J - DUCTILE IRON PILLAR HYDRANTS
|
|
- Kelly Ramsey
- 6 years ago
- Views:
Transcription
1 J - DUCTILE IRON PILLAR HYDRANTS 1.0 General 1.1 This specification briefly specifies the requirement for the standard 100mm and 150mm pillar hydrants Pillar hydrants will be of ductile iron material conforming to BS 750 : 1984 or JKR Specification Type of Pillar Hydrants mm diameter Pillar Hydrant The 100 mm pillar hydrant shall be designed with 65 mm diameter outlets as shown in Appendix 1 & 2. The pressurized 100 mm pillar hydrant shall be equipped with landing valves as in Appendix mm diameter Pillar Hydrant The 150 mm pillar hydrants is provided with two 65 mm diameter outlets and one 100 mm diameter outlet as in Appendix 4. The pressurized 150 mm pillar hydrant is equipped with two 65 mm diameter landing valve and one 100 mm diameter outlet in Appendix 5 & Materials 3.1 Body and Cap: - The body and cap of the pillar hydrants shall be made of ductile (spheroidal graphite) iron at least of quality conforming in all respect to the requirements specified in BS 2789:1985 of Grade 421/ Outlets The material for outlets shall be made of die-cast brass which must comply with the standard BS 1400 Grade DCB1 with minimum tensile strength of 210 N/mm². The screwed outlets shall be provided with caps to cover the outlet thread. J.1
2 The caps shall be securely attached to the hydrant by galvanized steel chain. A minimum 3 mm thick rubber gasket conforming to BS 3457 shall be provided. The screwed outlets shall be locked to prevent theft by using pins as shown. 3.3 Landing Valve: - The materials used for all the components of the landing valve are as shown and must comply with BS 5041 Part : Dimensions 4.1 Body mm Pillar Hydrant Overall height 827 mm ± 10 mm External diameter of hydrant 130 mm ± 5 mm Internal diameter of hydrant 102 mm ± 2.0 mm Flange at inlet as specified in Table 11 BS Section 3.2 for Ductile Iron mm Pillar Hydrants Overall height 875 mm ± 10 mm External diameter of hydrant 213 mm ± 3 mm Internal diameter 150 mm ± 3 mm Flange at inlet as specified in Table 11 BS Section 3.2 for Ductile Iron. 4.2 Outlet mm diameter Outlet This outlet is used as the standard outlets for the 100 mm diameter pillar hydrant and as the side outlets of the 150 mm diameter pillar hydrant. J.2
3 4.2.2 Outlet diameter Internal 64mm mm mm External 75 mm mm mm Length of outlet 122 mm ± 1.0 mm Thickness of flange 10 mm ± 1.5 mm Diameter of flange 96 mm ± 1.0 mm Length of thread 35 mm ± 1.0 mm Diameter of thread 35 mm ± 0.4 mm (External) Type of threads V - Threads Threads per 25.4 mm 5 1/3 Nos mm diameter Outlet For the front outlet for all 150 mm diameter pillar hydrants required dimensions are as follows: - (i) Outlet Diameter Internal 95 mm + 0 mm mm External 112 mm mm - 0 mm (ii) Length of Outlet 126 mm ± 1.0 mm (iii) Thickness of Flange 12 mm ± 1.5 mm (iv) Diameter of Flange 140 mm ± 1.0 mm (v) Length of thread 50 mm ± 1.0 mm (vi) Type of threads Round Threads (vii) Threads per 25.4 mm 3 Nos. J.3
4 4.2.4 Landing Valves 4.3 Caps All landing valves shall comply with BS 5041 Pt 1:1987 to be used for the pressurized 100mm pillar hydrant as well as the side outlets of the pressurized 150 mm pillar hydrant. Cap dimension are as follows: Cap for 65 mm diameter Outlets Width of cap 42 mm ± 1.0 mm External diameter of cap 100 mm ± 2.0 mm Internal diameter 81 mm ± 0.5 mm Rubber gasket Min. 3 mm thick 4.4 Chain Cap for 100 mm diameter Outlet Width of Cap 51 mm ± 1.0 mm External diameter 210 mm ± 3 mm Internal diameter 112 mm ± 0.5 mm Rubber gasket Min. 3 mm thick Material to be of galvanized steel. Minimum diameter for the link of the chain shall be 5 mm. The total minimum length of chain used for 100 mm pillar hydrant. 150 mm pillar hydrant shall be 660 mm and 1160 mm respectively. Link of galvanized steel chain can be fixed either by attaching to the ear with a 100 mm drill hole or embedding in lug formed in casting. 5.0 Coating 5.1 All machined surfaces shall be thoroughly cleaned and shall be treated with a protective composition before they become affected by rust. J.4
5 5.2 The outer surface of the body shall be coated of either fusion bounded epoxy powder or approved fire hydrant yellow with minimum thickness 250 µm conforming to AS / NZ Testing 6.1 Hydrostatic Test The hydrant is subjected to a hydraulic pressure of not less than 24 bar for a period of not less than 24 bar of a period of not less than 1 minute. Overall Flow Test The hydrant shall deliver not less than 210 liters / min at a constant pressure of 1.7 bar at the inlet to the hydrant (Results may be obtained by interpolation by referring to the pressure versus flow curve as in Appendix 7). 7.0 Markings Each hydrant shall have the following markings in raised letters of minimum 50 mm high cast on the body. The Manufacturer s name and trade mark The size of the hydrant The year of manufacture (last two digits) The word SYABAS The body material identification DI Made in Malaysia 8.0 Accessories 8.1 Accessories and fittings associated to pillar hydrants are: - Double-flanged duck-foot 90 (¼) bends Pipes with cast-on flanges, Class K12 Valves J.5
6 8.2 All fittings such as double-flanged duck-foot 90 (¼) bends and pipes with cast-on flanges, Class K 12 connecting to the pillar hydrants shall be made of ductile iron. 8.3 All ductile iron fittings shall have the tensile strength of 421 Mpa and minimum elongation of 5%. 8.4 Coating for fittings (both internally and externally) 9.0 Flanged joints All fitting shall be coated with fusion bonded epoxy powder of not less than 350 µm thickness. All bolts, nuts and washers made of hot dipped galvanize zinc plated carbon steel coated with Rislan Nylon with the finished thickness of coating between 75 µm and 125 µm. 9.1 The dimensions and tolerances of the flanges of pipes and fittings shall comply with PN 16 requirement for ductile iron. 9.2 Each fitting shall be supplied with a set of flange jointing materials, which shall be completed with nuts, bolts, washers and joint rings. 9.3 Joint rings shall be of flat section 5 mm thick, medium rubber reinforced with two-ply flexible fabric and shall not extend beyond the bolt circle Pre- Delivery Inspection and Evaluation 10.1 It is the responsibility of the Contractor to inform SYABAS Sdn. Bhd. for inspection purposes during manufacturing and before delivery SYABAS reserved the rights to inspect and witness the testing of product offered At any time, when requested, the Contractor is to provide SYABAS a sample of the product offered for evaluation purposes. All costs shall be borne by the Contractor If at any time the Contractor fails to deliver the required sample, the product is deemed fail to meet the specifications Certification 11.1 The Contractor is required to provide a copy of the certificate and testing report from SIRIM, IKRAM or other recognised certification body Tests report required should be those tests conducted within a year period. J.6
7 11.3 SYABAS reserved the rights to refuse offer or reject supply if the documents required are not enclosed Packaging All pillar hydrants shall be individually packed with proper methods and protected from damage during transit. J.7
8 J.8
9 J.9
10 J.10
11 J.11
12 J.12
13 J.13
