HORIZONTAL CONTINUOUS CASTING OF Al AND Al-Si ALLOY IN SEMI-INDUSTRIAL CONDITIONS. Tomasz WRÓBEL, Jan SZAJNAR
|
|
- Caroline Miller
- 6 years ago
- Views:
Transcription
1 HORIZONTAL CONTINUOUS CASTING OF Al AND Al-Si ALLOY IN SEMI-INDUSTRIAL CONDITIONS Tomasz WRÓBEL, Jan SZAJNAR Silesian University of Technology, Foundry Department, Towarowa 7, Gliwice, Poland, Abstract In paper is presented idea of construction and influence of selected parts of stand of horizontal continuous casting on quality of aluminum with purity of 99,5% and 99,8% and AlSi2 alloy ingots. The main parts of the made stand belong to induction furnace, which is also tundish, water cooling continuous casting mould, system of recooling, system of continuous ingot drawing and cutting. Mainly was considered influence of horizontal electromagnetic stirrer, which was placed in continous casting mould on refinement of ingots structure. The degree of structure refinement was represented by equiaxed crystals zone content on transverse section of ingot and average area of macro-grain in this zone. Effect of structure refinement obtained by influence of electromagnetic field was compared with refinement obtained by use of traditional inoculation, which consists in introducing of additives i.e. Ti, B and C to metal bath. The results of studies show possibility of effective refinement of Al and AlSi2 alloy primary structure, only with use of horizontal electromagnetic field and without necessity of application of inoculants. This method of inoculation is important, because inoculants decrease the degree of purity and electrical conductivity of pure aluminum and moreover are reason of point cracks formation during rolling of ingots. Keywords: aluminum, alloy, inoculation, continuous casting, electromagnetic field; 1. INTRODUCTION Technology of continuous casting is applying usually in production of ingots of Fe [1, 2], Al [3] or Cu [4] alloys, with high yield and quality. The quality of continuous ingot in comparison with traditional gravity casting with use of ingot mould concerns refinement and uniform of ingot structure, which results from solidification of metal in water cooling continuous casting mould. Moreover the refinement of ingot structure can be increases by forced liquid metal movement in time of its solidification results from influence of electromagnetic field [1 6]. The forced liquid metal movement guarantees elimination of unfavorable (mainly for plastic deformation of ingot) columnar macrograins from ingot primary structure at simultaneously increase amount of favorable equiaxed macrograins [5, 6]. Other method of structure refinement is use of traditional inoculation consists in introducing into metal bath of specified substances, called inoculants [7]. Inoculants increase grains density as result of creation of new particles in consequence of braking of grains growth velocity, decrease of surface tension on interphase boundary of liquid nucleus, decrease of angle of contact between the nucleus and the base and increase of density of bases to heterogeneous nucleation [7 9]. The effectiveness of this type of inoculation depends significantly on crystallographic match between the base and the nucleus of inoculated metal. Therefore active bases to heterogeneous nucleation for aluminum and particles, which have high melting point i.e. titanium borides, titanium carbides, titanium nitirdes, aluminum borides and aluminum titanide [8]. But this effective methods of inoculation in comparison with inoculation with use of electromagnetic field has three faults i.e. inoculants decrease the degree of purity and electrical conductivity of pure aluminum [8] and moreover are reason of point cracks formation during rolling of ingots [10].
2 2. THE RANGE AND RESULTS OF STUDIES On Fig.1 is presented scheme of the stand of horizontal continuous casting, which was constructed and built in Foundry Departmnet of Silesian Univestity of Technology. The main parts of the made stand belong to induction furnace, which is also tundish, water cooling continuous casting mould, system of recooling, system of continuous ingot drawing and cutting, which realized method of ingot movement defined by combination of forwards feed, stop and backwards performed in specified time and velocity from 100 to 500mm/min set in control system. Whereas on Fig.2 is presented view of example continous casting process of Al made on described stand. Fig. 1 Scheme of stand of horizontal continuous casting: 1 induction furnace (tundish), 2 continuous casting mould, 3 system of recooling, 4 system of ingot drawing, 5 system of ingot cutting Fig. 2 Example view of horizontal continous casting process: 1 continuous casting mould, 2 Al ingot, 3 dummy bar
