Schedule. Type of Test/ Properties Measured/ Range of Measurement

Transcription

1 LABORATORY LOCATION: (PERMANENT LABORATORY) Page: 1 of 9 PROFESSIONAL TESTING SERVICES SDN BHD 7 JALAN MEGA 1 TAMAN PERINDUSTRIAN NUSA CEMERLANG GELANG PATAH, JOHOR MALAYSIA This laboratory accredited under Skim Akreditasi Makmal Malaysia (SAMM) meets the requirements of :2005 General requirements for competence of testing and calibration laboratories. This Malaysian Standards is identical with ISO/IEC 17025:2005 published by the International Organization for Standardization (ISO). Tension Test (a) -Tension on test plates and tubular sections at ambient temperature in the range of 0 kn to 1000 kn with controlled strain rate and crosshead movement, including yield and proof stress. - Ultimate tensile strength of rebar in the range of 0 kn to 1000 kn - Modulus of elasticity on test pieces in the range of 0 kn to 1000 kn ASTM B ASTM E8/E8M 2015a SS 2-Part 1 : 1999 SS 2-Part 2 : 1999 SS 2-Part 3 : 1987 BS EN ISO : 2009 BS 4449+A2 : 2009 SS 18 -Part 1 : 1999 BS EN ISO 4136 : 2012 AS 1391 : 2007 (Amendment 1:2012) AS : 2003 *API (Addendum 1:2014) *NKK Rules Part K Chapter

2 Page: 2 of 9 (Continue) (b) Through Thickness Tensile Test *Lloyd s Pt.2, Chapter 3: Sect *ABS Pt.2, Chapter 1: Sect 1-17:2015 ASTM A770/770M 2003 (reapproved 2012) BS EN : 2004 (c) All Weld Tensile Test (d) Tensile test on cruciform and lapped joints. Hardness Test Vickers Hardness Test in the range of 0.3 kgf to 20 kgf ISO BS EN ISO AS : 2003 BS EN ISO 9018 : 2015 ASTM E E1 ASTM E bE1 BS EN ISO : 2011 BS EN ISO : 2005 AS : 2003 Rockwell Hardness Test ASTM E BS EN ISO : 2015

3 Page: 3 of 9 (Continue) Impact Test Charpy V-notch Impact Tests from ambient temperature down to -110oC and -196oC Bend Test / Roller Bend Test *API (Addendum ) Bend Test / Rebend Test *SS 32 Part 1: 1999 *SS 32 Part 2: 1986 *SS 18 Part 1: 1999 Fracture Test ASTM E c BS EN ISO : 2010 AS : 2003 ASTM E ASTM E AS : 2003 AS : 2003 BS EN ISO 5173: A1 : 2011 SS 2: Part SS 2: Part SS 2: Part BS 4449: A2 : 2009 SS AWS D1.1/D1.1M 2015 Clause ASME IX 2015 Clause QW-182

4 Page: 4 of 9 (Continue) Flattening Test *ABS Pt.2, Chapter 3: Sect *Lloyd s Pt.2, Chapter 2: Sect Steel Wire Mesh (Grade 300 & 500) (Grade 485) Flaring / Flanging Test (Up to outside diameter of 2 inches) *ABS Pt.2, Chapter 3: Sect 5-23& *Lloyd s Pt.2, Chapter 2: Sect 4.3& Nick Break Test *API (Addendum ) Tension Test Tension on steel wires taken from wire fabric at ambient temperature in the range of 0 kn to 1000 kn with controlled strain rate and crosshead movement, including yield and proof stress. BS EN ISO : 2009 * SS 32 Part 1: 1999 * SS 32 Part 2: 1986 * SS 18 Part 1: 1999 Bend and Rebend Test SS 427: 1998 Weld Shear Test SS 32 Part 1 : 1999 Annex A SS 32 Part 2 : 1986 Clause 4.8.4

5 Page: 5 of 9 Microstructural Test 1. - Macro Examination - Macroscopic Examination on Welds *API (Addendum ) 2. Macro-etching of Metals and Alloys Remarks: (*) denotes product/materials specification 2. Soo Boon Chai 3. Lee Chen Heng ASTM E (Reapproved 2012) BS EN ISO : 2013 ASTM E AS : 2003 Tensile Test at Elevated Temp, (up to 750 C) in the range of 0 kn to 300 kn with controlled strain rate & crosshead movement, including yield & proof stress ASTM E Brinell Hardness Test ASTM E a BS EN ISO : Soo Boon Chai

6 Page: 6 of 9 Fracture Mechanics Toughness Tests Crack Tip Opening Displacement (CTOD) test. BS :1991 ISO (Technical Corrigendum 1:2008) BS EN ISO : 2010 Fracture Mechanics Toughness Tests Crack Tip Opening Displacement (CTOD) - Single Edge Notched Tension (SENT) DNV-RP-F108 : Jan 2006 BS 8571: 2014 Fatigue Test ISO 1099 : 2006 BS EN ISO : 2010 BS EN ISO : 2010 BS 4449 : A3 : 2016 Corrosion Test Hydrogen Induced Cracking (HIC) Test Sulfide Stress Corrosion Cracking (SSCC) Test NACE Standard TM Item No ASTM G (Reapproved 2011) BS EN ISO : 2012 BS EN ISO : 1995 NACE Standard TM Item No Wong Kok Wei 3. Tan Keng Lip

7 Page: 7 of 9 Corrosion Test Pitting Corrosion Test ASTM G (Reapproved 2015) (Method A) 2. Tan Horng You Intergranular Corrosion Test ASTM A (Practice E) Microstructural Test Detection of Detrimental Intermetallic Phase in Duplex Austenitic/Ferritic Stainless Steels Coating Mass Determination for Zinc or Zinc-Alloy Coatings ASTM A (Method C) ASTM A90/A90M-2013 BS EN ISO 1460 : 1995

8 Page: 8 of 9 (METALLURGICAL) Carbon and low alloys steel Elements: Al, B, C, Cr, Co, Cu, Mn, Mo, N, Ni, Nb, P, Si, S, Sn, Ti, V, W Stainless steels Elements: Cr, Ni, Mo, Mn, Si, N, Cu, C, P, S Nickel Alloys Elements: Al, C, Cr, Co, Cu, Fe, Mn, Mo, Nb, P, Si, S, Ti, V, W 2. Tan Horng You Metallurgical Testing Elemental Analysis (Metal Composition Determination) Elemental Analysis (Metal Composition Determination) Elemental Analysis (Metal Composition Determination) ASTM A a ASTM E ASTM A a ASTM E In house Method PTS-M001 (Based on Arc Spark Spectrometry Method)

9 Page: 9 of 9 SITE TESTING: CATEGORY I Dimensional Measurement - Linear measurement in the range of up to 20 m. - Weight measurement in the range of up to 500 kg. - Corner radius measurement in the range of 0.5 mm to 13 mm. * ASTM A6/A6M 2016a * ASTM A20/A20M 2015 * BS EN : 2004 * BS EN : 2004 Remarks: (*) denotes product/materials specification 2. Soo Boon Chai In-House Test Method PTS-M002