Mechanical and Damping Properties of Silicon Bronze Alloys for Music Applications
|
|
- Bennett Joseph
- 6 years ago
- Views:
Transcription
1 International Journal of Engineering & Technology IJET-IJENS Vol: 11 No: Mechanical and Damping Properties of Silicon Bronze Alloys for Music Applications I Ketut Gede Sugita, R. Soekrisno, I Made Miasa, Suyitno Mechanical and Industrial Engineering Department, Gadjah Mada University, Jl. Grafika no 2, 5528 Yogyakarta, Indonesia. sgita_03@yahoo.com Abstract-- An alloy for musical instruments should have high enough strength, hardness, specific elastic properties and low damping capacity. The high tin bronze alloys with composition wt.% Sn has good acoustical properties, which is capable of producing long-lasting slowly damping vibrations but there is brittle materials. Cracks and fracture may appear on these materials. The study on mechanical and acoustic characteristic becomes the primary consideration in determining the new material as a musical instrument. The aim of this study is to investigate the effect of silicon fraction of Cu-( ) wt. % Si on mechanical and acoustical properties of bronze alloys for music instruments. As-cast Cu- ( ) wt. % Si were cut from 250 x 55 x 15 mm of billet and manufactured for tensile, hardness, impact, and damping test specimen. Simply supported beam model was used for measuring damping capacity. Mechanical and damping properties of silicon bronze (Cu-Si) were studied. Investigation of bronze 20 wt. % Sn alloys was conducted as comparison. The results show that the mechanical properties and damping capacity of Cu-xSi is higher than Cu-20 wt. % Sn bronze alloys. The ductility and impact strength of silicon bronze also higher than this of tin Cu-20 wt.% Sn. It is recommended that Cu (5-7.5) wt. % Si are suitable to substitute tin bronze (Cu-20 wt.% Sn) for music instrument applications. I. INTRODUCTION Tin bronze alloys are one of the importance materials in industry for a long time, because of their good properties such as; high strength, thermal conductivity, machine ability, corrosion resistance and wear resistance [1]. It has a good formability. Its crystal structure is hexagonal closed packed (HCP), which is quite easy to shape in hot conditions [2] The high tin bronze alloys with composition wt.% Sn has good acoustical properties, which is capable of producing long-lasting slowly damping vibrations [3-5]. It is commonly used for music materials such as bell, or Javanese and Balinese gamelan. This is a double phase alloy containing brittle particles of Cu 31 Sn 8 intermetallic (δphase), so that it becomes harder, more brittle than brass [6-7]. Also, tin bronze at low suffer from climate factor. It has a low frost resistance at temperature t = ( (20-25 o C), the metal becomes brittle and cracks may appear. Likewise, the sound that is produced becomes poor and short (5-6). The brittleness of bronze is a very important concern because cracked or broken often found in bell as well as gamelan as shown in Figure 1. Index Term-- Tin bronze, silicon bronze, mechanical properties and damping capacity crack Fig. 1. Crack on Balinese Gong Tin as the main alloying tin bronze have a great price and scarred element [3, 5], so that the resulting product becomes too expensive. Research on the weakness prevention efforts of high tin bronze and bronze acoustic as musical material has limited information The investigations of new materials need to be done to overcome the weaknesses of tin bronze. This research was carried out to investigate the mechanical properties and damping capacity of silicon bronze for music instruments. It is feasible to produce new alloys that have good mechanical properties, good acoustic and lower-priced, that is expected to as substitute for tin bronze
2 International Journal of Engineering & Technology IJET-IJENS Vol: 11 No: EXPERIMENTAL DETAILS 2.1. Materials and process Bronze alloys TABLE I CHEMICAL COMPOSITION OF ALLOYS Content of elements wt% Cu Sn Si Pb Zn Mn S As Cu-20%Sn Cu-2.5%Si Cu-5%Si Cu-5%Si The studied bronze alloys in this research were Cu- ( ) wt. %Si and Cu-20 wt. % Sn. Investigation of Cu- 20%Sn bronze alloy was conducted as comparison Table 1 shows the composition of the alloys. The commercial pure copper (99.99 wt. %) and commercial pure silicon (99.99 wt. %) were melted in crucible furnace at temperature of 1100 o C. The molten metal was poured into the preheated permanent mold at 200 o C, 300 o C, and 400 o C. Tensile test specimens were cut from as-cast materials 250 x 55 x 15 mm. They were made based on JIS Z2201. No.7 standard. Tensile test are conducted on Universal testing machine with a digital 20 KN capacity. Hardness test was carried out on Vickers type hardness-test. The notched specimens were used for impact toughness measurement, using a Charpy hammer impact testing machine. damping capacity measurement refers to the standard ASTM E , it can be shown in Fig. 2. The logarithmic decrement method is used to calculate damping capacity. The logarithmic decrement δ, derived from the amplitude decay of specimen under free vibration, is given by [8]. 1 n ln Ai A Where A i and A i+n are the amplitudes of the i th cycle and the (i + n) th cycle, by n periods of oscillation. For the case of relatively small damping capacity, the relationship between δ and ζ is simple and it is given by [8]. in 2.2. Damping test ( ) The damping capacity was determined under simply supported free vibration bending model. The set up of 2.3 Microstructure observation The specimens for the metallographic investigation were prepared by cutting, mounting, grinding and polishing of the small (30 mm diameter, 15 mm long) specimens. Having cut them off, they were polished using silicon carbide abrasive paper of: 240, 400, 600, 800, 1000, 2000, grits, respectively, and then were polished perfectly using diamond pasta and etched using 10% HNO3+90% alcohol. These procedures were applied in accordance with standard metallographic techniques 3. RESULTS 3.1 Mechanical Properties The solidification rate was influenced by variations in the temperature gradient between the molten metal with the mold temperature. The greater the temperature difference between liquid metal with the mold temperature, Fig. 2. Set up of damping measurement the solidification rate will increase by lowering the solidification time. The solidification time and heat transfer affect the morphology of microstructure forms, such as grain size and dendrite arm spacing. The effect of silicon contents on mechanical properties such as the tensile strength, hardness, and impact strength of bronze silicon on the variation of mold temperature shows in Fig. 3-5 respectively. It can be seen from Fig. 2, that the ultimate tensile strength (UTS) increase on addition of 2.5% wt Si and 5% wt silicon, but there is a decrease on addition of 7.5% wt. Si. Also, the raising the molds temperature (200 o C to 400 o C) decreasing tensile strength. It indicated that the higher mould temperature on casting process, the lower the tensile strength in which the highest ultimate strength was MPa at the temperature of 200 o C. Meanwhile the lowest ultimate strength was about MPa at the temperature of 400 o C.