3 Important element of presented stand, which strongly influences on structure refinement of continuous ingot is electromagnetic stirrer placed in continuous casting mould (Fig.3), which enables cast of cylindrical ingots with diameter from 20 to 40mm. The principle of operation of stirrer based on construction of induction coil, which generated horizontal electromagnetic filed. Efficiency of influence of electromagnetic field on intensity of liquid metal stirring is depending mainly on value of magnetic induction in inside the induction coil. As show on Fig.4a the value of magnetic induction (B) depends on current intensity (I) supplied to the induction coil. Moreover as show in papers [6 and 8] is a possibility of increasing the force, which creates movement of liquid metal and in result of this the velocity of its rotation in mould, also by increasing the frequency (f) of the current supplied to the induction coil (Fig.4b). Fig.3 Cross-section of continuous casting mould contains electromagnetic stirrer a) b) B [mt] 30 B = 6,26I + 3,02 R 2 = 0, I [A] Fig.4 The influence of the current (I) supplied to the induction coil on magnetic induction (B) (Fig. a) and common influence of magnetic induction and frequency (f) of the current supplied to the induction coil on force value (F), which creates movement of liquid metal (Fig. b)
4 Forced movement of liquid metal in time of its solidification generated by influence of electromagnetic field results in refinement of ingot primary structure, which was represented by equiaxed crystals zone content (SKR) on transverse section of ingot and average area of macro-grain in this zone (PKR). On Fig.5 7 are presented example macrostructures of ingots of aluminum with purity of 99,5% and 99,8% and alloy AlSi2 respectively in initial state, after traditional inoculation with use of Ti, B and/or C additives and after inoculation with use of horizontal electromagnetic field. a) b) c) Fig. 5 Macrostructure of aluminum with a purity of 99,5% ingots: a - in initial state, b - after inoculation with use of master alloys AlTi3C AlTi5B1 (Ti = 25ppm, B = 3ppm, C 0.5ppm) and c - after inocualtion with use of horizontal electromagnetic field (B = 60mT, f = 100Hz) a) b) c) Fig. 6 Macrostructure of aluminum with a purity of 99,8% ingots: a - in initial state, b - after inoculation with use of master alloy AlTi5B1 (Ti = 25ppm, B = 5ppm) and c - after inocualtion with use of horizontal electromagnetic field (B = 60mT, f = 100Hz) a) b) c) Fig. 7 Macrostructure of AlSi2 alloy ingots: a - in initial state, b - after inoculation with use of master alloy AlTi5B1 (Ti = 0,1%, B = 0,02%) and c - after inocualtion with use of horizontal electromagnetic field (B = 60mT, f = 100Hz)
5 On the basis of obtained results was affirmed that refinement of primary structure of pure Al and AlSi2 alloy obtained with use of horizontal electromagnetic field is larger than in initial state and is comparable with obtained with use of traditional inoculation (Fig.8). Fig.8 Characteristic of primary structure of pure Al and AlSi alloy in initial state, after inoculation by Ti, B and/or C additives and after inoculation by use of horizontal electromagnetic field 3. SUMMARY In conclusion can say, that even endogenous inoculation with small amount of Ti, B and/or C strongly increase on refinement in primary structure of pure aluminum and AlSi2 alloy. It results from reactions, which proceed between inoculating elements and inoculated metal or charge impurities. These reactions lead to formation of active bases to heterogeneous nucleation of aluminum as high melting small particles of type TiB, TiB 2, AlB 2, Al 3 Ti and TiC or TiN, which have analogy in crystal lattice with Al. However on the basis of conducted analysis of the literature and results of authors researches it was affirmed, that the horizontal electromagnetic field generated by stirrer (induction coil) supplied by current with frequency larger than power network, influences liquid metal in time of its solidification in mould simultaneously generates thermal and mechanical erosion of crystallization front, what guarantees
6 refinement of primary structure of pure Al and AlSi2 alloy without necessity of application of inoculants sort Ti, B and/or C. This method of exogenous inoculation is important, because Ti, B and C decrease the degree of purity and electrical conductivity of pure aluminum. Moreover titanium, boron and carbon are reason of point cracks formation during rolling of ingots. ACKNOWLEDGEMENTS Project financed from means of National Science Centre LITERATURE [1] ADAMCZYK, J. Engineering of metallic materials. Gliwice: Publishers of Silesian University of Technology, 2004, 342 p. ISBN [2] SZAJNAR, J., STAWARZ, M., WRÓBEL, T., SEBZDA, W., GRZESIK, B., STĘPIEŃ, M. Influence of continuous casting conditions on grey cast iron structure. Archives of Materials Science and Engineering, 2010, vol. 42, no. 1, p. ISSN [3] LEE, D., KANG, S., CHO, D., KIM, K. Effects of casting speed on microstructure and segregation of electromagnetically stirred aluminum alloy in continuous casting process. Rare Metals, 2006, vol. 25, special issue, p. ISSN [4] YAN, Z., JIN, W., LI, T. Effect of rotating magnetic field (RMF) on segregation of solute elements in CuNi10Fe1Mn alloy hollow billet. Journal of Materials Engineering and Performance. 2012, vol. 21, no. 9, p. ISSN [5] SZAJNAR, J., WRÓBEL, T. Influence of magnetic field and inoculation on size reduction in pure aluminium structure. International Journal of Materials and Product Technology, 2008, vol. 33, no. 3, p. ISSN [6] WRÓBEL, T. The influence of inoculation type on structure of pure aluminum. From Conference Proceedings METAL 2012: 21st International Conference on Metallurgy and Materials. Brno, Czech Republic: TANGER, 2012, p. [7] FRAŚ, E. Crystallization of metals. Warsaw: WNT, 2003, 470 p. ISBN [8] WRÓBEL, T. Structure of pure aluminum after endogenous and exogenous inoculation. Chapter no. 21 from Advances in Crystallization Processes. Edited by MASTAI, Y. Rijeka, Croatia: INTECH, 2012, p. ISBN [9] JANERKA, K., BARTOCHA, D., SZAJNAR, J., JEZIERSKI, J. The carburizer influence on the crystallization process and the microstructure of synthetic cast iron. Archives of Metallurgy and Materials, vol. 55, no. 3, p. ISSN [10] KELES, O., DUNDAR, M. Aluminum foil: its typical quality problems and their causes. Journal of Materials Processing Technology, 2007, vol. 186, no.1-3, p. ISSN