14 Appendix 5 Cold Applied High Solid Liquid Epoxy Coatings On Casting Surfaces (Both Internally and Externally) 1. Surface Preparation All surfaces to be coated shall be clean and dry and free from porosity, crack, sand, rust, oil, grease and other foreign matter. They shall be prepared by abrasive blast cleaning to Sa 2 ½ Standard (ISO ). Only dry abrasive blasting procedures shall be used. Any clean surface left overnight without coating shall be reblasted before application of coating. In the event rusting occurs after completion of surface preparation due to bad weather, the surface shall again be cleaned in accordance with the specified standard. Cleaning shall be discontinued each day in sufficient time to permit the surfaces cleaned to be coated before rust booming. 2. Coating Application Coatings shall be applied in accordance with Section 3.3 of AWWA C Application of coating shall be by spraying to a total dry film thickness of more than 356 microns but less than 635 microns. The coating shall not have coating imperfections such as blisters, cracks, bubbles, underfilm voids, mechanical damages, holidays, pinholes or discontinuities. 3. Coating Repair Areas requiring coating repairs due to coating imperfections shall be cleaned using hand and power tool to minimum St 2 Standard (ISO ). The adjacent coating shall be roughened. All dust shall be wiped off. Same coating material shall be applied to the prepared repair areas immediately to the required thickness. Repairs shall be electrically inspected using a holiday detector. 4. Coating Procedure a. Coating System 1 (one) coat system b. Application Condition : J.14
15 Surfaces shall not be coated in rain, wind, fog, mist or in areas where airborne elements exist; when the steel surface temperature is less than 3 0 C above dewpoint; when the relative humidity is greater than 85%. Blast-cleaned surfaces shall be coated as soon as practical, not later than rust booming. c. Paint Application Procedure : Mixing, pot life, thinner shall be as per paint manufacture recommendation. Apply a wet coat in even parallel passes. Overlap each pass 50% to avoid bare areas pinholes or holidays. Thinning normally not required. Thin only for workability with not more than 10% by volume of thinner. Check thickness of dry coating with non-destructive dry film thickness gauge. In confined areas, observe safety rules provided by paint manufacturer. Uncured paint should not be exposed to water, chemicals or mechanical stress before the paint is fully cured. It is recoatable provided that the existing surface is cleaned from oil or other foreign contamination. Prior to recoating all irregular surfaces are to be sand paper abraded. For multicoat system, recoating time shall follow paint manufacturer recommendation. Prior to recoating, all irregular surfaces are to be sand paper abraded. 5. Inspection a. Surface Preparation : Visually (From ST2 to SA 2.5) b. Surface Profile : The profile height shall be spot checked with Elcometer Profile Gauge or Keane- Tator Comparator with reference to5a. above. c. Paint Material J.15
16 Record batch number d. Metal Temperature The magnetic metal temperature gauge should be used. Metal temperature must be 3 0 C above the dew point. e. Wet Film Thickness (WFT) The comb-type gauge shall be used. f. Dry Film Thickness (DFT) The Elcometer DFT Gauge shall be used. g. Visual Inspection Coats shall be smooth, free from dry spray, pinholes, blisters, craters and excessive sagging. 6. Testing on Applied External and Internal Coating 6.1 Holiday Test ASTM G62-87 All pipes shall be checked for continuity of the applied protection in accordance with ASTM G Discontinuities and pinholes indicated by the test shall be made good as per the manufacturer recommendation. 6.2 Adhesion Test When an adhesion test is carried out, it shall comprised one of the following methods : a. The Ring Test A ring 75mm wide shall be cut cold from one end of finished pipes. The ring shall be flattened at a temperature between 10 0 C and 21 0 C to 50% of the original diameter. The lining and / or coating shall not part from the metal under this test. b. The Strip Test Using a tool with a thin sharp blade, two cuts approximately 50mm apart shall be J.16
17 made through the protection on the metal pipe. Sudden impact that would cause ultimately separation shall be avoided. The blades shall be worked under the protection and an attempt made to peel it from the metal. The adhesion shall be considered satisfactory if removal of the protection causes cohesive failure and the protection does not peel cleanly from the primer or the pipe surface. c. Measuring Adhesion by Tape Test ASTM D Test method A is primarily intended for use at job sites. An X cut is made in the film to the substrate, pressure sensitive tape is applied over the cut and then removed, and adhesion is assessed qualitatively on the 0 to 5 scale. The acceptance should be 4A-Trace peeling or removal along incision or at their intersection. d. Pull-Off Strength of Coating Using Portable Adhesion Testers ASTM D This test method is for the determination of perpendicular force of the coating can bear a plug of material is detached. It has to be carried on a flat surface. The general pull-off test is performed by securing a loading fixture (dolly) normal (perpendicular) to the surface of the coating with an adhesive. After the adhesive is cured, a testing apparatus is attached to the loading fixture and aligned to apply tension normal (perpendicular) to the test surface. The force applied to the loading fixture is then gradually increased and monitored until either a plug of coating material is detached or a specified value is reached. The acceptance criterion is a minimum strength of 20 kg/cm 2. The tests shall be performed when the protection has been allowed to cure at a temperature not less than 10 0 C or more than 35 0 C for a minimum of 48 hours after application. However for pull-off adhesion test, a proper curing period of 7 days is required before the test. Note : When an adhesion test is required, this should be stated by the purchaser during enquiring or ordering. J.17
18 STANDARD INSPECTION PROCEDURE (BLASTING) A. BEFORE BLASTING INSPECTION OF CASTINGS To check 1. Condition of Rust - Grade A, B, C, D 2. Oil or grease solvent wipe in accordance with SSPC-SP1 3. Sharp edges, wedge slag - grind off INSPECTION OF ABRASIVE To check 1. Grade / Mesh size 2. Salt free and general utility INSPECTION OF BLASTING EQUIPMENT To check 1. Test run for equipment 2. Compressed air free from oil and moisture trap and separator 3. Pressure at blast hose nozzle - hyperdermix needles (85 100psi) 4. No defective on blasting nozzle J.18
19 B. DURING BLASTING MEASURE AND RECORD WEATHER CONDITION INSPECTION OF CASTINGS To check To check 1. Measure and record weather condition dew point, relative humidity, steel surface temperature. No blasting shall be allowed if steel temperature is not at least 3 0 C above dew point 1. Standards achieved visual comparison using Pictorial Standard ISO Surface roughness of minimum 30µ as measured by Keane- Tator surface comparator Note : 1. No blasting to be allowed if relative humidity is above 85% (Whitling Hygrometer to be used). Casting surface temperature (using Magnetic Contact Thermometer) is not more than 3 0 C above dew point (using Dew Point Calculator) 2. Blasted casting surfaces should be primed within 4 hours at normal weather condition provided that no abrupt change in weather condition, and surface (rust blooming). 3. Blasted surfaces left uncoated overnight shall receives a complete light blasting the next day before priming. J.19