3 International Journal of Engineering & Technology IJET-IJENS Vol: 11 No: Fig. 3 Tensile strength of tensile strength Fig 4 shows that the hardness of bronze increased along with the increase of the silicon percentage within the alloys. Besides, it was also affected by the variation of mold temperature. The lower of the mold temperature, the harder the bronze gained. The highest hardness materials were obtained from cast in mold temperature of 200 o C, 300 o C, and then 400 o C. In contrast, the impact strength decreased by the increase of silicon within the alloy. The strength impact as the result of the casting increased along with the temperature. It can be best shown in Fig 5. Fig. 5. Impact strength of bronze alloys 3.2 Damping Capacity The damping capacity of materials (internal damping) is the measure of a material s ability to dissipate elastic energy during mechanical vibration or wave propagation. Internal damping of materials is characterized by the energy dissipation associated with microstructure defect, such as grain boundaries, thermo elastic effect, dislocation motion in metals, and non uniform stresses. Fig. 5 shows the effect of wt % Si on the damping capacity of silicon bronze alloys. The damping capacity of materials decreased along with the increase of Si content. On the other hand, the increase of the mold temperature on casting resulted in the decrease of damping capacity. Figure 5 also shows that the damping capacity of 20 wt. % Sn tin bronze is relatively lower compared with 5 wt. % Si bronze alloy. It means that when the blades are made of tin bronze is vibrated; the blades will vibrate longer than the blades are made from silicon bronze. Fig. 4. Hardness strength of bronze alloys Fig. 6. Damping capacity of bronze alloys
4 3.3 Microstructure Examination International Journal of Engineering & Technology IJET-IJENS Vol: 11 No: a b Figs. 7a-c show that the microstructures of tin bronze 20 wt %. Sn and silicon bronze by containing varied of silicon content i.e.; 2.5 wt.% Si, 5 wt.% Si, and 7.5 wt.% Si, respectively. The microstructure of as-cast silicon bronze containing 2.5% Si is the largest structure of Cu primary α- phase. Only α phase was formed in this alloy. On the other hand, microstructure of silicon bronze containing 5 wt % Si is dendrite structures. The dendrite structural of silicon bronze 7.5 wt. % Si was finer than dendrite structure of silicon bronze 5 wt. % Si. (Fig.7c and d). The changes in the microstructures are associated with the addition of wt% Si. 4. DISCUSSIONS Mechanical properties and damping capacity are influenced by the variation of silicon composition in alloys and solidification process. The raising mold temperature affected the solidification process and increased the solidification time. High gradient temperature on liquid cooling region was affected by different temperature between pouring temperature and the mold temperature. When the thermal gradient between the mold and the molten metal is high, the cooling rate increases and solidification time decreases. The solidification rate affects the microstructure forms, such as grain size and dendrite arm spacing [10-13]. The microstructure that results from solidification directly affects on the mechanical properties of alloys [12, 13]. The ultimate strength (UTS) and hardness c d Fig. 7 Microstructure of bronze alloys a) Tin bronze 20 wt.% Sn, b) Silicon bronze 2.5 wt.% Si, c) Silicon bronze 5 wt.% Si, d) Silicon bronze 7.5 wt.% Si strength (VHN) increases as the solidification rate increases but impact strength decreases. In the metals and alloys, internal damping results from mechanical-energy dissipation within the material due to various microscopic and macroscopic processes. Material damping is extremely sensitive to the presence of defects. The defects in metals and alloys include point defects, dislocation, surface defect and bulk defect. point defects give rise to damping in the range of low to intermediate levels, line defects give rise to damping levels in the intermediate to high range, and surface defects give rise to damping levels in the high range [16]. The addition of silicon alloy produced finer dendrite structure, hence increases in the amount of grain boundaries. The greater grain boundary surface area more effectively block or movement of dislocation and the strength increased. The microstructure of the silicon bronze 7.5%wt Si consists of coarse δ phase in the microstructure. The area of grain boundary is small, so the damping capacity is low. 5. CONCLUSION The mechanical and damping properties of silicon bronze with the variation of wt% Si content were evaluated and compared with high tin bronze 20% Sn. It was found out that the variation content of Si and solidification rate affected the mechanical properties and damping capacity. The ultimate tensile strength (UTS) and hardness of material
5 International Journal of Engineering & Technology IJET-IJENS Vol: 11 No: increase as cooling rate increases but impact strength and damping capacity decreases. The properties of silicon bronze with containing 5% wt Si and 7% wt Si showed better mechanical properties and high ductility, when it is compared with high tin bronze. The damping capacity of silicon bronze is relatively the same with high tin bronze 20% Sn, therefore, it is suitable to substitute high tin bronze especially for music instrument applications. REFERENCES [1] Schmidt, R.F., Schmidt D.G., Selection and Application of Copper Alloy Castings, ASM Handbook, Metals Handbook, vol. 2, pp. 346, [2] Callister, W., Fundamental of Materials Science and Engineering. John Wiley and Son Inc. p. 179, [3] Gupta, R.B., Materials Science, Tech India Publication, p.239, [4] Hosford, F. W., Mechanical Behaviour of Materials, Cambridge University Press, [5] Lisovskii, V.A., Lisovskaya, O.B., Kochetkova, L.P, Favstov, Y..K., Sparingly Alloyed Bell Bronze with Elevated Parameters of Mechanical Properties Journal Metal Science and Heat treatment, vol. 49, , [6] Jang-Sik, P., Robert, B., Gordon, Traditions and Transitions in Korean Bronze Technology, Journal of Archaeological Science, pp. 1-12, [7] Favstov, Y. K., Zhravel, L.V., Kochetkova, L.P., Structure and Damping Capacity of Br022 Bell Bronze, Journal Metal science and Heat treatment, vol.45, pp , [8] De Silva, C., Vibration Fundamental and Practice, Boca Raton London, CRC Press, [9] ASTM, E , Standard Test Method for Dynamic Young, Shear Modulus, and Poisson s Ratio, by Impulse Excitation of vibration, ASTM International, [10] Campbell, J., The New Metallurgy of Cast Metals, Second Edition, Butterworth Heinemann, [11] Stefanescu, D.M., Science and Engineering of Casting Solidification, Kluwer Academic/Plenum Publisher, [12] Hemanth, J., Effect of cooling rate on dendrite arm spacing (DAS),eutectic cell count (ECC) and ultimate tensile strength (UTS) of austempered chilled ductile iron, Materials and Design 21, pp. 1-8, [13] Talamantes-Silva, M.A., Rodri, G, A. Talamantes-Silva, J.S., Valtierra, S., and Cola, L., Effect of Solidification Rate and Heat Treating on the Microstructure and Tensile Behavior of an Aluminum-Copper Alloy, The Minerals, Metals & Materials Society and ASM International, [14] Huang, S.K., Lia, N., Wen, Y.H., Tenga, Y.G., Xub S. Ding, Temperature Dependence of The Damping Capacity in Fe 19.35Mn Alloy, Journal of Alloys and Compounds vol.455,pp , [15] Zhang, L,Y, Jiang, Y,H, Ma, Z, Shan, S.F., Jia, Y.Z., Fan, C.Z, Wang, W.K., Microstructural evolution of the supersaturated ZA27 alloy and its damping capacities, Journal of Materials Processing Technology, vol. 207, pp , 2008.