The Stand of Horizontal Continuous Casting of Al and its Alloys
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 13 Issue 3/2013 113 118 23/3
More informationInfluence of Inoculation on Properties of Aluminium EN AW-Al99,5
ARCHIVES of FOUNDRY ENGINEERING Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 7 Issue 3/2007 157 162 30/3 Influence of Inoculation
More informationStructure of Pure Aluminum After Endogenous and Exogenous Inoculation
21 Structure of Pure Aluminum After Endogenous and Exogenous Inoculation Tomasz Wróbel Silesian University of Technology, Foundry Department Poland 1. Introduction The phenomenon of crystallization following
More informationTECHNOLOGICAL PARAMETERS INFLUENCE ON CONTINUOUS CAST GREY IRON. Wojciech SEBZDA, Jan SZAJNAR
TECHNOLOGICAL PARAMETERS INFLUENCE ON CONTINUOUS CAST GREY IRON Wojciech SEBZDA, Jan SZAJNAR Foundry Department, Silesian University of Technology, ul. Towarowa 7, 44-100 Gliwice, Poland, EU, wojciech.sebzda@polsl.pl
More informationA R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume Issue 2 DOI: /amm
A R C H I V E S O F M E T A L L U R G Y A N D M A T E R I A L S Volume 59 2014 Issue 2 DOI: 10.2478/amm-2014-0125 J. SZAJNAR, M. STAWARZ, T. WRÓBEL, W. SEBZDA INFLUENCE OF SELECTED PARAMETERS OF CONTINUOUS
More informationStereological Analysis of Carbides in Hypoeutectic Chromium Cast Iron
A R C H I V E S o f F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 15 Issue 2/2015 17 22 4/2 Stereological
More informationSimulation of the ingot extraction in the continuous casting process
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 11 Issue 3/2011 93 100 19/3 Simulation
More informationCrystallization of Low-alloyed Construction Cast Steel Modified with V and Ti
ARCHIVES of FOUNDRY ENGINEERING DOI: 10.2478/afe-2013-0067 Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (2299-2944) Volume 13 Issue 3/2013 92 96 Crystallization
More informationAnalysis of columnar crystals growth during the solidification in magnetic field J. Szajnar
Analysis of columnar crystals growth during the solidification in magnetic field J. Szajnar Foundry Institute, Silesian Technical University, 44-10 Gliwice, Towarowa 7, Poland ABSTRACT Interaction of rotational
More informationSiMo Ductile Iron Crystallization Process
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-331) Volume 17 Issue 1/217 147 152 27/1 SiMo
More informationStrength properties examination of high zinc aluminium alloys inoculated with Ti addition
DOI: 10.1007/s41230-017-6098-y Strength properties examination of high zinc aluminium alloys inoculated with Ti addition *J. Buraś 1, M. Szucki 1, G. Piwowarski 1, W. K. Krajewski 1 and P. K. Krajewski
More informationContinuous Casting of Aluminum and Copper Clad Ingots under Electromagnetic Fields
Continuous Casting of Aluminum and Copper Clad Ingots under Electromagnetic Fields Joonpyo Park, Jong Ho Kim, Myoung Gyun Kim, Young Joon Lee, Tingu Li, Kwang Seok Lee, Jong Sup Lee To cite this version:
More informationModel castings with composite surface layer - application
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 8 Issue 3/2008 105 110 19/3 Model
More informationGrain Refinement of Aluminum Alloys
Grain Refinement of Aluminum Alloys Presented By SUBRATA SAHA Objectives Whats and Whys? Grain Refinement is a process used for grain boundary strengthening of casting material. Aluminum alloys with ultra
More informationSolidification and Crystallisation 5. Formation of and control of granular structure
MME 345 Lecture 08 Solidification and Crystallisation 5. Formation of and control of granular structure Ref: [1] A. Ohno, The Solidification of Metals, Chijin Shokan Co. Ltd., 1976 [2] P. Beeley, Foundry
More informationEffect of magnetostatic field on microstructure of 5005 aluminum alloy sheet by roll-casting
University of Wollongong Research Online Faculty of Engineering and Information Sciences - Papers: Part A Faculty of Engineering and Information Sciences 2011 Effect of magnetostatic field on microstructure
More informationLearning Objectives. Chapter Outline. Solidification of Metals. Solidification of Metals
Learning Objectives Study the principles of solidification as they apply to pure metals. Examine the mechanisms by which solidification occurs. - Chapter Outline Importance of Solidification Nucleation
More informationMulti-layers castings
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 10 Issue 1/2010 181 186 31/1
More informationCarburizer particle dissolution in liquid cast iron computer simulation
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 10 Issue 1/2010 7 14 1/1 Carburizer
More informationMetal Casting. Manufacturing Processes for Engineering Materials, 5th ed. Kalpakjian Schmid 2008, Pearson Education ISBN No.