20 C. AFTER BLASTING CHECK WEATHER CONDITION To check No coating to be applied if casting temperature is less than3 0 C above dew point INSPECTION OF CASTINGS Within 4 hours To check 1. Sharp edges to be removed by sanding down 2. Dust free surface to blow off dust 3. Dust/pollution free environment to be applied when blasting work is being carried out nearby PAINT APPLICATION J.20
21 First Edition: May 2007 Manufacture Description References of Cold-Applied High Solids (solvent or solventless) Epoxy as Internal and External Coating System For Metal Surfaces Suitable For Portable Water (Using High Solids (solvent or solventless) Epoxy-Based Primer/Topcoat) Jotun Dimet Jotamastic 87 Naviguard Amerlock 400 Amercoat 395 Courtaulds Coatings (International Paint) Intergard Potable Interline 925 Water Tank Coating Nippon Paint Coppon EA-9 Finish HB Certification AWWA C by COT 10 Dec 92 AWWA C210 84/92 by COT 27 Sep 94 Coating System 1 or 2 coats 1 or 2 coats 1 or 2 coats 2 coats Multicoat System Multicoat System 2 coats Colour Varieties Varieties Varieties White. Off- White, Pink Cream, White Varieties White Orange Solids Volume 82% ± 2% 100% 83% ± 3% 91% ± 3% 56% 100% 55% DFT per Coat µ µ µ µ 125µ µ 150µ Recommended Total DFT 400µ 400µ 400µ 400µ 400µ 400µ 400µ Application Method Airless or Conventional Spray Airless or Conventional Spray Airless or Conventional Spray Airless or Conventional Spray Airless Spray Airless Spray Airless or Conventional Spray Drying Period Touch Dry Hard Dry Curing BS 3900 C2 & C3 (35 0 C) 2.5 hrs 5 hrs 3 days BS 3900 C2 & C3 (35 0 C) 2.5 hrs 4 hrs 3 days ASTM D1640 (32 0 C) 4.5 hrs 12 hrs 4 days ASTM 1640 (21 0 C) 6 hrs 24 hrs 7 days (35 0 C) 1 hrs 3 hrs - (35 0 C) 4 hrs 8 hrs - (25 0 C C) 2 hrs 16 hrs 9 days J.21
22 Polymeric Coating Appendix 6 1. Materials and Thickness Pipes and fittings shall be coated with either a thermoset or thermoplastic polymeric coating material. The coating shall be applied using either the fluidized bed dipping process or the electrostatic spray process. The minimum thickness of polymeric coating material shall be not less than those specified below : Coating Type Coating Thickness (µm) Thermoplastic Thermoset Note : A coating manufacturer may specify higher minimum coating thickness than those specified above 2. Performance Testing Water Quality All coating material in contact with or likely to come in contact with potable water shall meet the requirements of BS 6920 Part Physical Characteristics and Performance a. Holidays Coating shall be tested in accordance with AS Only pinhole-free coated test piece shall be used in subsequent performance test. b. Hot Water Immersion Test in accordance with AS 3862 at 60 0 C ±21C for 100 days. The coating shall have a rating of equal to or greater than four when tested in accordance with method of AS 1580, immediately after exposure. J.22
23 c. Water Absorption d. Flexibility When tested in accordance with AS 3682 at 0 0 C, the coating shall not crack when strained at 1.0% as calculated in the following equation : e. Impact Resistant Strain β = 100 Sc % 2R Sc where Sc Sample Thickness R Radius of Mandrel When tested in accordance with ASTM G14 at 23 0 C, the impact resistant shall be equal to or greater than 2.0 J. The test may either be conducted on pipe with an outside diameter of 110mm to 125mm and wall thickness from 5mm to 7mm (6mm for flat plate). If cast plate is used, the side in contact with the anvil shall be machined flat prior to testing. f. Abrasion Resistance The abrasion resistance test shall be undertaken according to ASTM D4060 with CS18 wheel, 1000 cycles at 23 0 C ± 21C. The weight loss shall be equal to or less than 40mg. g. Cathodic Disbondment Coated test piece shall be tested according to sections 5, 6, 7, 8 and 9 of BS 3900 : F 11. The coating when subjected to an impressed current at a negative voltage of 1.5V, shall not disbond more than 5mm radially from the end of the damaged coating after 28 days. h. Cure Test This test applied only to thermosetting coatings, including liquid thermosets. After an appropriate combination of time and conditions (both to be defined prior to the test by the manufacturer) from the point of coating application, thermosetting coating on coated test pieces shall be demonstrated to have been cured within J.23
24 declared limits. The method used shall also be declared. Whenever practicable, the method chosen should produce quantitative results. Thermoplastic coating do not required this test. i. Adhesion Test Adhesion testing shall be carried out to determine the adhesive strength of the coating to the substrate. It does not prove cohesive strength of the coating. Testing shall be by means of a V -cut test. Toughness of the film and visual evidence of coating in the anchor pattern valleys will give good indication of satisfactory adhesion. The test shall be carried out using a sharp knife. Two cuts are made in the coating at an included angle of approximately Using the sharp point craft knife or similar, the knife shall be used to attempt to lift the point of V in a single action levering against a fulcrum. Not more than 2mm of the V shall be removed by this method by adhesive failure to the substrate or the adhesion shall be considered to be unsatisfactory. The purchaser shall state his requirement for an adhesion test and the frequency of testing at the time of enquiry and order. j. Salt Spray Test Prior to exposure, each test piece shall have a V cut made through the coating in accordance with D Coated test pieces shall undergo 2100 hours exposure to salt spray in accordance with BS 3900 : F4. After exposure, the underfilm corrosion must not extend more than 1mm from the cut edge of the coating. There shall be no blistering in this area. Addition, a V cut test shall be carried out in accordance with D.3.10 on the undamaged side of the sample after exposure. On this side, there shall be not more than 1mm disbondment, no underfilm corrosion and no blistering. J.24
25 First Edition: May 2007 J.25
26 J.26
27 J.27
COATING NEW STRUCTURAL STEEL SIGN SUPPORT STRUCTURES - Item No. Special Provision No. 911S09 November 2006
COATING NEW STRUCTURAL STEEL SIGN SUPPORT STRUCTURES - Item No. Special Provision No. 911S09 November 2006 Amendment to OPSS 911, November 2004 for hot dip galvanizing and subsequent painting, where required,
More informationBharat Heavy Electricals Limited Piping Centre Chennai-17. Specification Number Revision Number Sheet Number PC:E:GF: of 7 CONTENTS
PC:E:GF:001 00 2 of 7 CONTENTS 1 SCOPE 2 PRODUCT SPECIFICATION 3 SURFACE PREPARATION 4 PRIMING 5 COATING 6 FIELD JOINTING 7 INSPECTION AND TESTING PC:E:GF:001 00 3 of 7 Technical Specification for Glass
More informationPOLYURETHANE COATINGS ON STEEL OR DUCTILE IRON PIPE
Section 02527 PART 1 G E N E R A L 1.01 SECTION INCLUDES A. Two-component polyurethane coating system for use as external coating for steel or ductile iron pipe. 1.02 MEASUREMENT AND PAYMENT A. Unit Prices.