The Effect of Annealing Temperature on Damping Capacity of the Bronze 20%Sn Alloy
International Journal of Mechanical & Mechatronics Engineering IJMME-IJENS Vol: 11 No: 04 1 The Effect of Annealing Temperature on Damping Capacity of the Bronze 20%Sn Alloy I Ketut Gede Sugita, R. Soekrisno,
More informationEffect of Nickel and Iron Addition on the Structure and Mechanical Properties of Tin Bronze (Cu-10wt%Sn)
American Journal of Engineering, Technology and Society 2017; 4(6): 110-118 http://www.openscienceonline.com/journal/ajets ISSN: 2381-6171 (Print); ISSN: 2381-618X (Online) Effect of Nickel and Iron Addition
More informationEFFECT OF HEAT TREATMENT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF 6061 ALUMINUM ALLOY
Effect of Heat Treatment on Microstructure and Mechanical Properties of 6061 Aluminum Alloy EFFECT OF HEAT TREATMENT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF 6061 ALUMINUM ALLOY J. Ridhwan 1*, J.
More informationOPTIMIZATION OF PROPERTIES AND STRUCTURE WITH ADDITION OF TITANIUM IN HADFIELD STEELS Mohammad Bagher Limooei (1), Shabnam Hosseini (1)
Abstract OPTIMIZATION OF PROPERTIES AND STRUCTURE WITH ADDITION OF TITANIUM IN HADFIELD STEELS Mohammad Bagher Limooei (1), Shabnam Hosseini (1) 1- Islamic Azad University, Ayatollah Amoli Branch sh_hosseini@yahoo.com,
More informationInternational Journal of Scientific & Engineering Research, Volume 4, Issue 6, June-2013 ISSN
1497 Behaviour of Aluminium Alloy Casting with the variation of Pouring Temperature and Permeability of Sand 1 Mahipal Singh, 2Manjinder Bajwa, 3Rohit Sharma, 4Hitesh Arora Abstract: The effect of pouring
More informationInternational Journal of Scientific & Engineering Research Volume 3, Issue 7, July ISSN
International Journal Scientific & Engineering Research Volume 3, Issue 7, July-01 1 EFFECT OF MAGNESIUM ENHANCEMENT ON MECHANICAL PROPERTY AND WEAR BEHAVIOUR OF LM6 ALUMINUM ALLOY R. S. Rana and Rajesh
More informationEFFECT OF PERCENTAGE REINFORCEMENT OF B4C ON THE TENSILE PROPERTY OF ALUMINIUM MATRIX COMPOSITES
Int. J. Mech. Eng. & Rob. Res. 2012 Gopal Krishna U B et al., 2012 Research Paper ISSN 2278 0149 www.ijmerr.com Vol. 1, No. 3, October 2012 2012 IJMERR. All Rights Reserved EFFECT OF PERCENTAGE REINFORCEMENT
More informationEFFECT OF SOLUTION TREATMENT TEMPERATURE ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A356 ALLOY
International Conference on Mechanical Engineering Research (ICMER2013), 1-3 July 2013 Bukit Gambang Resort City, Kuantan, Pahang, Malaysia Organized by Faculty of Mechanical Engineering, Universiti Malaysia
More informationApplication of aluminum alloy castings in aerospace
February 2010 Research & Development Effect of returns on microstructure and mechanical properties of Al-Cu based alloys *Li Min, Wang Hongwei, Wei Zunjie, Zhu Zhaojun (School of Materials Science and
More informationME -215 ENGINEERING MATERIALS AND PROCESES
ME -215 ENGINEERING MATERIALS AND PROCESES Instructor: Office: MEC325, Tel.: 973-642-7455 E-mail: samardzi@njit.edu PROPERTIES OF MATERIALS Chapter 3 Materials Properties STRUCTURE PERFORMANCE PROCESSING
More informationA Study on Mechanical Properties of Aluminium LM25- Si c Composites Fabricated Using Stir Casting Technique
A Study on Mechanical Properties of Aluminium LM25- Si c Composites Fabricated Using Stir Casting Technique.Satyanarayen 1, Dominic Roystan 2, M.Shreesaravanan 3 Balaguru 4, C.Devanathan 5 1,2,3,4 UG Students,
More informationEffect of melt treatment on microstructure and impact properties of Al 7Si and Al 7Si 2 5Cu cast alloys
Bull. Mater. Sci., Vol. 30, No. 5, October 2007, pp. 439 445. Indian Academy of Sciences. Effect of melt treatment on microstructure and impact properties of Al 7Si and Al 7Si 2 5Cu cast alloys K G BASAVAKUMAR*,
More informationStructural Modification of Aluminium-Manganese-Silicon Alloy with Sodium Fluoride
International Journal of Engineering Science Invention ISSN (Online): 2319 6734, ISSN (Print): 2319 6726 Volume 3 Issue 4 ǁ April 2014 ǁ PP.25-30 Structural Modification of Aluminium-Manganese-Silicon
More informationHot Cracking Susceptibility in the TIG Joint of AZ31 Mg-Alloy Plates Produced by the TRC Process with and without Intensive Melt Shearing
Materials Science Forum Vol. 765 (2013) pp 756-760 (2013) Trans Tech Publications, Switzerland doi:10.4028/www.scientific.net/msf.765.756 Hot Cracking Susceptibility in the TIG Joint of AZ31 Mg-Alloy Plates
More informationA Study on Semi Solid Squeeze Forging of High Strength Brass. K.H. Choe*, G.S.Cho*, K.W. Lee*, Y.J. Choi**, K.Y. Kim*** and M.H.