Metal Casting Important factors in casting Solidification of the metal from its molten state and accompanying shrinkage Flow of the molten metal into the mold cavity Heat transfer during solidification
More informationTHE INFLUENCE OF COOLING RATE ON GRAIN REFINING OF 6063 ALLOY WITH ALTIC
U.P.B. Sci. Bull., Series B, Vol. 68, No. 2, 2006 THE INFLUENCE OF COOLING RATE ON GRAIN REFINING OF 6063 ALLOY WITH ALTIC C.D. Urban În lucrare se analizează influenţa vitezei de răcire asupra gradului
More informationTHERMAL EFFECT OF PHASE TRANSFORMATIONS IN HIGH SILICON CAST IRON. Marcin Stawarz, Krzysztof Janerka, Jan Jezierski, Jan Szajnar
THERMAL EFFECT OF PHASE TRANSFORMATIONS IN HIGH SILICON CAST IRON Marcin Stawarz, Krzysztof Janerka, Jan Jezierski, Jan Szajnar Silesian University of Technology, Faculty of Mechanical Engineering, Department
More informationInfluence of Remelting AlSi9Cu3 Alloy with Higher Iron Content on Mechanical Properties
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 18 Issue 3/2018 25 30 4/3 Influence
More informationEffectiveness of Zn-Ti Based Refiner of Al and Zn Foundry Alloys
Effectiveness of Zn-Ti Based Refiner of Al and Zn Foundry Alloys W. K. Krajewski* 1, A. L. Greer**, J. Zych* and J. Buraś* * AGH University of Science and Technology, Faculty of Foundry Engineering. Reymonta
More informationMelt Conditioned Direct Chill Casting (MC-DC) Process for Production of High Quality Aluminium Alloy Billets
Melt Conditioned Direct Chill Casting (MC-DC) Process for Production of High Quality Aluminium Alloy Billets Jayesh B Patel 1, a *, Hu-Tian Li 1, Xia Mingxu 1, Simon Jones 1, Sundaram Kumar 2, Keyna O
More informationMagnetically-Controlled Electroslag Melting (MEM) of Multicomponent Titanium Alloys
Magnetically-Controlled Electroslag Melting (MEM) of Multicomponent Titanium Alloys Y.Y. KOMPAN The E. O. Paton Electric Welding Institute, Ukraine NATO ARW Metallic Materials with High Structural Efficiency
More informationProgress of some techniques on electromagnetic metallurgy
Progress of some techniques on electromagnetic metallurgy Engang Wang To cite this version: Engang Wang. Progress of some techniques on electromagnetic metallurgy. 8th International Conference on Electromagnetic
More informationContinuous Rheocasting for Aluminum-Copper Alloys
Materials Transactions, Vol. 43, No. 9 (2002) pp. 2285 to 2291 c 2002 The Japan Institute of Metals Continuous Rheocasting for Aluminum-Copper Alloys Kiyoshi Ichikawa, Masahito Katoh and Fumio Asuke Ecology-Oriented
More informationUniMet LLC and Siberian Federal University developments in collaboration with MHD Center GmbH
UniMet LLC and Siberian Federal University developments in collaboration with MHD Center GmbH Propose the collaboration for R&D and implementation the following MHD technologies for aluminium industry:
More informationSOLIDIFICATION, PHASE DIAGRAM & STEELS
MODULE TWO SOLIDIFICATION, PHASE DIAGRAM & STEELS 4. SOLIDIFICATION Introduction Mechanism of solidification - crystallization and development of cast structure - nucleation and grain growth - dendritic
More informationGrain Refinement of Al-Si Alloys by Nb-B Inoculation. Part 1: Concept Development and Effect on Binary Alloys. Part 2: Application to Commercial
Grain Refinement of Al-Si Alloys by Nb-B Inoculation. Part 1: Concept Development and Effect on Binary Alloys. Part 2: Application to Commercial Alloys 1 Grain refinement of Al-Si alloys by Nb-B inoculation
More informationSolidification. Nov. 2010
Solidification Nov. 2010 Rapid Solidification (10 5 K/s) Rapidly cool or quench to produce amorphous or glassy structure (metallic glass) Rapid Solidification Cooling
More informationPrincipals of Billet Making
Billet quality directly controls the quality of extrusions and affects productivity, in term profitability. The quality of billets& cost are the two important considerations for extrusion producers. Day
More informationRUNNING HOT. Sub-topics. Fuel cells Casting Solidification
RUNNING HOT Sub-topics 1 Fuel cells Casting Solidification CONCEPT OF FUEL CELLS International concerns regarding the emission of greenhouse gases and the trend toward distributed power generation are
More informationApplication of Ni-Mg-Ce Master Alloy Scrap for Inoculation of Copper-Nickel Alloys
International Conference with Elements of School for Young Scientists on Recycling and Utilization of Technogenic Formations (2017) Conference Paper Application of Ni-Mg-Ce Master Alloy Scrap for Inoculation
More informationMICROSTRUCTURE AND PROPERTIES OD RAPID SOLIDIFIED AL-SI-FE AND AL-SI-FE-CR ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION. Filip PRŮŠA*, Dalibor VOJTĚCH
MICROSTRUCTURE AND PROPERTIES OD RAPID SOLIDIFIED AL-SI-FE AND AL-SI-FE-CR ALLOYS PREPARED BY CENTRIFUGAL ATOMIZATION Filip PRŮŠA*, Dalibor VOJTĚCH Department of Metals and Corrosion Engineering, Institute
More informationANOMALOUS GRAIN COARSENING BEHAVIOUR IN GRAIN-REFINED ALUMINIUM ALLOYS CAST USING LOW SUPERHEAT
Abstract ANOMALOUS GRAIN COARSENING BEHAVIOUR IN GRAINREFINED ALUMINIUM ALLOYS CAST USING LOW SUPERHEAT. Chemical grain refinement of aluminium alloys has been commercially practiced for many years. Low