More informationCOATING SPECIFICATION HIGH BUILD EPOXY COATING ON BUTTERFLY VALVES COATING SPECIFICATION: D2 ISSUE: 2 DATE: FEBRUARY 2016
1.0 SCOPE This document summarises the procedure for the application of a 2 pack High Build Epoxy Coating, with > 80% volume solids, on steel or ductile iron butterfly valves. Refer Design Standard, DS
More informationCONCRETE STEPS, HANDRAILS, AND SAFETY RAIL
CONCRETE STEPS, HANDRAILS, AND SAFETY RAIL PART 1 - GENERAL 1.01 SECTION INCLUDES A. Concrete Steps B. Handrails C. Safety Rail 1.02 DESCRIPTION OF WORK A. Construction of concrete steps. B. Furnishing
More informationEXAMPLE COATING PRODUCER
No.101 No. 101 (June 2008) IACS Model Report for IMO Resolution MSC.215(82) Annex 1 Test Procedures for Coating Qualification EXAMPLE COATING PRODUCER BALLAST TANK COATING TEST OF 2 * 160 µm EXAMPLE EPOXY
More informationCONCRETE STEPS, HANDRAILS, AND SAFETY RAIL
SUDAS Standard Specifications Division 9 - Site Work and Landscaping Section 9080 - Concrete Steps, Handrails, and Safety Rail CONCRETE STEPS, HANDRAILS, AND SAFETY RAIL PART - GENERAL.0 SECTION INCLUDES
More informationSECTION WELDED STEEL PICKET FENCE. 1. Fusion welded and rackable ornamental steel picket fence system.
PART 1 - GENERAL 1.1 SUMMARY A. Section includes: 1. Fusion welded and rackable ornamental steel picket fence system. B. Related sections: 1. Section 03310 Concrete Work for post support. 2. Section 09960
More informationZinc Silicate (Inorganic)
Product code: 477-041: part A 477-042: part B General description: Two-component, zinc-ethyl silicate-. Forms a continuous coat of metallic zinc that provides cathodic protection to metal (as in hot galvanization).
More informationSECTION CERAMIC EPOXY LINING DUCTILE IRON PIPE AND FITTINGS
SECTION 02500 CERAMIC EPOXY LINING DUCTILE IRON PIPE AND FITTINGS (As provided by Tnemec Company, Inc.) GENERAL 1.1 SUMMARY 1. This Section includes surface preparation and shop application of Series 431
More informationPrepared By: Engineering Staff Approved By: Jerome T. Schmitz
MS C-17 Section No: Page No.: 1 of 16 1. SCOPE This specification defines the minimum requirements for materials, application and inspection for Powercrete and Powercrete R60 epoxy-based polymer concrete
More informationDURASHIELD 110 &
DURASHIELD 110 & 110-61 EFFECTIVE: 3/01/19 I. Scope A. This specification defines application requirements of DuraShield 110/110-61 plural-component, 100% solids, 1:1 volumetric mix ratio polyurethane
More informationTnemec 394 Proprietary Long Form Coatings Schedule
1.1 PRIMER Tnemec 394 Proprietary Long Form Coatings Schedule A. Primer: Tnemec Series 394 PerimePrime Aromatic Polyurethane Mio/Zinc filled Primer applied @ 2.5-3.5 mils DFT and conforming to the following
More informationDURASHIELD 210 &
DURASHIELD 210 & 210-61 I. Scope A. This specification defines application requirements of DuraShield 210 & DuraShield 210-61 plural-component 100% solids, 2:1 volumetric mix ratio polyurethane to steel
More informationDURASHIELD JARS APPLICATION SPECIFICATION SHEET FIELD-APPLIED JOINT & REPAIR SYSTEM (JARS) EFFECTIVE: 6/2/15
DURASHIELD 310-61 JARS FIELD-APPLIED JOINT & REPAIR SYSTEM (JARS) I. Scope A. This specification defines application requirements of DuraShield 310-61 Joint and Repair System (JARS) plural-component 100%
More informationSECTION High Performance Coatings Field Applied Acrylic Urethanes (Solid Color, Pearl and Metallic Finishes)
- 1 - SECTION 099600 High Performance Coatings Field Applied Acrylic Urethanes (Solid Color, Pearl and Metallic Finishes) PART 1 GENERAL 1.1 SECTION INCLUDES A. Systems for field applied acrylic urethane
More informationSPECIALTY POLYMER COATINGS, INC.