A Study on Semi Solid Squeeze Forging of High Strength Brass K.H. Choe*, G.S.Cho*, K.W. Lee*, Y.J. Choi**, K.Y. Kim*** and M.H. Kim**** *Advanced Material R/D Center, KITECH, 994-32 Dongchun-dong, Yeonsu-gu,
More informationEffect of Cooling Rate and Pouring Temperature on the Hardness and Wear Resistance of Bronze SAE660
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 18 Issue 3/2018 144 151 25/3
More informationThe Effect of La Addition on the Microstructure and Tensile Properties of Hot-Extruded Al 15%Mg 2 Si Composite
The Effect of La Addition on the Microstructure and Tensile Properties of Hot-Extruded Al 15%Mg 2 Si Composite Paper Presenter: S.H. Allameh 1 A. Akhlaghi 2, M. Noghani 3, M. Emamy 4. 1,4- School of Metallurgy
More informationMECHANICAL PROPERTIES OF ALUMINIUM 6063 ALLOY BASED GRAPHITE PARTICLES REINFORCED METAL MATRIX COMPOSITE MATERIAL
MECHANICAL PROPERTIES OF ALUMINIUM 6063 ALLOY BASED GRAPHITE PARTICLES REINFORCED METAL MATRIX COMPOSITE MATERIAL 1 Sandeep kansari, 2 Ashutosh dwivedi 1 Student of M.tech, 2 professor 1,2 Department of
More informationMechanical Properties of Metals. Goals of this unit
Mechanical Properties of Metals Instructor: Joshua U. Otaigbe Iowa State University Goals of this unit Quick survey of important metal systems Detailed coverage of basic mechanical properties, especially
More informationWrought Aluminum I - Metallurgy
Wrought Aluminum I - Metallurgy Northbrook, IL www.imetllc.com Copyright 2015 Industrial Metallurgists, LLC Course learning objectives Explain the composition and strength differences between the alloy
More informationEffect of Processes Parameter on Mechanical Properties in Aa2218-Fe2o3 MMCS Processed by Stir Casting
Effect of Processes Parameter on Mechanical Properties in Aa2218-Fe2o3 MMCS Processed by Stir Casting Puneet Kumar Assistant Professor Department of Mechanical Engineering MIT Moradabad Moradabad, India
More informationEffect of Hardness on A413 intermetallic Alloy with the influence of typical heat treatment
IOSR Journal of Mechanical and Civil Engineering (IOSR-JMCE) e-issn: 2278-1684,p-ISSN: 2320-334X, Volume 14, Issue 4 Ver. V (Jul. - Aug. 2017), PP 18-23 www.iosrjournals.org Effect of Hardness on A413
More informationAnalysis of Mechanical and Metallurgical properties of Al-SiCp Composite by Squeeze-cum-Stir Casting
International Journal of Research in Engineering and Science (IJRES) ISSN (Online): 2320-9364, ISSN (Print): 2320-9356 Volume 2 Issue 5 ǁ May. 2014 ǁ PP.45-49 Analysis of Mechanical and Metallurgical properties
More informationTutorial 2 : Crystalline Solid, Solidification, Crystal Defect and Diffusion
Tutorial 1 : Introduction and Atomic Bonding 1. Explain the difference between ionic and metallic bonding between atoms in engineering materials. 2. Show that the atomic packing factor for Face Centred
More informationA STUDY OF CASTING CHARACTERISTICS FOR DIE-CAST ALUMINUM ALLOY
ME8109: Casting And Solidification of Material A STUDY OF CASTING CHARACTERISTICS FOR DIE-CAST ALUMINUM ALLOY Department of Mechanical & Industrial Engineering Graduate Program in Mechanical Engineering
More informationMATERIALS TECHNOLOGY LABORATORY DESIGN PARAMETERS FOR LEAD-FREE COPPER-BASE ENGINEERING ALLOYS IN PERMANENT MOLDS
MATERIALS TECHNOLOGY LABORATORY DESIGN PARAMETERS FOR LEAD-FREE COPPER-BASE ENGINEERING ALLOYS IN PERMANENT MOLDS F.A. Fasoyinu, D. Cousineau, R. Bouchard, M. Elboujdaini and M. Sahoo EXECUTIVE SUMMARY
More informationMaterial Characterization Analysis and Effects of Temperature on Microstructure with Respect to Their Mechanical Properties
Material Characterization Analysis and Effects of Temperature on Microstructure with Respect to Their Mechanical Properties Muhammad Bilal 1 * and Mohsin Ali Memon 2 1 Department Materials Engineering,
More informationChulalongkorn University, Bangkok, Thailand. Chulalongkorn University, Bangkok, Thailand; Abstract
Journal of Metals, Materials and Minerals. Vol.16 No.2 pp.25-31, 2006 The Effect of Long-Term Thermal Exposure at Elevated Temperatures on Microstructures and Mechanical Properties in Centrifugally Casted
More informationStudy of Dispersoid Content and Chill Effect for Improved Mechanical Properties of Aluminum-Garnet-Carbon Hybrid Metal Matrix Composites
Study of Dispersoid Content and Chill Effect for Improved Mechanical Properties of Aluminum-Garnet-Carbon Hybrid Metal Matrix Composites Nityanand Bandekar V.T.U. Belgaum S.D.M. Institute of Technology
More informationThe Microstructure and Mechanical Properties of Inconel 718 Fine Grain Ring Forging
The Microstructure and Mechanical Properties of Inconel 718 Fine Grain Ring Forging Zixing Wang 1, Dianhua Zhou 1, Qun Deng 2, Guosheng Chen 1, Wei Xie 1 1 Special Steel R & D Center of Special Steel Business
More informationA.S. Kiran 1, V. Desai 2, Narendranath 2 and P.G. Mukunda 1. R G g
International Journal of Mechanical and Materials Engineering (IJMME), Vol.6 (2011), No.2, 275-279 EVOLUTION OF MICROSTRUCTURE AND HARDNESS OF AL-SI FUNCTIONALLY GRADED MATERIAL CAST THROUGH CENTRIFUGE
More informationEvaluation of a New High Temperature Cast Aluminum for Cylinder Head Applications
2018 AFS Proceedings of the 122nd Metalcasting Congress, Fort Worth, Texas Paper 18-034 (7 pages) Page 1 Evaluation of a New High Temperature Cast Aluminum for Cylinder Head Applications Qigui Wang, Devin
More informationSteel Properties. History of Steel