More informationEffect of Al5Ti1B master alloy on microstructures and properties of AZ61 alloys
Effect of Al5Ti1B master alloy on microstructures and properties of AZ61 alloys MA Xu-liang( ) 1, 2, WANG Xiang( ) 2, LI Xin-lin( ) 2, YANG Lei( ) 2 1. School of Materials Science and Engineering, Harbin
More informationEFFECT OF YTTRIUM ADDITION ON MICROSTRUCTURE OF ALLOY Ti-47Al, PREPARED BY PLASMA MELTING AND VACUUM INDUCTION MELTING
EFFECT OF YTTRIUM ADDITION ON MICROSTRUCTURE OF ALLOY Ti-47Al, PREPARED BY PLASMA MELTING AND VACUUM INDUCTION MELTING Tomáš ČEGAN, Miroslav KURSA VŠB-TU Ostrava, 17. listopadu 15, 708 33, Ostrava-Poruba,
More informationInvestigation of Wear Resistant of Low-Alloyed and Chromium Cast Steel
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 12 Issue 2/2012 79 84 16/2 Investigation
More informationPhase Transformation Die Casting Process for Manufacturing a Thin- Type Product and Its Mechanical Performance Assessment
Key Engineering Materials Online: 2004-10-15 ISSN: 1662-9795, Vols. 274-276, pp 535-540 doi:10.4028/www.scientific.net/kem.274-276.535 2004 Trans Tech Publications, Switzerland Phase Transformation Die
More informationEffects of Mechanical Stirring and Vibration on the Microstructure of Hypereutectic Al-Si-Cu-Mg Alloy Billets
Materials Transactions, Vol. 48, No. 5 (2007) pp. 960 to 966 Special Issue on New Developments and Analysis for Fabrication of Functional Nanostructures #2007 The Japan Institute of Metals Effects of Mechanical
More informationCHAPTER INTRODUCTION
1 CHAPTER-1 1.0 INTRODUCTION Contents 1.0 Introduction 1 1.1 Aluminium alloys 2 1.2 Aluminium alloy classification 2 1.2.1 Aluminium alloys (Wrought) 3 1.2.2 Heat treatable alloys (Wrought). 3 1.2.3 Aluminum
More informationGrain Refiner Fade in Aluminium Castings
Proceedings of the 9 th International Conference on Aluminium Alloys (2004) Edited by J.F. Nie, A.J. Morton and B.C. Muddle Institute of Materials Engineering Australasia Ltd 705 Grain Refiner Fade in
More informationChromium and copper influence on the nodular cast iron with carbides microstructure
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (8973) Volume Issue 4/2 47 54 /4 Chromium and copper
More informationStructure of AlSi Skeleton Castings
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-331) Volume 12 Issue 2/212 147 152 29/2 Structure
More informationMetallurgy of Aluminum Die Casting Alloys EC 305 Dave Neff
Metallurgy of Aluminum Die Casting Alloys EC 305 Dave Neff Dave Neff OUTLINE Where aluminum comes from Why alloys are useful Alloy designation and nomenclature Specific roles of alloy elements Properties
More informationPrimary Crystallization Studies and Abrasion Analysis of Cr-Ni-Mo Cast Steel
ARCHIVES of FOUNDRY ENGINEERING Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 15 Issue 4/2015 75 80 15/4 Primary Crystallization Studies
More informationEFFECT OF SOME GRAIN REFINERS ON THE MECHANICAL PROPERTIES OF ALUMINUM
EFFECT OF SOME GRAIN REFINERS ON THE MECHANICAL PROPERTIES OF ALUMINUM Prof. Adnan I.O.Zaid e-mail: adnan_kilani@yahoo.com ABSTRACT It is well established that aluminum and its alloys are grain refined
More informationPREPARATION AND PROPERTIES OF Al Fe AND Al Fe Cr ALLOYS. Petra HANUSOVÁ 1, Pavel NOVÁK 2
PREPARATION AND PROPERTIES OF Al Fe AND Al Fe Cr ALLOYS Petra HANUSOVÁ 1, Pavel NOVÁK 2 1 Brno University of Technology, Faculty of Mechanical Engineering, Institute of Material Science and Engineering,
More informationTHE EFFECT OF THE VOLUME OF INCLUSIONS ON THE FATIGUE STRENGTH COEFFICIENT OF STRUCTURAL STEEL
ISSN 1392-1134 / elssn 2345-0371 Agricultural Engineering, Research papers, 2016, vol. 48, 1-6 p. THE EFFECT OF THE VOLUME OF INCLUSIONS ON THE FATIGUE STRENGTH COEFFICIENT OF STRUCTURAL STEEL Tomasz Lipiński,
More informationVibration influence on structure and density of aluminum alloys
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS Vibration influence on structure and density of aluminum alloys To cite this article: A A Usoltsev et al 2016 IOP Conf. Ser.:
More informationCrystallization, microstructure and mechanical properties of silumins with micro-additions of Cr, Mo, W and V
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (897-330) Volume 0 Issue /200 23 36 23/ Crystallization,
More informationInfluence of compound deoxidation of steel with Al, Zr, rare earth metals, and Ti on properties of heavy castings
ARCHIVES of FOUNDRY ENGINEERING Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 12 Issue 1/2012 99 104 19/1 Influence of compound deoxidation
More informationPREDICTION OF CASTING AND SOLIDIFICATION OF SLAB STEEL INGOT
PREDICTION OF CASTING AND SOLIDIFICATION OF SLAB STEEL INGOT TKADLEČKOVÁ Markéta 1, MICHALEK Karel 1, MACHOVČÁK Pavel 2 1 VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering,
More informationMATHEMATICAL SIMULATION OF THE PROCESS OF ROLLING IN THE BACK TAPER ROLLS. Eldar AZBANBAYEV, Aristotel ISAGULOV, Zhasulan ASHKEYEV
MATHEMATICAL SIMULATION OF THE PROCESS OF ROLLING IN THE BACK TAPER ROLLS Eldar AZBANBAYEV, Aristotel ISAGULOV, Zhasulan ASHKEYEV Karaganda State Technical University, Karaganda, Kazakhstan, eldarazbanbayev@yandex.kz,