SPECIALTY POLYMER COATINGS, INC. LABORATORY TESTING OF SP2831 LOW TEMPERATURE CURE 0154-01-05-T Amal Al-Borno, Ph. D. President Jason Hartt, B. Sc. Chemical Technician #6, 4604 13 th Street N.E. Calgary,
More informationFABRICATED STEEL PIPE AND SPECIALS
SECTION 02420 - PART 1 -- GENERAL 1.1 WORK OF THIS SECTION A. The WORK of this Section includes providing fabricated steel pipe, specials and connections to new and existing piping. Polyurethane and fusion
More informationCOATING SPECIFICATION ZINC RICH EPOXY PRIMER, EPOXY MASTIC COATING ON STEEL OR CAST IRON COATING SPECIFICATION: C3 ISSUE:2 DATE: OCTOBER 2016
1.0 SCOPE This document summarises the procedure for the application of 2 pack Zinc Rich Epoxy primer over-coated with 2 pack Epoxy mastic. Refer Design Standard, DS 95 (Standard for the Selection, Preparation,
More informationKENT COUNTY WATER AUTHORITY. ERRATUM to Rules and Regulations of the Kent County Water Authority
KENT COUNTY WATER AUTHORITY ERRATUM to Rules and Regulations of the Kent County Water Authority Section 4.9.1.1 Resilient Seat Gate 4 inch to 12 inch: Replace with the attached. Section 4.9.1.3 Tapping
More informationEXAMPLE COATING PRODUCER
No.102 No. 102 (June 2008) IACS Model Report for IMO Resolution MSC.215(82) Annex 1 Test Procedures for Coating Qualification, Section 1.7 - Crossover Test EXAMPLE COATING PRODUCER BALLAST TANK COATING
More informationREGIONAL CONSTRUCTION STANDARDS
REGIONAL CONSTRUCTION STANDARDS SIXTH EDITION Publication Update 6.1 (Full Committee Approved Proposed Revision 6.1 Ductile Iron Pipe Protections - Section 200 As Publication Update 6.1) March 27, 2018
More informationDURASHIELD 210 &
DURASHIELD 210 & 210-61 I. Scope A. This specification defines application requirements of DuraShield 210 & DuraShield 210-61 plural-component 100% solids, 2:1 volumetric mix ratio polyurethane to steel
More informationCOATING SPECIFICATION INORGANIC ZINC SILICATE, EPOXY PRIMER MIST-COAT, TWO PACK ACRYLIC TOP COAT ON STEEL OR CAST IRON
1.0 SCOPE This document summarises the procedure for the application of Inorganic Zinc Silicate (IZS), Epoxy Primer Mist Coat coat followed by two pack Acrylic on Steel or Cast Iron structures. Refer Design
More informationtwo component polyamide cured epoxy primer yellow/green - eggshell
6 pages Revision of December 006 DESCRIPTION PRINCIPAL CHARACTERISTICS COLOURS AND GLOSS BASIC DATA AT 0 C Mass density Volume solids VOC (supplied) Recommended dry film thickness Theoretical spreading
More informationtwo component polyamide cured epoxy primer yellow/green (redbrown on request) - eggshell
5 pages Revision of September 2009 DESCRIPTION PRINCIPAL CHARACTERISTICS COLOURS AND GLOSS BASIC DATA AT 20 C Mass density Volume solids VOC (supplied) Recommended dry film thickness Theoretical spreading
More information1. Temperature Change: 120 deg F (67 deg C), ambient; 180 deg F (100 deg C), material surfaces.
SECTION 05500- METAL FABRICATIONS PART 1 - GENERAL 1.1 RELATED DOCUMENTS A. Drawings and general provisions of the Contract, including General and Supplementary Conditions and Division 01 Specification
More informationCOATING SPECIFICATION HIGH BUILD CERAMIC FILLED EPOXY COATING ON NEW AND EXISTING PUMPS COATING SPECIFICATION: F3 ISSUE: 1 DATE: 12 DECEMBER 2012
1.0 SCOPE This document summarises the procedure for the application of using 2 pack High Build Ceramic Filled Epoxy coating. Refer Design Standard, DS 95 (Standard for the Selection, Preparation, Application,
More informationSIGMAZINC 158. Revision of September 2008 DESCRIPTION. two component moisture curing zinc (ethyl) silicate primer PRINCIPAL CHARACTERISTICS
5 pages Revision of September 2008 DESCRIPTION PRINCIPAL CHARACTERISTICS COLOURS AND GLOSS BASIC DATA AT 20 C Mass density Volume solids VOC (supplied) Recommended dry film thickness Theoretical spreading
More informationNap-Gard Plant Application - Nap-Gard Gold Dual Powder System on Line Pipe Revised: 17 September 2013
Nap-Gard 7-2504 Plant Application - Nap-Gard Gold Dual Powder System on Line Pipe Revised: 17 September 2013 1.0 SYSTEM: NAP-GARD GOLD DUAL POWDER 7-2504 2.0 GENERAL 2.1 The following definitions are used
More informationSpecial Specification 4038 Zinc Cathodic Protection System
Special Specification 4038 Zinc Cathodic Protection System 1. DESCRIPTION Furnish, install, and energize a sacrificial zinc anode cathodic protection system to bent caps, tie beams, concrete walls and
More informationA. The CONTRACTOR shall provide pipe coating, complete and in place, in accordance with the Contract Documents.
POLYURETHANE COATING ON STEEL PIPE PART 1 -- GENERAL 1.1 THE REQUIREMENT A. The CONTRACTOR shall provide pipe coating, complete and in place, in accordance with the Contract Documents. 1.2 REFERENCE SPECIFICATIONS,
More informationSIGMAZINC 160. Revision of March 2007 DESCRIPTION. two component moisture curing inorganic zinc (ethyl) silicate primer PRINCIPAL CHARACTERISTICS
5 pages Revision of March 2007 DESCRIPTION PRINCIPAL CHARACTERISTICS COLOURS AND GLOSS BASIC DATA AT 20 C Mass density Volume solids VOC (supplied) Recommended dry film thickness Theoretical spreading
More informationApplication Guidelines
Application Guidelines 1.0 SCOPE This document contains general instructions and recommended practices for the application of the SERVIWRAP cold applied tape coating system. The various coating grades
More informationTEST PROCEDURE SUMMARY
TEST PROCEDURE SUMMARY 1. Compressive Strength - ASTM D695 The compressive strength of a product is determined by subjecting a solid cylinder of material whose length is equal to twice its diameter to
More informationNote: This specification was written for Clarabelle Mill's flotation cells but may have other applications.
017/03/3 1/7 1.0 PURPOSE This specification describes the minimum application and performance requirements for a field-applied, elastomer spray coating either polyurethane or polyurea type. Note: This
More informationAll definitions are defined according to ANSI/AWWA C
SAN ANTONIO WATER SYSTEM SPECIFICATIONS FOR REDUCED-WALL, RESILIENT-SEATED GATE AND TAPPING VALVES FOR WATER SUPPLY SERVICE 4 IN. THROUGH 48 IN. ANSI/AWWA C515-01 July 2017 1. SCOPE This product specification
More informationApplication Procedures for Uncured Rubber Linings on Pipe
Application Procedures for Uncured Rubber Linings on Pipe INDEX 1.0 GENERAL 2.0 SURFACE INSTRUCTIONS 3.0 CEMENTING INSTRUCTIONS 4.0 APPLICATION OF RUBBER LINING 5.0 CURING OF LINING 6.0 INSPECTION AFTER
More informationDUCTILE IRON PIPES AND FITTINGS DETAILED PRODUCTS SPECIFICATIONS
DUCTILE IRON PIPES AND FITTINGS DETAILED PRODUCTS SPECIFICATIONS General All Materials shall be EN, ISO or equivalent standard and shall be supplied from approved manufacturers. According to the International
More informationRefer to Substrates & Surface Preparation.