History of Steel Steel Properties Cast Iron Cast iron preceded wrought iron. It is brittle, has high carbon content with low tensile strength. It has excellent casting properties. It was mainly used to
More informationArch. Metall. Mater. 62 (2017), 3,
Arch. Metall. Mater. 62 (2017), 3, 1615-1624 DOI: 10.1515/amm-2017-0247 M. UHRÍČIK* #, P. PALČEK*, M. CHALUPOVÁ*, M. ORAVCOVÁ*, M. FRKÁŇ* THE INFLUENCE OF THE STRUCTURE ON THE FATIGUE PROPERTIES OF Al-Mg
More informationEngineering Materials
Engineering Materials Lecture 2 MEL120: Manufacturing Practices 1 Selection of Material A particular material is selected is on the basis of following considerations 1. Properties of material 1. Properties
More informationCONVENTIONAL AND SEMI-SOLID A356 ALLOY WITH ADDITION OF STRONTIUM
CONVENTIONAL AND SEMI-SOLID A356 ALLOY WITH ADDITION OF STRONTIUM Y.S.Seo, L.M.M.Nasir, H.Zuhailawati, A.S.Anasyida * Structural Materials Niche Area, School of Materials & Mineral Resources Engineering,
More informationIssues to address. Why Mechanical Test?? Mechanical Properties. Why mechanical properties?
Mechanical Properties Why mechanical properties? Folsom Dam Gate Failure, July 1995 Need to design materials that can withstand applied load e.g. materials used in building bridges that can hold up automobiles,
More informationTHE EFFECTS OF CASTING PARAMETERS ON RESIDUAL STRESSES AND MICROSTRUCTURE VARIATIONS OF AN AL- SI CAST ALLOY
Copyright JCPDS-International Centre for Diffraction Data 29 ISSN 197-2 553 THE EFFECTS OF CASTING PARAMETERS ON RESIDUAL STRESSES AND MICROSTRUCTURE VARIATIONS OF AN AL- SI CAST ALLOY S. Mohsen Sadrossadat
More informationCOMPUTER SIMULATION AND EXPERIMENTAL RESEARCH OF CAST PISTON POROSITY
Tome V (year 2007), Fascicole 2, (ISSN 1584 2665) COMPUTER SIMULATION AND EXPERIMENTAL RESEARCH OF CAST PISTON POROSITY D. KAKAS, L. KOVACEVIC, P. TEREK UNIVERSITY OF NOVI SAD, FACULTY OF TECHNICAL SCIENCES,
More informationGlobal Journal of Engineering Science and Research Management
DIFFUSION BONDING OF AL ALLOY USING DIFFERENT IINTERLAYERS Assist. Prof. Dr. Ahmed A. Akbar*, Samer K. Khaleel * Asst. Prof. Dr. at University of Technology, Production Engineering and Metallurgy, Iraq
More informationTHE EFFECT OF CERIUM ADDITION ON THE MICROSTRUCTURE OF AlSiMgCe ALLOY. Anasyida Abu Seman and Abdul Razak Daud.
THE EFFECT OF CERIUM ADDITION ON THE MICROSTRUCTURE OF AlSiMgCe ALLOY Anasyida Abu Seman and Abdul Razak Daud. School of Applied Physics, Faculty of Science and Technology, University Kebangsaan Malaysia,
More informationFerrous Alloys. Metal Alloys. Ferrous. Non ferrous. Grey iron. Carbon Low Alloy High Alloy. Nodular iron White iron Malleable iron Alloy cast irons
Metal Alloys Most engineering metallic materials are alloys. Metals are alloyed to enhance their properties, such as strength, hardness or corrosion resistance, and to create new properties, such as shape
More informationG. K. Triantafyllidis, I. Kiligaridis, D. I. Zagkliveris, I. Orfanou, S. Spyridopoulou, E. Mitoudi-Vagourdi, S. Semertzidou
Materials Sciences and Applications, 2015, 6, 86-94 Published Online January 2015 in SciRes. http://www.scirp.org/journal/msa http://dx.doi.org/10.4236/msa.2015.61011 Characterization of the A6060 Al Alloy
More informationAERO 214. Introduction to Aerospace Mechanics of Materials. Lecture 2
AERO 214 Introduction to Aerospace Mechanics of Materials Lecture 2 Materials for Aerospace Structures Aluminum Titanium Composites: Ceramic Fiber-Reinforced Polymer Matrix Composites High Temperature
More informationThe Effects of Heat Treatment on the Mechanical Properties of Camshaft Made of Ductile Cast Iron
International Refereed Journal of Engineering and Science (IRJES) ISSN (Online) 2319-183X, (Print) 2319-1821 Volume 6, Issue 11 (November 2017), PP. 34-40 The Effects of Heat Treatment on the Mechanical
More informationEvaluation of Mechanical Properties of Aluminium Metal Matrix Reinforced with Silicon
SSRG International Journal of Mechanical Engineering (SSRG - IJME) Volume Issue 1 January 2018 Evaluation of Mechanical Properties of Aluminium Metal Matrix Reinforced with Silicon V.Naga Malleswari #1
More informationINTERDEPENDENCE BETWEEN COOLING RATE, MICROSTRUCTURE AND POROSITY IN MG ALLOY AE42
INTERDEPENDENCE BETWEEN COOLING RATE, MICROSTRUCTURE AND POROSITY IN MG ALLOY AE42 Liang Wang 1, Hongjoo Rhee 1, Sergio D. Felicelli 2, Adrian S. Sabau 3, John T. Berry 2 1 Center for Advanced Vehicular
More informationSchematic representation of the development of microstructure. during the equilibrium solidification of a 35 wt% Ni-65 wt% Cu alloy
Schematic representation of the development of microstructure during the equilibrium solidification of a 35 wt% Ni-65 wt% Cu alloy At 1300 ºC (point a) the alloy is in the liquid condition This continues
More informationChapter 1. The Structure of Metals. Body Centered Cubic (BCC) Structures
Chapter 1 The Structure of Metals Body Centered Cubic (BCC) Structures Figure 1. The body-centered cubic (bcc) crystal structure: (a) hard-ball model; (b) unit cell; and (c) single crystal with many unit
More informationEngineering Materials
Engineering Materials Learning Outcome When you complete this module you will be able to: Describe the mechanical properties of ferrous and non-ferrous engineering materials, plus the effects and purposes
More informationEffects of Microstructures and Process Variables on the Mechanical Properties of Rolled Ribbed Medium Carbon Steel
