CLASSIFICATION OF REACTION TO FIRE FIRES-CR AUPE

Transcription

1 CLASSIFICATION OF REACTION TO FIRE Polymethylmethacrylate PMMA, Akrylon XT This is an electronic version of a classification report which was made as a copy of classification report officially issued in a form. The electronic version of a classification report shall be used only for informative purpose. Any information listed in this classification report is the property of the sponsor and shall not be used or published without written permission. Contents of this file may only be modified by the editor i.e. FIRES, s.r.o. Batizovce. Sponsor is allowed to publish this classification report in parts only with written permission of the editor. FIRES 9/S4-10/02/2010-E-el

2 CLASSIFICATION OF REACTION TO FIRE IN ACCORDANCE WITH EN : A1: 2009 with direct field of application Name of the product: Polymethylmethacrylate PMMA, Akrylon XT Sponsor: Prepared by: Polycasa Slovakia, s.r.o. M.R.Štefánika Žilina Slovak Republic FIRES, s.r.o. Osloboditeľov Batizovce Slovak Republic Tested property: Reaction to fire Test method: : 2002 Type of test: Accredited Task No.: PR Date of issue: Reports: 3 Copy No.: 2 Distribution list: Copy No. 1 Copy No. 2 Copy No. 3 FIRES, s. r. o., Osloboditeľov 282, Batizovce, Slovak Republic (electronic version) Polycasa Slovakia, s.r.o., M.R.Štefánika 71, Žilina, Slovak Republic (electronic version) Polycasa Slovakia, s.r.o., M.R.Štefánika 71, Žilina, Slovak Republic This classification report may only be used or reproduced in its entirety. This report includes accreditation mark SNAS with additional mark ILAC-MRA. SNAS is signatory of ILAC-MRA, Mutual recognition agreement (of accreditation), which is focused on promoting of international acceptance of accredited laboratory data and reducing technical barriers to trade, such as the retesting of products on markets of signatories. More information about ILAC-MRA is on Signatories of ILAC-MRA are e.g. SNAS (Slovakia), CAI (Czech Republic), PCA (Poland), DakkS (Germany) or BMWA (Austria). Up to date list of ILAC-MRA signatories is on FIRES, s.r.o. Batizovce is full member of EGOLF also, more information FIRES 049/S2-28/03/2014-E FIRES, s.r.o., Osloboditeľov 282, Batizovce, Slovak Republic tel , fax , Notified Body No. 1396, Approved Body No. SK01, Member of EGOLF

3 1. INTRODUCTION This classification report defines the reaction to fire classification assigned to element polymethylmethacrylate PMMA, Akrylon XT in accordance with the procedures given in EN : A1: DETAILS OF CLASSIFIED PRODUCT 2.1 GENERAL The element, polymethylmethacrylate PMMA, Akrylon XT is used in board form as a door glazing, separating walls, roofs ceilings and from thickness 10 mm as a sound barrier to the highways, after treatment by formation or bending as skylights, covers on lamps, luminous boards in accordance with EN ISO : PRODUCT DESCRIPTION Polymethylmethacrylate PMMA, type Akrylon XT is made from PMMA granulate, which contains from 4,5 % up to 6 % MA. The additional additives, which modify the polymer properties or its appearance, are possible to add (antioxidants, inner oils, UV absorbers etc.) Boards are made with thickness from 1,8 mm up to 25 mm and with bulk density from 1190 kg.m -3 up to 44 kg.m TEST REPORTS IN SUPPORT OF CLASSIFICATION 3.1 TEST REPORTS No. Name of laboratory Name of sponsor Test report No. Date of the test Test method [1] FIRES, s.r.o., Batizovce, SK MPA NRW, Erwitte, Germany Barlo Plastics Slovakia s.r.o., SK Barlo Plastics GmbH, Germany FIRES RF 040/04 CS STN EN ISO DIN EN ISO [1] - Test specimens were conditioned according to EN before the fire resistance test [1] Tested product Tested product Polymethylmethacrylate PMMA, AKRYLON XT, clear sheet, thickness 1,8 mm, bulk density 1190 kg.m -3 Tested product Polymethylmethacrylate PMMA, BARLO XT, clear sheet, thickness 1,8 mm, bulk density 1171 kg.m -3 ; Tested product Polymethylmethacrylate PMMA, BARLO XT opal, white translucent sheet, thickness 2 mm, bulk density 27 kg.m -3 ; Tested product Polymethylmethacrylate PMMA, BARLO XT opal, white translucent sheet, thickness 2 mm, bulk density 00 kg.m -3 ; Tested product Polymethylmethacrylate PMMA, BARLO XT opal, white opaque sheet, thickness 2 mm, bulk density 44 kg.m -3 ; Tested product Polymethylmethacrylate PMMA, BARLO XT opal, white opaque sheet, thickness 6 mm, bulk density 20 kg.m -3 ; FIRES 049/S2-28/03/2014-E Page: 2/5

4 3.2 TEST RESULTS AKRYLON XT clear sheet, thickness 1,8 mm, bulk density 1190 kg.m -3 [1] BARLO XT clear sheet, thickness 25 mm, bulk density 1171 kg.m -3 BARLO XT opal, white translucent sheet, thickness 2 mm, bulk density 27 kg.m -3 FIRES 049/S2-28/03/2014-E Page: 3/5

5 BARLO XT opal, white translucent sheet, thickness 4 mm, bulk density 00 kg.m -3 BARLO XT opal, white opaque sheet, thickness 2 mm, bulk density 44 kg.m -3 BARLO XT opal, white opaque sheet, thickness 6 mm, bulk density 20 kg.m -3 * Specimens main surface and edge (bottom part of boards) were exposed. 4. CLASSIFICATION AND FIELD OF APPLICATION 4.1 REFERENCE OF CLASSIFICATION This classification has been carried out in accordance with clause 11.3 of EN : A1: FIRES 049/S2-28/03/2014-E Page: 4/5

6 4.2 CLASSIFICATION The product, Polymethylmethacrylate PMMA, Akrylon XT, in relation to its reaction to fire behaviour is classified: E The additional classification in relation to smoke production is: - The additional classification in relation to is: - The format of the reaction to fire classification for construction products excluding floorings is: Fire behaviour Smoke production Flaming droplets E - - -, - - Reaction to fire classification: E 4.3 FIELD OF APPLICATION This classification is valid for the following final use applications: Thickness change in the thickness from 1,8 mm up to 25 mm for clear sheets and from 2 mm up to 25 mm for translucent colour sheets is allowed; Bulk density change in the bulk density from 1190 kg.m -3 up to 44 kg.m -3 is allowed; Chemical composition no change in chemical composition of product is allowed; 5. LIMITATIONS This classification document does not represent type approval or certification of the product. The classification is valid provided that the product, field of application and standards and regulations are not changed. Approved: Signed: Ing. Štefan Rástocký leader of the testing laboratory Ing. Samuel Skokan technician of the testing laboratory FIRES 049/S2-28/03/2014-E Page: 5/5