SELECTION & SPECIFICATION DATA Generic Type Description Features Color Finish Primer Dry Film Thickness Aliphatic Acrylic Polyurethane Thin film, high gloss finish with exceptional weathering performance
More informationGirth Weld Coating With Fusion Bond Epoxy
fact sheets Girth Weld Coating With Fusion Bond Epoxy Processing guidelines The guidelines below describe surface preparation and application requirements and procedures, inspection and safety recommendations
More informationMATERIAL SPECIFICATION FOR FRAMES, GRATES, COVERS, AND GRATINGS
ONTARIO PROVINCIAL STANDARD SPECIFICATION OPSS.PROV 1850 APRIL 2018 (Formerly OPSS 1850, April 2013) Note: The PROV published in April 2018 replaces OPSS 1850 COMMON, April 2013 with no technical content
More informationApplication Guidelines
Application Guidelines 1.0 SCOPE This document contains general instructions and recommended practices for the application of the SERVIWRAP cold applied tape coating system. The various coating grades
More informationSECTION POLYURETHANE MIC COATINGS. A. Furnish and install special coating systems in accordance with the Contract Documents.
SECTION 09802 POLYURETHANE MIC COATINGS PART 1 -- GENERAL 1.01 THE REQUIREMENTS A. Furnish and install special coating systems in accordance with the Contract Documents. B. Polyurethane MIC Coating 1.
More informationCOATINGS & LININGS DUCTILE IRON PIPELINE SYSTEMS
Viadux supplies a range of coatings and linings to meet the most demanding specifications in the water industry This data sheet describes the range of coatings systems that are currently available on TYTON
More informationProduct Index. Coating Thickness. Porosity. Adhesion. Inspection Kit. Surface Profile. Surface Cleanliness. Gloss
Paint Test Equipment Price List 2018 Coating Thickness Wet Film Thickness Porosity Adhesion Surface Roughness Surface Cleanliness Climatic Conditions www.paint-test-equipment.com Product Index Coating
More informationProduct Index. Coating Thickness. Porosity. Adhesion. Inspection Kit. Surface Profile. Surface Cleanliness. Gloss
Paint Test Equipment Price List 2019 Coating Thickness Wet Film Thickness Porosity Adhesion Surface Roughness Surface Cleanliness Climatic Conditions www.paint-test-equipment.com Product Index Coating
More informationProduct Index. Coating Thickness. Porosity. Adhesion. Inspection Kit. Surface Profile. Surface Cleanliness. Gloss
Paint Test Equipment Price List 2018 Coating Thickness Wet Film Thickness Porosity Adhesion Surface Roughness Surface Cleanliness Climatic Conditions www.paint-test-equipment.com Product Index Coating
More informationSECTION POLYETHYLENE TAPE WRAPPING FOR PIPE
PART 1 -- GENERAL 1.1 THE SUMMARY SECTION 09 96 12 - A. The CONTRACTOR shall provide a prefabricated, cold-applied, multilayer polyethylene tape coating system on pipe, complete and in place, in accordance
More informationZINGA. Physical data and technical information
ZINGA 1/6 ZM-RE-PRO-04-A (01/08/06) The film galvanising system Zinga is a one pack coating that contains 96% zinc in the dry film and provides cathodic protection to ferrous metals. It can be used as
More informationAll definitions are defined according to ANSI/AWWA C b. Flanged Joint: The flanged and bolted joint as described in ANSI/AWWA C110/A21.10.
21-02 SAN ANTONIO WATER SYSTEM SPECIFICATIONS FOR RESILIENT-SEATED GATE AND TAPPING VALVES FOR WATER SUPPLY SERVICE ANSI/AWWA C509-01 3 IN., 4 IN., 6 IN., 8 IN., 10 IN., 12 IN., 16 IN., & 20 IN. Revised
More informationAPPLICATION SPECIFICATION SHEET GENERAL INDUSTRIAL EFFECTIVE: 01/09/12
I. Scope A. This specification defines application requirements of SpectraGarde NSF-61 plural-component 100% solids, 3:1 volumetric mix ratio polyurethane to concrete, ferrous and non-ferrous substrates
More informationONTARIO PROVINCIAL STANDARD SPECIFICATION
ONTARIO PROVINCIAL STANDARD SPECIFICATION METRIC OPSS 1850 NOVEMBER 2003 MATERIAL SPECIFICATION FOR FRAMES, GRATES, COVERS, AND GRATINGS TABLE OF CONTENTS 1850.01 SCOPE 1850.02 REFERENCES 1850.03 DEFINITIONS
More informationCOATING SPECIFICATION ELASTOMERIC POLYURETHANE PROTECTIVE COATING ON CONCRETE COATING SPECIFICATION: I1 ISSUE: 1 DATE: 12 DECEMBER 2012
1.0 SCOPE This document summarises the procedure for spray applying Elastomeric Polyurethane protective coatings (e.g. Polybrid, Polyurea ) onto concrete structures. Refer Design Standard, DS 95 (Standard
More informationCOATING SPECIFICATION EPOXY MASTIC, POLYURETHANE TOP COATING ON FUSION BONDED POLYETHYLENE COATING (SINTAKOTE )
1.0 SCOPE This document summarises the procedure for the application of a 2 pack Epoxy Mastic coating, followed by a Polyurethane top coat, onto a Fusion Bonded Medium Density Polyethylene (Sintakote )
More informationDIMETCOTE 9 H. PRODUCT DATA SHEET May 2, 2018 (Revision of August 7, 2015) DESCRIPTION. Inorganic Zinc Silicate Primer PRINCIPAL CHARACTERISTICS
DESCRIPTION Inorganic Zinc Silicate Primer PRINCIPAL CHARACTERISTICS >85% zinc in dry film VOC Compliant
More informationQUALITY ASSURANCE MANUAL FOR APPLICATORS OF ELASTOMERIC SHEET LININGS
QUALITY ASSURANCE MANUAL FOR APPLICATORS OF ELASTOMERIC SHEET LININGS 1.0 Purpose To establish a recommended quality assurance program for applicators of elastomeric sheet linings. 2.0 Scope This bulletin
More informationPTFE BELLOWS POLY FLUORO LTD. POLY FLUORO LTD.260A. Bommasandra Industrial Area, Hosur Road, Bangalore TECHNICAL SPECIFICATION
PTFE BELLOWS TECHNICAL SPECIFICATION 1. MATERIALS 1.1 PTFE Only virgin (not reprocessed) PTFE conforming to ASTM D 1457, type III, IV or V shall be used for the production of bellows; the PTFE raw material
More information1(5) Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
1(5) A two-component, resin modified epoxy paint. Excellent resistance to abrasion, chemicals and water immersion Used as a primer or finish for interior and exterior steel, aluminium and zinc surfaces
More informationApplication Guide. Steelmaster 1200WF. Intumescent Coating
Application Guide Steelmaster 1200WF Intumescent Coating Steelmaster 1200WF Application Guide Page 1 of 13 CONTENTS: 1. Introduction 2. Storage 3. Environmental conditions 4. Surface Preparation 5. Primers
More informationApplication Guide for Internal Flow Efficiency Coating Jotapipe FC 400
Jotapipe FC 400 Application Guide for Internal Flow Efficiency Coating Jotapipe FC 400 Date of Last Revision: February 2014 Page 1 of 6 Contents 1.0 Product Description... 2 2.0 Surface preparation and
More informationDIMETCOTE 9 VOC. PRODUCT DATA SHEET July 12, 2016 (Revision of August 7, 2015) DESCRIPTION. Inorganic Zinc Silicate Primer PRINCIPAL CHARACTERISTICS
DESCRIPTION Inorganic Zinc Silicate Primer PRINCIPAL CHARACTERISTICS High level of zinc in dry film VOC compliant for
More informationFood Service FDA Title 21 CFR
1.0 Scope 1.1 This recommendation covers the requirements for the surface preparation, application of primers and finish coats of resin linings to the interior surfaces of carbon/stainless steel vessels.