Journal of Emerging Trends in Engineering and Applied Sciences (JETEAS) 3 (3): 507-512 Scholarlink Research Institute Journals, 2012 (ISSN: 2141-7016) jeteas.scholarlinkresearch.org Journal of Emerging
More informationCHAPTER INTRODUCTION
1 CHAPTER-1 1.0 INTRODUCTION Contents 1.0 Introduction 1 1.1 Aluminium alloys 2 1.2 Aluminium alloy classification 2 1.2.1 Aluminium alloys (Wrought) 3 1.2.2 Heat treatable alloys (Wrought). 3 1.2.3 Aluminum
More informationFailure Analysis for the Economizer Tube of the Waste Heat Boiler
China Steel Technical Report, No. 22, pp. 53 58, (2009) Tsung-Feng Wu 53 Failure Analysis for the Economizer Tube of the Waste Heat Boiler TSUNG-FENG WU New Materials Research and Development Department
More informationThe Effect of Arc Voltage and Welding Current on Mechanical and Microstructure Properties of 5083-Aluminium Alloy Joints used in Marine Applications
EP11 The Effect of Arc Voltage and Welding Current on Mechanical and Microstructure Properties of 5083-Aluminium Alloy Joints used in Marine Applications C.W. Mohd Noor 1, Khalid Samo 2, Nurazilla 3, M.
More informationMSE-226 Engineering Materials
MSE-226 Engineering Materials Lecture-7 ALLOY STEELS Tool Steels TYPES of FERROUS ALLOYS FERROUS ALLOYS Plain Carbon Steels Alloy Steels Cast Irons - Low carbon Steel - Medium carbon steel - High carbon
More informationMONITORING OF COPPER ALLOYS STRUCTURES DURING SOLIDIFICATION AND COOLING OF CASTINGS. MACHUTA Jiří 1, NOVÁ Iva 1
March 25 th 2015 MONITORING OF COPPER ALLOYS STRUCTURES DURING SOLIDIFICATION AND COOLING OF CASTINGS MACHUTA Jiří 1, NOVÁ Iva 1 1 TU v Liberci - Technical University of Liberec, Liberec, Czech Republic,
More informationAvailable online at ScienceDirect
Available online at www.sciencedirect.com *.s;@# *," ScienceDirect JOURNAL OF IRON AND STEEL RESEARCH, INTERNATIONAL. 2011, 18(3) : 34-39 Influence of Mold Preheating and Silicon Content on Microstructure
More informationINFLUENCE OF HEAT TREATMENT ON MECHANICAL BEHAVIOR OF ALUMINIUM- 7075/SILCON CARBIDE COMPOSITES MANUFACTURED BY SQUEEZE CASTING PROCESS
Influence of heat treatment on mechanical behavior. INFLUENCE OF HEAT TREATMENT ON MECHANICAL BEHAVIOR OF ALUMINIUM- 7075/SILCON CARBIDE COMPOSITES MANUFACTURED BY SQUEEZE CASTING PROCESS P. Laxminarayana
More informationStudy of Mechanical Properties of Aluminium Alloy Composites
American Journal of Materials Science 2016, 6(4A): 72-76 DOI: 10.5923/c.materials.201601.14 Study of Mechanical Properties of Aluminium Alloy Composites Poornesh M. 1,*, Harish N. 2, Kiran Aithal 2 1 Department
More informationROLE OF SOLUTE AND TRANSITION METALS IN GRAIN REFINEMENT OF ALUMINUM ALLOYS UNDER ULTRASONIC MELT TREATMENT
13 th International Conference on Aluminum Alloys (ICAA13) Edited by: Hasso Weiland, Anthony D. Rollett, William A. Cassada TMS (The Minerals, Metals & Materials Society), 2012 ROLE OF SOLUTE AND TRANSITION
More informationME254: Materials Engineering Second Midterm Exam 1 st semester December 10, 2015 Time: 2 hrs
ME254: Materials Engineering Second Midterm Exam 1 st semester 1436-1437 December 10, 2015 Time: 2 hrs Problem 1: (24 points) A o = π/4*d o 2 = π/4*17 2 = 227 mm 2 L o = 32 mm a) Determine the following
More informationEffect of grain size for the tensile strength and the low cycle fatigue at elevated temperature of alloy 718 cogged by open die forging press
Superalloys 718, 625, 706 and Derivatives 2005 Edited by E.A. Loria TMS (The Minerals, Metals & Materials Society), 2005 Effect of grain size for the tensile strength and the low cycle fatigue at elevated
More informationFatigue life estimation of Aluminium Alloy reinforced with SiC particulates in annealed conditions
18 TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS Abstract Fatigue life estimation of Aluminium Alloy reinforced with SiC particulates in annealed conditions D. P. Myriounis, S.T.Hasan Sheffield Hallam
More informationCRACKING MECHANISMS IN A HOT-DIP ZINC COATED STEEL
CRACKING MECHANISMS IN A HOT-DIP ZINC COATED STEEL V. Di Cocco 1, F Iacoviello 1 & S. Natali 2 1 Di.M.S.A.T., Università di Cassino, Cassino (FR), ITALY 2 I.C.M.M.P.M., Università di Roma La Sapienza,
More informationEFFECTS OF COOLING MEDIA ON THE MECHANICAL PROPERTIES AND MICROSTRUCTURE OF SAND AND DIE CASTING ALUMINIUM ALLOYS
EFFECTS OF COOLING MEDIA ON THE MECHANICAL PROPERTIES AND MICROSTRUCTURE OF SAND AND DIE CASTING ALUMINIUM ALLOYS B.O. Adewuyi and J.A. Omotoyinbo Department of Metallurgical and Materials Engineering,
More informationA MICROSTRUCTURAL STUDY ON CuSn10 BRONZE PRODUCED BY SAND AND INVESTMENT CASTING TECHNIQUES
A MICROSTRUCTURAL STUDY ON CuSn10 BRONZE PRODUCED BY SAND AND INVESTMENT CASTING TECHNIQUES Zeynep TAŞLIÇUKUR*, Gözde S. ALTUĞ*, Şeyda POLAT**, Ş. Hakan ATAPEK**, Enbiya TÜREDİ** *) Gedik University, Faculty
More informationChapter Two. Aluminum Extrusion Alloys
Chapter Two Aluminum Extrusion Alloys Advantages of Aluminum Extrusions Aluminum s Material Advantages: Recyclable and Nontoxic Lightweight Strong High Strength to Weight Ratio Resilient Corrosion-Resistant
More informationof Metal Alloys This is just an extension of the previous chapter Hardenability of Steels: The Jominy Test
Chapter 11 Applications and Processing of Metal Alloys This is just an extension of the previous chapter Hardenability of Steels: The Jominy Test As usual, everything is standardized! After the Jominy
More informationCHAPTER 4 1/1/2016. Mechanical Properties of Metals - I. Processing of Metals - Casting. Hot Rolling of Steel. Casting (Cont..)