More informationTHE EFFECT OF Ti ON HIGH-ZINC Al CAST ALLOYS STRUCTURE AND PROPERTIES
Acta Metallurgica Slovaca, Vol. 17, 2011, No.2, p. 123-128 123 THE EFFECT OF Ti ON HIGH-ZINC Al CAST ALLOYS STRUCTURE AND PROPERTIES W. K. Krajewski, K. Haberl AGH University of Science and Technology,
More informationRecrystallization Theoretical & Practical Aspects
Theoretical & Practical Aspects 27-301, Microstructure & Properties I Fall 2006 Supplemental Lecture A.D. Rollett, M. De Graef Materials Science & Engineering Carnegie Mellon University 1 Objectives The
More informationEFFECTS OF Sr AND B INTERACTIONS IN HYPOEUTECTIC Al-Si FOUNDRY ALLOYS
Light Metals 6 Edited by Travis J. Galloway TMS (The Minerals, Metals & Materials Society), 6 EFFECTS OF Sr AND B INTERACTIONS IN HYPOEUTECTIC Al-Si FOUNDRY ALLOYS Liming Lu, Arne K Dahle CSIRO Minerals,
More informationInternational Conference on Material Science and Application (ICMSA 2015)
International Conference on Material Science and Application (ICMSA 2015) Effect of Magnesium Addition on the Inclusions Composition in the Cast Microstructure of HSLA Steel Yan LIU 1, a,*, Kai WANG 2,
More informationEffect of Cooling Rate and Pouring Temperature on the Hardness and Wear Resistance of Bronze SAE660
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 18 Issue 3/2018 144 151 25/3
More informationStudy on rheo-diecasting process of 7075R alloys by SA-EMS melt homogenized treatment
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS Study on rheo-diecasting process of 7075R alloys by SA-EMS melt homogenized treatment Recent citations - Wear analysis of A356
More informationEffects of Electromagnetic Vibrations on Glass-Forming Ability in Fe-Co-B-Si-Nb Bulk Metallic Glasses
Materials Transactions, Vol. 47, No. 5 (2006) pp. 1360 to 1364 #2006 The Japan Institute of Metals Effects of Electromagnetic Vibrations on Glass-Forming Ability in Fe-Co-B-Si-Nb Bulk Metallic Glasses
More informationEffect of Electromagnetic Vibrations on Fe-Co-B-Si-Nb Bulk Metallic Glasses
Materials Transactions, Vol. 48, No. 1 (2007) pp. 53 to 57 #2007 The Japan Institute of Metals Effect of Electromagnetic Vibrations on Fe-Co-B-Si-Nb Bulk Metallic Glasses Takuya Tamura*, Daisuke Kamikihara,
More informationDevelopment of Al-TiC Alloys Using Powder Metallurgy as Grain Refiners for Aluminium and Its Alloys
Abdel-Nasser.M. Omran Int. Journal of Engineering Research and Applications RESEARCH ARTICLE OPEN ACCESS Development of Al-TiC Alloys Using Powder Metallurgy as Grain Refiners for Aluminium and Its Alloys
More information2.1 Fundamentals of Nucleation
2. LITERATURE REVIEW 2.1 Fundamentals of Nucleation Nucleation can be defined as the formation of a new phase in a distinct region, separated from the surroundings by a definite boundary. When a liquid
More informationCHAPTER 3 SELECTION AND PROCESSING OF THE SPECIMEN MATERIAL
54 CHAPTER 3 SELECTION AND PROCESSING OF THE SPECIMEN MATERIAL 3.1 HIGH STRENGTH ALUMINIUM ALLOY In the proposed work, 7075 Al alloy (high strength) has been identified, as a material for the studies on
More informationFundamentals of Casting
Fundamentals of Casting Chapter 11 11.1 Introduction Products go through a series of processes before they are produced Design Material selection Process selection Manufacture Inspection and evaluation
More informationSTRUCTURE AND PROPERTIES OF ALUMINUM ALLOYS WITH ADDITIONS OF TRANSITION METALS PRODUCED VIA COUPLED RAPID SOLIDIFICATION AND HOT EXTRUSION
STRUCTURE AND PROPERTIES OF ALUMINUM ALLOYS WITH ADDITIONS OF TRANSITION METALS PRODUCED VIA COUPLED RAPID SOLIDIFICATION AND HOT EXTRUSION KULA Anna 1, BLAZ Ludwik 1 1 AGH University of Science and Technology,
More informationPROPERTIES OF AL-BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMISATION AND HOT EXTRUSION. Filip PRŮŠA, Dalibor VOJTĚCH
PROPERTIES OF AL-BASED ALLOYS PREPARED BY CENTRIFUGAL ATOMISATION AND HOT EXTRUSION Filip PRŮŠA, Dalibor VOJTĚCH Institute of Chemical Technology Prague, Department of Metals and Corrosion Engineering,
More informationSpecification Aluminium Die-Casting Alloy, high silicon content Aluminium Die-Casting Alloy, high silicon content
Specification 2012-10 Class: Aluminium and Al-alloys Class No.:21 Aluminium Die-Casting Alloy, high silicon content JED 853 Previous Edition Part name (for databases) 2011-11 Aluminium Die-Casting Alloy,
More informationHigh Speed Twin-Roll Casting of Aluminum Alloys
Proceedings of the 9 th International Conference on Aluminium Alloys (2004) Edited by J.F. Nie, A.J. Morton and B.C. Muddle Institute of Materials Engineering Australasia Ltd 718 High Speed Twin-Roll Casting
More informationSiC/Aluminum Composites Fabricated by in situ Processing using Reactive Infiltration Aid
Proceedings of the 12th International Conference on Aluminium Alloys, September 5-9, 2010, Yokohama, Japan 2010 2010 The Japan Institute of Light Metals pp. 1886-1890 1886 /Aluminum Composites Fabricated
More informationIndex Terms Solidification, Zinc-base alloys, thermal parameters, columnar-to-equiaxed transition. Fig. 1: Schematic of experimental setup.