More informationInstruction Guide APPLICATION OF CIM TO CONCRETE
23 Elm St., Peterborough, NH 03458 Tel: (800) 543-3458 (603) 924-9481 Fax: (603) 924-9482 Web site: Instruction Guide APPLICATION OF CIM TO CONCRETE 1.0 DESCRIPTION This guide covers the installation of
More informationPROLINE MID-TEMPERATURE VINYL ESTER LINING INSTALLATION GUIDE ProLine 4865T with optional 4822S Gel Coat Food Service FDA Title 21 CFR 175.
1.0 Scope 1.1 This recommendation covers the requirements for the surface preparation, application of primers and finish coats of resin linings to the interior surfaces of carbon/stainless steel vessels.
More informationMATERIAL SPECIFICATION FOR EPOXY COATED REINFORCING STEEL BARS FOR CONCRETE
ONTARIO PROVINCIAL STANDARD SPECIFICATION METRIC OPSS 1442 NOVEMBER 2007 MATERIAL SPECIFICATION FOR EPOXY COATED REINFORCING STEEL BARS FOR CONCRETE TABLE OF CONTENTS 1442.01 SCOPE 1442.02 REFERENCES 1442.03
More informationSTRUCTURAL STEEL FRAMING
SECTION 05 12 00 - STRUCTURAL STEEL FRAMING PART 1 - GENERAL 1.1 SUMMARY A. Section includes 1. Structural steel framing 2. Structural steel framing required for support and framing of rooftop mechanical
More informationElastocoat Protective Coatings APPLICATION GUIDE
Elastocoat Protective Coatings DESCRIPTION Elastocoat polyurea and polyurethane coatings are two-component, 100% solids elastomer systems. The coatings systems are designed for processing through plural
More informationIGS-M-TP-027(0) Jan IGS !"#$ %$!& ' () * +, +-!".!
IGS-M-TP-027(0) Jan. 2013 approved!"# $%& IGS '( )* +,-./01#!"#$ %$!& ' () * +, +-!".! External Liquid Epoxy Coating for Rehabilitation and Repair of Buried Steel Pipelines, Bends, Field Joints,Valves
More information1. Base plates, setting plates and anchor rods for columns. 8. Lintels if connected to structural steel columns.
PAGE 051200-1 SECTION 051200 PART 1 - GENERAL 1.1 RELATED DOCUMENTS A. Drawings and general provisions of the Contract, including General and Supplementary Conditions and Division 01 Specification sections,
More informationDET NORSKE VERITAS. Report Crossover test of Jotacote Universal N10 on Galvany IZ 182 (J) Jotun A/S
Report Crossover test of Jotacote Universal N10 on Galvany IZ 182 (J) Jotun A/S Report No./DNV Reg No.: 2010-5335 / 12KETUL-13 Rev 00, 2010-11-26 Table of Contents 1 INTRODUCTION... 1 2 SCOPE OF WORK...
More informationDURASHIELD 310 &
DURASHIELD 310 & 310-61 I. Scope A. This specification defines application requirements of DuraShield 310 & DuraShield 310-61 plural-component 100% solids, 3:1 volumetric mix ratio polyurethane to concrete,
More informationPRODUCT GUIDE: ZINC-RICH COATINGS. Version:
PRODUCT GUIDE: ZINC-RICH COATINGS Version: 08.07.17 305 Zinc Rich Epoxy Polyamide Primer Description: 305 is a user friendly zinc-rich epoxy primer formulated for use as a primer under acrylic, epoxy,
More informationProperty Test/Standard Description. US EPA method 24 (tested) (CARB(SCM)2007, SCAQMD rule 1113, Hong Kong)
Approved 16561;16840;18880 1,2 18880 epoxy mastic ^(ValidationDate) 1 Product description This is a two component polyamine cured epoxy mastic coating. It is a surface tolerant, abrasion resistance, high
More informationSECTION STRUCTURAL METAL FRAMING
SECTION 05100 STRUCTURAL METAL FRAMING PART 1 GENERAL 1.01 SUMMARY A. Section Includes: Structural steel framing including lintels, shelf angles, bearing plates, anchor bolts and other items as shown on
More informationHEMPEL S GALVOSIL 15780
For product description refer to product data sheet Scope: This application instruction covers surface preparation, application equipment and application of. For optimum performance, the following is recommended:
More informationRust-Oleum Industrial Brands Specification
Rust-Oleum Industrial Brands Specification Coating Specification for Rust-Oleum Virtual Solutions Coating Solution 23 A solvent based coating system High Performance 4315 High Heat Aluminum For service
More informationSECTION HIGH DENSITY POLYETHYLENE PIPE AND FITTINGS (PRESSURE PIPE)
SECTION 02623 HIGH DENSITY POLYETHYLENE PIPE AND FITTINGS (PRESSURE PIPE) PART 1 - GENERAL 1.1 SCOPE OF WORK A. Furnish all labor, materials, equipment and incidentals required and install high density
More informationMATERIAL SPECIFICATION FOR FRAMES, GRATES, COVERS, AND GRATINGS
ONTARIO PROVINCIAL STANDARD SPECIFICATION METRIC OPSS 1850 NOVEMBER 2007 MATERIAL SPECIFICATION FOR FRAMES, GRATES, COVERS, AND GRATINGS TABLE OF CONTENTS 1850.01 SCOPE 1850.02 REFERENCES 1850.03 DEFINITIONS
More informationMETALS Commissioning of Metals Structural Steel Framing Steel Studs... 2
~ 05-1 ~ 05 00 00 Metals 05 00 00 METALS... 2 05 08 00 Commissioning of Metals... 2 05 12 00 Structural Steel Framing... 2 05 12 30 Steel Studs... 2 05 45 00 METAL SUPPORT ASSEMBLIES... 2 05 50 00 METAL
More informationTNEMEC ELEVATED TEMERATURE VINYL ESTER LINING INSTALLATION GUIDE ProPolymer Series 1402, 1422 and 1432 Direct Food Contact FDA Title 21 CFR 175.
