium chloride - Aluminium sulfate + Amines + Ammonia (gas) + Ammonium bicarbonate + Ammonium chloride? Ammonium hydroxide + Amyl acetate + Anhydrides + Aniline + Anisole + Argon (gas) + Asphalt + Barium chloride? Benzaldehyde + Benzene + Benzoic acid + Bio-diesel + Bio-ethanol + Black liquor? Borax + Boric acid + Butadiene (gas) + Butane (gas) + Butyl alcohol (Butanol) + Butyric acid + Calcium chloride? Calcium hydroxide + Carbon dioxide (gas) + Carbon monoxide (gas) + Cellosolve + Chlorine (gas)? Chlorine (in water) - Chlorobenzene + Chloroform + Chloroprene + Chlorosilanes? Chromic acid - Citric acid? Copper acetate + Copper sulfate + Creosote + Cresols (Cresylic acid) + Cyclohexane + Cyclohexanol + Cyclohexanone + Decalin + Dextrin + Dibenzyl ether + Dibutyl phthalate + Dimethylacetamide (DMA) + Dimethylformamide (DMF) + Dioxane + Diphyl (Dowtherm A) + Esters + Ethane (gas) + Ethers + Ethyl acetate + Ethyl alcohol (Ethanol) + Ethyl cellulose + Ethyl chloride (gas) + Ethylene (gas) + Ethylene glycol + Formaldehyde (Formalin) + Formamide + Formic acid, 1% + Formic acid, 8%? Formic acid, 1%? Freon-12 (R-12) + Freon-134a (R-134a) + Freon-22 (R-22) + Fruit juices + Fuel oil + Gasoline + Gelatin + Glycerine (Glycerol) + Glycols + Helium (gas) + Heptane + Hydraulic oil (Glycol based) + Hydraulic oil (Mineral type) + Hydraulic oil (Phosphate ester based) + Hydrazine + Hydrocarbons + Hydrochloric acid, 1% - Hydrochloric acid, 37% - Hydrofluoric acid, 1% - Hydrofluoric acid, 48% - Hydrogen (gas) + Iron sulfate + Isobutane (gas) + Isooctane + Isoprene + Isopropyl alcohol (Isopropanol) + Kerosene + Ketones + Lactic acid? Lead acetate + Lead arsenate + Magnesium sulfate + Maleic acid + Malic acid? Methane (gas) + Methyl alcohol (Methanol) + Methyl chloride (gas) + Methylene dichloride + Methyl ethyl ketone (MEK) + N-Methyl-pyrrolidone (NMP) + Milk + Mineral oil (ASTM no.1) + Motor oil + Naphtha + Nitric acid, 1%? Nitric acid, 6%? Nitrobenzene + Nitrogen (gas) + Nitrous gases (NOx)? Octane + Oils (Essential) + Oils (Vegetable) + Oleic acid + Oleum (Sulfuric acid, fuming) - Oxalic acid? Oxygen (gas) + Palmitic acid + Paraffin oil + Pentane + Perchloroethylene + Petroleum (Crude oil) + Phenol (Carbolic acid) + Phosphoric acid, 4%? Phosphoric acid, 8%? Phthalic acid + Potassium acetate + Potassium bicarbonate + Potassium carbonate + Potassium chloride + Potassium cyanide + Potassium dichromate? Potassium hydroxide + Potassium iodide + Potassium nitrate + Potassium permanganate? Propane (gas) + Propylene (gas) + Pyridine + Salicylic acid + Seawater/brine? Silicones (oil/grease) + Soaps + Sodium aluminate + Sodium bicarbonate + Sodium bisulfite + Sodium carbonate + Sodium chloride + Sodium cyanide + Sodium hydroxide + Sodium hypochlorite (Bleach) - Sodium silicate (Water glass) + Sodium sulfate + Sodium sulfide? Starch + Steam + Stearic acid + Styrene + Sugars + Sulfur + Sulfur dioxide (gas) + Sulfuric acid, 2% - Sulfuric acid, 98% - Sulfuryl chloride - Tar + Tartaric acid? Tetrahydrofuran (THF) + Titanium tetrachloride - Toluene + 2,4-Toluenediisocyanate + Transformer oil (Mineral type) + Trichloroethylene + Vinegar + Vinyl chloride (gas) + Vinylidene chloride + Water + White spirits + Xylenes + Xylenol + Zinc sulfate + All information and data quoted are based upon years of experience in the production and operation of sealing elements. This data may not be used to support any warranty claims. With its publication this latest edition supersedes all previous issues and is subject to change without further notice. CHEMICAL RESISTANCE CHART The recommendations made here are intended to be a guideline for the selection of the suitable gasket quality. Because the function and durability of the products depend upon a number of factors, the data may not be used to support any warranty claims. + Recommended? Recommendation depends on operating conditions - Not recommended DONIT TESNIT, d.o.o. Cesta komandanta Staneta 38 121 Medvode, Slovenia Phone: +386 ()1 82 33 Fax: +386 ()1 82 32 6 +386 ()1 82 32 8 Web: www.donit.eu E-mail: info@donit.eu Copyright 21 DONIT TESNIT, d.o.o. All rights reserved Date of issue: 1.6.21 / TDS-GIQ--21

Slovenia DONIT Tesnit, d.o.o. Cesta komandanta Staneta 38, 121 Medvode, Slovenia Phone: +386 ()1 82 33 E-mail: info@donit.eu China Suzhou Donit Sealing Materials Import and Export Co., Ltd. No. 8 Suzhou Avenue West, Bank of China Building, Room 194, SIP, 2121, P.R. China Phone: +86 ()12 69 3 29 E-mail: sales.suzhou@donit.eu Slovenia Donit Tesnit, d.o.o. Donit Industrial Sealing Solutions Paradiž 4, 821 Trebnje, Slovenia Phone: +386 ()8 44 E-mail: salesgaskets@donit.eu Belgium DISS-Europe BVBA Donit Industrial Sealing Solutions Toekomstlaan 34, 22 Herentals, Belgium Phone: +32 ()14 32 1 E-mail: sales@disseurope.be India DONIT Tesnit INDIA C-46, Mantri Lavendula Mulshi Road, Bavdhan Khurd, Pune - 411 21, India Phone: +91 2 62 78 E-mail: sales.india@donit.eu Middle East DONIT Tesnit MIDDLE EAST E-mail: sales.middleeast@donit.eu North America DONIT Tesnit NORTH AMERICA E-mail: sales.northamerica@donit.eu Latin America DONIT Tesnit LATIN AMERICA E-mail: sales.latinamerica@donit.eu Copyright 21 DONIT TESNIT, d.o.o. All rights reserved Date of issue: 1.6.21 / BIQ--21 www.donit.eu