Unidirectional Solidified Zn-Al-Si-Cu Alloys: Columnar-to-Equiaxed Transition (CET) Alicia Esther Ares Faculty of Sciences (FCEQyN) - National University of Misiones (UNaM). Posadas-Misiones. Researcher
More informationGrain Morphology of As-Cast Wrought Aluminium Alloys
Proceedings of the 12th International Conference on Aluminium Alloys, September 5-9, 2010, Yokohama, Japan 2010 2010 The Japan Institute of Light Metals pp. 173-178 173 Grain Morphology of As-Cast Wrought
More information(c) by Trans Tech Publica
NAOSITE: Nagasaki University's Ac Title Solid free-form fabrication of meta Author(s) Kagawa, Akio; Mizumoto, Masayuki; O Citation Advanced Materials Research15-17, p Issue Date 2009-01-21T02:57:23Z URL
More informationTechnical Note Ref: MH002/01 March 2005
Contents > Abstract > Techniques > Introduction > Method > Results and Discussion > Conclusions Root Cause Analysis of Hot Tearing Using the MetalHealth System Abstract This technical note discusses the
More informationStrontium As a Structure Modifier for Non-binary Al Si Alloy
Strontium As a Structure Modifier for Non-binary Al Si Alloy Barbora Bryksí Stunová 1 1 CTU in Prague, Faculty of Mechanical Engineering, Department of Manufacturing Technology, Technická 4, 166 07 Prague,
More informationThe Treatment of Liquid Aluminium-Silicon Alloys. Topics to discuss
MME 6203; Lecture 15 The Treatment of Liquid Aluminium-Silicon Alloys 3. Modification in Hypereutectic Alloys and Grain Refining AKMB Rashid Department of MME BUET, Dhaka Topics to discuss 1. Refinement
More informationMECHANICAL PROPERTIES OF AlSi12 ALLOY WITH ALUMINIUM BRONZE
ENGINEERING FOR RURAL DEVELOPMENT Jelgava, 4.-6.05.07. MECHANICAL PROPERTIES OF AlSi ALLOY WITH ALUMINIUM BRONZE Tomasz Lipinski University of Warmia and Mazury in Olsztyn, Poland tomaszlipinski.tl@gmail.com
More informationInternational Conference on Material Science and Application (ICMSA 2015)
International Conference on Material Science and Application (ICMSA 2015) Influence of Er on Microstructure and Properties of Al-0.2%Zr-0.06%B Heat-resistant Alloy Conductor Prepared by Continuous ECAE
More informationInfluences of Silicon on Properties of Hard Drawn Aluminium Wire
Influences of Silicon on Properties of Hard Drawn Aluminium Wire XueXia XU 1, a*, YanTing FENG 1,b, DongYu LIU 2,3,c, Yong WANG 1,d, WenBin LI 1,e, KangHua YAN 2,f and BaoRang LI 2,3,g 1 State Grid Hebei
More informationMetals, Refining Processes and Materials Recycling, 17. listopadu 15/2172, Ostrava - Poruba, Czech Republic,
MECHANICAL CHARACTERISTICS OF Ni 3 Al BASED ALLOYS WITH STOICHIOMETRIC AND HYPO-STOICHIOMETRIC COMPOSITION Jitka MALCHARCZIKOVÁ a, Miroslav KURSA b a VŠB-TU Ostrava, Faculty of Metallurgy and Materials
More informationHigh speed steels are widely used in making highspeed
Solidification microstructure of M2 high speed steel by different casting technologies *Zhou Xuefeng, Fang Feng and Jiang Jianjing (Jiangsu Key Laboratory of Advanced Metallic Materials, Southeast University,
More informationCONVENTIONAL AND SEMI-SOLID A356 ALLOY WITH ADDITION OF STRONTIUM
CONVENTIONAL AND SEMI-SOLID A356 ALLOY WITH ADDITION OF STRONTIUM Y.S.Seo, L.M.M.Nasir, H.Zuhailawati, A.S.Anasyida * Structural Materials Niche Area, School of Materials & Mineral Resources Engineering,
More informationThe Effect of Rotation Stirring on Macrosegregation in Bi-Sn Alloy
The Effect of Rotation Stirring on Macrosegregation in Bi-Sn Alloy Yeni Muriani Zulaida 1*, Riyan Afrizal 1 and Suryana Suryana 1 1 Metallurgical Department Faculty of Engineering, Sultan Ageng Tirtayasa
More informationGrain Refinement for Improved Lead-Free Solder Joint Reliability
Grain Refinement for Improved Lead-Free Solder Joint Reliability K. Sweatman 1, S. D. McDonald 2, M. Whitewick 2, T. Nishimura 1, and K. Nogita 2 1. Nihon Superior Co., Ltd, Osaka, Japan 2. University