1.0 Scope 1.1 This recommendation covers the requirements for the surface preparation and the application of primers and finish coat linings for the interior surfaces of carbon/stainless steel vessels
More informationSECTION PAINTING AND COATING
SECTION 09 90 00 PART 1 - GENERAL 1.1 THE REQUIREMENT A. The Work of this section consists of furnishing and applying paint for miscellaneous non-galvanized ferrous surfaces. Galvanized ferrous surfaces
More information3M Scotchkote Liquid Epoxy Coating 323+
Product Description 3M TM Scotchkote TM Liquid Epoxy Coating 323+ is a two part liquid epoxy coating designed to protect steel pipe and other metal surfaces from corrosion. 3M TM Scotchkote TM Liquid Epoxy
More informationMATERIAL SPECIFICATION FOR FRAMES, GRATES, COVERS, AND GRATINGS
ONTARIO PROVINCIAL STANDARD SPECIFICATION OPSS.MUNI 1850 NOVEMBER 2018 MATERIAL SPECIFICATION FOR FRAMES, GRATES, COVERS, AND GRATINGS TABLE OF CONTENTS 1850.01 SCOPE 1850.02 REFERENCES 1850.03 DEFINITIONS
More informationTECHNICAL REQUIREMENTS AND SPECIFICATIONS. PROTECTIVE COATING OF STEEL (As Provided by Raven Lining Systems) FOREWORD
TECHNICAL REQUIREMENTS AND SPECIFICATIONS PROTECTIVE COATING OF STEEL (As Provided by Raven Lining Systems) FOREWORD This specification covers work, materials and equipment required for protecting and/or
More informationProtective Industrial Polymers - USA Manufacturer s Specification February 11, 2015
This specification covers InhibiChem SR-GF-L Enhanced Chemical and Solvent-Resistant Glass-Flake Reinforced Steel Tank Lining System. This system consists of a vinyl ester primer, and two troweled coats
More informationRefer to Substrates & Surface Preparation.
SELECTION & SPECIFICATION DATA Generic Type Description Features Aliphatic Acrylic Polyurethane High gloss finish with exceptional weathering performance characteristics. Used extensively in virtually
More informationApplication Guide for Internal Flow Efficiency Coating
Jotapipe FC 407 Application Guide for Internal Flow Efficiency Coating Jotapipe FC 407 Date of Last Revision: March 2015 Page 1 of 6 Contents 1.0 Product Description... 2 2.0 Surface preparation and cleanliness...
More informationProperty Test/Standard Description. matt (0-35) Flash point ISO 3679 Method 1
7461;7680 1 7680 zinc silicate VValidationDate). 1 Product description This is a two component polyamide cured zinc rich epoxy coating. It is a high solids, high zinc dust containing product. It conforms
More informationApplication Guide HI-TEMP 1027 APPLICATION GUIDE. Number: AG-3001 Revision: Page 1 of Introduction. 2. Where to apply Hi-Temp 1027
Page 1 of 7 This document provides information and details for the use and application of Hi-Temp 1027. It is designed to supplement the Hi-Temp 1027 Product Data sheet (PDS) and MSDS, not to replace them.
More informationSIGMAZINC 158. PRODUCT DATA SHEET January 7, 2015 (Revision of December 15, 2014) DESCRIPTION
DESCRIPTION Two-component, moisture-curing zinc (ethyl) silicate primer PRINCIPAL CHARACTERISTICS Certificate for ASTM A-490 class 'B' for slip coefficient Complies with the compositional requirements
More informationSECTION 15 STRUCTURAL STEEL
SECTION 15 STRUCTURAL STEEL 1 GENERAL 1.1 SCOPE Outline description This section applies to the provision, fabrication, treatment, erection and connection of structural steelwork. 1.2 CROSS REFERENCES
More informationSection 716. SHOP CLEANING AND COATING STRUCTURAL STEEL
716.01 Section 716. SHOP CLEANING AND COATING STRUCTURAL STEEL 716.01. Description. This work consists of shop cleaning and applying a complete coating system on new structural steel as a part of fabricating
More informationMATERIAL SPECIFICATION FOR FRAMES, GRATES, COVERS, AND GRATINGS
ONTARIO PROVINCIAL STANDARD SPECIFICATION OPSS 1850 APRIL 2018 (Formerly OPSS 1850, April 2013) Note: The MUNI implemented in April 2018 replaces OPSS 1850 COMMON, April 2013 with no technical content
More informationRust-Oleum Industrial Brands Specification
Rust-Oleum Industrial Brands Specification Coating Specification for Rust-Oleum Virtual Solutions Coating Solution 65 A solvent based coating system High Performance 9100 System 100 VOC DTM Epoxy Mastic
More informationPPG HI-TEMP PRODUCT DATA SHEET April 16, 2018 (Revision of September 5, 2017) DESCRIPTION
DESCRIPTION One-component, high-build heat-resistant inert multipolymeric matrix / inorganic ceramic coating PRINCIPAL CHARACTERISTICS Designed to prevent corrosion under insulation (CUI) of carbon steel
More informationTnemec Fluid Applied Thermal Break Long Form Specification
PART 1 GENERAL 1.01 DESCRIPTION Tnemec Fluid Applied Thermal Break Long Form Specification A. This specification covers labor, materials, equipment, and application necessary for, and incidental to, the
More informationSpecial Provision No. 911F04 March 1997
COATING STEEL RAILING SYSTEM(S) - Item No. Special Provision No. 911F04 March 1997 Definitions, Elimination of Pre-Start Material Sample, Material Requirements, Operational Constraints, Time Between Surface
More informationSECTION STRUCTURAL STEEL
SECTION 05120 PART 1 - GENERAL 1.1 RELATED DOCUMENTS A. Drawings and general provisions of the Contract, including General and Supplementary Conditions and Division 1 Specification Sections, apply to this
More informationB. Shop Drawings: Include plans, elevations, sections, details, and attachments.
SECTION 055119 - METAL GRATING STAIRS PART 1 - GENERAL 1.1 RELATED DOCUMENTS A. Drawings and general provisions of the Contract, including General and Supplementary Conditions and Division 01 Specification
More information