Processing of Metals - Casting CHAPTER 4 Mechanical Properties of Metals - I Most metals are first melted in a furnace. Alloying is done if required. Large ingots are then cast. Sheets and plates are then
More informationLAB IV. Effects of Heat Treatment on Steel, Aluminum and Brass Alloys - Microstructure and Properties
LAB IV Effects of Heat Treatment on Steel, Aluminum and Brass Alloys - Microstructure and Properties PRE LAB PREPARATION (required!) 1. Using the ASM metal handbooks or other resources find and print/copy
More informationLAB IV. Effects of Heat Treatment on Steel, Aluminum and Brass Alloys - Microstructure and Properties
LAB IV Effects of Heat Treatment on Steel, Aluminum and Brass Alloys - Microstructure and Properties PRE LAB PREPARATION (required!) 1. Using the ASM metal handbooks or other resources find and print/copy
More informationJouji Oshikiri 1, Norio Nakamura 2 and Osamu Umezawa 1
Proceedings of the 12th International Conference on Aluminium Alloys, September 5 9, 5-9, 21, Yokohama, Japan 21 21 The Japan Institute of Light Metals pp. 2381-2386 2381 Jouji Oshikiri 1, Norio Nakamura
More informationInfluence of Niobium or Molybdenum in Titanium Alloy for Permanent Implant Application Yuswono Marsumi 1, a and Andika Widya Pramono 1,b
Advanced Materials Research Vol. 900 (2014) pp 53-63 (2014) Trans Tech Publications, Switzerland doi:10.4028/www.scientific.net/amr.900.53 Influence of Niobium or Molybdenum in Titanium Alloy for Permanent
More informationEXPERIMENTAL STUDIES ON MECHANICAL PROPERTIES OF E- GLASS SHORT FIBRES & FLY ASH REINFORCED AL 7075 HYBRID METAL MATRIX COMPOSITES
EXPERIMENTAL STUDIES ON MECHANICAL PROPERTIES OF E- GLASS SHORT FIBRES & FLY ASH REINFORCED AL 7075 HYBRID METAL MATRIX COMPOSITES PRABHAKAR KAMMER 1*, DR. H.K.SHIVANAND 2, SANTHOSH KUMAR.S 3 1* professor,
More informationHeat treatment and effects of Cr and Ni in low alloy steel
Bull. Mater. Sci., Vol. 34, No. 7, December 2011, pp. 1439 1445. Indian Academy of Sciences. Heat treatment and effects of Cr and Ni in low alloy steel MOHAMMAD ABDUR RAZZAK Materials and Metallurgical
More informationHigh Temperature Mechanical Properties of Silicon Carbide Particulate Reinforced Cast Aluminum Alloy Composite
Leonardo Electronic Journal of Practices and Technologies ISSN 1583-1078 Issue 18, January-June 2011 p. 9-16 High Temperature Mechanical Properties of Silicon Carbide Particulate Reinforced Cast Aluminum
More informationEVALUATION OF MECHANICAL PROPERTIES OF AL6061 METAL MATRIX COMPOSITE REINFORCED WITH FUSED ZIRCONIA ALUMINA
EVALUATION OF MECHANICAL PROPERTIES OF AL6061 METAL MATRIX COMPOSITE REINFORCED WITH FUSED ZIRCONIA ALUMINA *P.V.Rajesh, **S.Roseline, *** V.Paramasivam *P.G Scholar: Department of Mechanical Engineering,
More informationEffect of thermal exposure on mechanical properties hypo eutectic aerospace grade aluminium-silicon alloy
IOP Conference Series: Materials Science and Engineering PAPER OPEN ACCESS Effect of thermal exposure on mechanical properties hypo eutectic aerospace grade aluminium-silicon alloy To cite this article:
More informationInternational Journal of Scientific & Engineering Research, Volume 6, Issue 3, March-2015 ISSN
1530 Component Crack Analysis of high pressure die casting aluminum alloy (Alsi9cu ) Satish kumar Manocha Designation Dy. Manager Department - R&D Name of industries Rico auto industries ABSTRACT: Crack
More informationInfluence of Remelting AlSi9Cu3 Alloy with Higher Iron Content on Mechanical Properties
A R C H I V E S of F O U N D R Y E N G I N E E R I N G Published quarterly as the organ of the Foundry Commission of the Polish Academy of Sciences ISSN (1897-3310) Volume 18 Issue 3/2018 25 30 4/3 Influence
More informationEVALUATION OF THERMAL FATIGUE PROPERTIES OF HSS ROLL MATERIALS. Jong Il Park a Chang Kyu Kim b Sunghak Lee b
EVALUATION OF THERMAL FATIGUE PROPERTIES OF HSS ROLL MATERIALS Jong Il Park a Chang Kyu Kim b Sunghak Lee b a Hot Rolling Department, Pohang Iron and Steel Co., Ltd., Pohang 79-75 b Center for Advanced
More informationComparative study of metallurgical mechanical characteristics obtained through stir casting and centrifugal casting of Al-Si alloys
Comparative study of metallurgical mechanical characteristics obtained through stir casting and centrifugal casting of Al-Si alloys Shrishail M B 1*, A Chaitanya 2*, Prabhu T B 3*, Gajendra S 4* 1,2,3,4UG
More informationDevelopment of creep-resistant magnesium casting alloys for high temperature automotive applications
High Performance Structures and Materials IV 53 Development of creep-resistant magnesium casting alloys for high temperature automotive applications L. Han, H. Hu & D. O. Northwood Department of Mechanical,
More informationTensile & Fracture Behavior of Al-Si Cp Metal Matrix Composites