More informationTransmission electron microscope studies of the chromium cast iron modified at use of B 4 C addition
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 10 Issue 4/2010 209 216 39/4
More informationSemi-solid casting of pure magnesium
Semi-solid casting of pure magnesium CURLE Ulyate A. a* and WILKINS Jeremias D. b Light Metals, Materials Science and Manufacturing, Council for Scientific and Industrial Research Pretoria, South Africa
More informationOriginal. DOI: /
Original Elsayed, F.R.; Hort, N.; Salgado-Ordorica, M.; Kainer, K.U.: Magnesium Permanent Mold Castings Optimization Materials Science Forum, Light Metals Technology V (2011) Trans Tech Publications DOI:
More information[ICAMS: March 2017] ISSN: IMPACT FACTOR Keywords: Magnetic molding, lost foam process, Mechanical properties, Aluminum alloy
INNOVATIVE CASTING USING MAGNETIC MATERIALS Basavarajappa V N *1, H B Niranjan 2 & Manjunatha A R 3 *1 Assistant Professor, Department of Mechanical Engineering, Sambhram Institute of Technology, Bangalore,
More informationA PROMISING PREPARATION METHOD FOR AL/7075-B4C/AL LAYERED COMPOSITE BY CONTINUOUS CASTING AND HOT ROLLING
A PROMISING PREPARATION METHOD FOR AL/7075-B4C/AL LAYERED COMPOSITE BY CONTINUOUS CASTING AND HOT ROLLING Yubo Zhang*,Yingshui Yu, Tingju Li Key Laboratory of Solidification Control and Digital Preparation
More informationMSE-226 Engineering Materials
MSE-226 Engineering Materials Lecture-7 ALLOY STEELS Tool Steels TYPES of FERROUS ALLOYS FERROUS ALLOYS Plain Carbon Steels Alloy Steels Cast Irons - Low carbon Steel - Medium carbon steel - High carbon
More informationSharif University of Technology, Material Science and Engineering Department Tehran, Iran.
Microstructural Investigation of Semisolid Aluminum A356 Alloy Prepared by the Combination of Electromagnetic Stirring and Gas Induction Nora Nafari 1,a, Farnoush Yekani 1,b, Hossein Aashuri 1,c* 1 Sharif
More informationMODELING AND DEVELOPMENT OF A FORGING INGOT OF RATIONAL DESIGN AND MASS. Aleksandr N. Rogotovsky, Alexey A. Shipelnikov, Natalya A.
Journal Journal of Chemical of Chemical Technology Technology and Metallurgy, and Metallurgy, 53, 5, 53, 2018, 5, 2018 936-942 MODELING AND DEVELOPMENT OF A FORGING INGOT OF RATIONAL DESIGN AND MASS Aleksandr
More informationThe effect of structure on the cavitational wear of FeAl intermetallic phase-based alloys with cubic lattice
ARCHIVES Of FOUNDRY ENGINEERING Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (97-33) Volume 11 Special Issue /11 97 19/ The effect of structure on the
More informationApplication of computed tomography for an analysis of composite with fine dispersive reinforcement made of the Fe 65 Co 10 Ni 3 W 2 B 20 alloy
Volume 83 Issue 1 January 2017 Pages 17-22 International Scientific Journal published monthly by the World Academy of Materials and Manufacturing Engineering Application of computed tomography for an analysis
More informationAL LM6 HOLLOW CYLINDER FABRICATED USING CENTRIFUGAL CASTING
AL LM6 HOLLOW CYLINDER FABRICATED USING CENTRIFUGAL CASTING Saifulnizan Jamian 1, Safwan Yutiman 2 and Haffidzudin Hehsan 3 1 Crashworthiness and Collisions Research Group, Universiti Tun Hussein Onn Malaysia,
More informationPrediction of mechanical properties of Al alloys with change of cooling rate
November 2012 Overseas Foundry Prediction of mechanical properties of Al alloys with change of cooling rate Quan-Zhi Dong 1, Young-Sim Choi 2, Jun-Ho Hong 2 and *Ho-Young Hwang 2 (1. Dept. of Virtual Engineering,
More informationTemperature dependent measurement of internal damping of austenitic stainless steels
Temperature dependent measurement of internal damping of austenitic stainless steels Monika Oravcová 1,*, Peter Palček 1, Mária Chalupová 1, Milan Uhríčik 1 1 Department of Materials Engineering, Faculty
More information