Tensile & Fracture Behavior of Al-Si Cp Metal Matrix Composites Jushkumar Siddani Department of Mechanical Engineering Anurag Group of Institutions, Hyderabad, Telangana, India Dr. C. Srinvas Department
More informationMg-Al alloys, such as AZ91 and AM60 alloys, have been
Effect of Cu addition on microstructure and properties of Mg-10Zn-5Al-0.1Sb high zinc magnesium alloy *You Zhiyong, Zhang Yuhua, Cheng Weili, Zhang Jinshan and Wei Yinghui ( College of Materials Science
More informationPREPARATION AND PROPERTIES OF Al Fe AND Al Fe Cr ALLOYS. Petra HANUSOVÁ 1, Pavel NOVÁK 2
PREPARATION AND PROPERTIES OF Al Fe AND Al Fe Cr ALLOYS Petra HANUSOVÁ 1, Pavel NOVÁK 2 1 Brno University of Technology, Faculty of Mechanical Engineering, Institute of Material Science and Engineering,
More informationThe Recycling of Steel and Brass Chips to Produce Composite Materials via Cold Pressing and Sintering
The International Journal Of Engineering And Science (IJES) Volume 5 Issue 5 Pages PP -1-6 216 ISSN (e): 2319 1813 ISSN (p): 2319 185 The Recycling of Steel and Brass Chips to Produce Composite Materials
More informationBehavior Analysis of Aluminium Alloy with Reinforced Silicon Carbide Particles
Behavior Analysis of Aluminium Alloy with Reinforced Silicon Carbide Particles Vijayakumar S S PG Student, M E Computer Aided Design, Mahendra Engineering College, Salem, Tamilnadu, India Annamalai P Department
More informationFatigue Behaviour of Medium Carbon Steel of Different Grain Structures
Fatigue Behaviour of Medium Carbon Steel of Different Grain Structures S. AbdulKareem 1* S. I. Talabi 2 J. A. Adebisi 2 T. Yahaya 2 O. H. Amuda 3 1.Department of Mechanical Engineering, University of Ilorin,
More informationDEVELOPMENT OF TWIN-SCREW RHEO-EXTRUSION PROCESS
DEVELOPMENT OF TWIN-SCREW RHEO-EXTRUSION PROCESS K. A. Roberts and Z Fan Department of Mechanical Engineering, Brunel University, Uxbridge, Middlesex, UB8 3PH, UK Summary Conventional hot extrusion reductions
More information3 Department of Mechanical Engineering Technology, Universiti Tun Hussein Onn Malaysia, Batu Pahat, Malaysia,
AL LM6 HOLLOW CYLINDER FABRICATED USING CENTRIFUGAL CASTING Saifulnizan Jamian 1, Safwan Yutiman 2 and Haffidzudin Hehsan 3 1 Department of Engineering Mechanics, Universiti Tun Hussein Onn Malaysia, Batu
More informationTENSILE AND FRACTURE BEHAVIOR OF 6061 Al-Si Cp METAL MATRIX COMPOSITES
International Conference on Advanced Materials and manufacturing Technologies (AMMT) December 8-20, 204 JNTUH College of Engineering Hyderabad TENSILE AND FRACTURE BEHAVIOR OF 606 Al-Si Cp METAL MATRI
More informationSolidification and Crystallisation 5. Formation of and control of granular structure
MME 345 Lecture 08 Solidification and Crystallisation 5. Formation of and control of granular structure Ref: [1] A. Ohno, The Solidification of Metals, Chijin Shokan Co. Ltd., 1976 [2] P. Beeley, Foundry
More informationInfluence of Semi-Solid Isothermal Heat Treatment on Microstructure of Gray Cast Iron
Journal of Minerals and Materials Characterization and Engineering, 2013, 1, 326-330 Published Online November 2013 (http://www.scirp.org/journal/jmmce) http://dx.doi.org/10.4236/jmmce.2013.16049 Influence
More informationChapter 11: Applications and Processing of Metal Alloys
Chapter 11: Applications and Processing of Metal Alloys ISSUES TO ADDRESS... What are some of the common fabrication techniques for metals? What heat treatment procedures are used to improve the mechanical
More informationMATERIALS SCIENCE-44 Which point on the stress-strain curve shown gives the ultimate stress?
MATERIALS SCIENCE 43 Which of the following statements is FALSE? (A) The surface energy of a liquid tends toward a minimum. (B) The surface energy is the work required to create a unit area of additional
More informationCopper & Copper Alloys CuZn31Si1 (OF 2270)
Copper and Copper Alloys Page 1 of 5 no responsibility is taken for the correctness of this information 02/2014 Cu Zn Pb Sn Fe Mn Ni Al Si As Co Cr Others min. 66.0 Rem. 0.1 - - - - - 0.7 - - - - max.
More informationChapter 11 Part 2. Metals and Alloys
Chapter 11 Part 2 Metals and Alloys Nomenclature of Steels Historically, many methods for identifying alloys by their composition have been developed The commonly used schemes in this country are those
More informationEffect of Zn content on microstructure, mechanical properties and fracture behavior of Mg-Mn alloy
Effect of Zn content on microstructure, mechanical properties and fracture behavior of Mg-Mn alloy *Yin Dongsong 1, Zhang Erlin 2 and Zeng Songyan 1 (1. School of Materials Science and Engineering, Harbin
More informationInvestigation on the homogenization annealing treatment of 5052-based aluminum alloys
Indian Journal of Engineering & Materials Sciences Vol. 24, February 2017, pp. 57-62 Investigation on the homogenization annealing treatment of 5052-based aluminum alloys Jing Zhang*, Jingjing Zhao & Rulin
More information