Rev. 03. Supercored 71. FLUX CORED ARC WELDING CONSUMABLE FOR WELDING OF MILD & 490MPa CLASS HIGH TENSILE STEEL HYUNDAI WELDING CO., LTD.

Size: px

Start display at page:

Download "Rev. 03. Supercored 71. FLUX CORED ARC WELDING CONSUMABLE FOR WELDING OF MILD & 490MPa CLASS HIGH TENSILE STEEL HYUNDAI WELDING CO., LTD."

Alexis Garrett
6 years ago
Views:

1 Rev. 03 FLUX CORED ARC WELDING CONSUMABLE FOR WELDING OF MILD & 490MPa CLASS HIGH TENSILE STEEL HYUNDAI WELDING CO., LTD.

2 v Specification (M E491T1-C1A2-CS1) (AWS A5.20 E71T-1C) EN ISO A T 42 2 P C1 1 H10 v Applications All position welding of machinery, shipbuilding, bridges. Impact values of weld metal are good. v Characteristics on Usage is a flux cored wire which has been designed to get a good usability in all position for wide range of welding currents. With its quiet and smooth arc, its slag detachability is very good. v Note on Usage 1. Proper preheating(50~150, 122~302 ) and interpass temperature must be used in order to release hydrogen which may cause cracking in weld metal when electrodes are used for medium and heavy plates. 2. One-side welding defects such as hot cracking may occur with wrong welding parameter such as high welding speed. 3. Use 100% CO₂gas.

3 Mechanical Properties & Chemical Composition of All Weld Metal v Welding Conditions Method by AWS Spec. Welding Position : 1G(PA) Diameter : 1.2mm (0.045in) Shielding Gas : 100%CO₂ Flow Rate : 20 l /min Amp./ Volt. : 280A / 32V Stick-Out : 20~25mm (0.79~0.98in) Pre-Heat : R.T. Interpass Temp. : 150±15 (302±59 ) [ Joint Preparation & Layer Details ] Polarity : DC(+) v Mechanical Properties of all weld metal Tensile Test CVN Impact Test J(ft lbs) YS TS EL (%) 0 (32 ) -20 (-4 ) 545 (79) 572 (83) (81) 70 (52) 400 (58) 490~660 (70~95) 22 27J at 20 ( 20ft lbs at 0 ) v Chemical Analysis of all weld metal(wt%) C Si Mn P S

4 Mechanical Properties & Chemical Composition of All Weld Metal v Welding Conditions Method by AWS Spec. Welding Position : 1G(PA) Diameter : 1.4mm (0.052in) Shielding Gas : 100%CO₂ Flow Rate : 20 l /min Amp./ Volt. : 300A / 32V Stick-Out : 20~25mm (0.79~0.98in) Pre-Heat : R.T. Interpass Temp. : 150±15 (302±59 ) [ Joint Preparation & Layer Details ] Polarity : DC(+) v Mechanical Properties of all weld metal Tensile Test CVN Impact Test J(ft lbs) YS TS EL (%) 0 (32 ) -20 (-4 ) 548 (79) 576 (84) (94) 81 (60) 400 (58) 490~660 (70~95) 22 27J at 20 ( 20ft lbs at 0 ) v Chemical Analysis of all weld metal(wt%) C Si Mn P S

5 Mechanical Properties & Chemical Composition of All Weld Metal v Welding Conditions Method by AWS Spec. Welding Position : 1G(PA) Diameter : 1.6mm (1/16in) Shielding Gas : 100%CO₂ Flow Rate : 20 l /min Amp./ Volt. : 320~330A / 29~30V Stick-Out : 20~25mm (0.79~0.98in) Pre-Heat : R.T. Interpass Temp. : 150±15 (302±59 ) [ Joint Preparation & Layer Details ] Polarity : DC(+) v Mechanical Properties of all weld metal Tensile Test CVN Impact Test J(ft lbs) YS TS EL (%) 0 (32 ) -20 (-4 ) 551 (80) 586 (85) (77) 66 (49) 400 (58) 490~660 (70~95) 22 27J at 20 ( 20ft lbs at 0 ) v Chemical Analysis of all weld metal(wt%) C Si Mn P S

6 Welding Efficiency v Deposition Rate & Efficiency (size) Welding Conditions Amp.(A) Volt.(V) Wire Feed Speed m/min (in/min) Deposition Efficiency % Deposition Rate kg/hr(lb/hr) 1.2mm (0.045in) 1.4mm (0.052in) (400) 84~ (7.5) (450) 85~ (9.9) (600) 86~ (11.4) (300) 85~ (8.6) (400) 85~ (10.6) (500) 86~ (12.8) (250) 85~ (9.2) 1.6mm (1/16in) (300) 86~ (10.6) (320) 87~ (11.7) (360) 87~ (12.5) Remark Deposition efficiency =(Deposited metal weight/ Wire weight used) 100 Deposition rate =(Deposited metal weight/ Welding time,min.) 60 * Shielding Gas : 100%CO₂

7 Diffusible Hydrogen Content v Welding Conditions Diameter : 1.2mm (0.045in) Amps(A) / Volts(V) : 230A / 26V Shielding Gas : 100%CO₂ Flow Rate : 20 l /min Welding Position : 1G (PA) Stick-Out : Welding Speed : 20~25mm (0.79~0.98in) 30 cm/min (12 in/min) Current Type & Polarity : DC(+) v Hydrogen Analysis Using Gas Chromatography Method Hydrogen Evolution Time : 72 hrs Evolution Temp. : 45 (113 ) Barometric Pressure : 780 mm-hg v Result( ml /100g Weld Metal) X1 X2 X3 X Average Hydrogen Content 5.4 ml / 100g Weld Metal

8 Proper Welding Condition v Proper Current Range Wire Dia, Shielding Gas Welding Position 1.2mm (0.045in) 1.4mm (0.052in) 1.6mm (1/16in) F & HF 120~300Amp 200~350Amp 180~400Amp Supercored %CO₂ V-Up & OH 120~260Amp 140~270Amp 160~280mp V-Down 200~300Amp 220~320Amp 250~300Amp

9 Approvals v Shipping Approvals Welding Position Register of shipping & Size KR ABS LR BV DNV GL NK All V-Down 3SMG, 3YSMG H10 3SAH10, 3YSA 3S, 3YSH10 SA3M,3YMHH A3M,3YMHH IIIYMSH10 3YH10S KSW53G H10 KAW53MG H 10 v F No & A No F No A No 6 1

Rev. 02 SF-71LF. FLUX CORED ARC WELDING CONSUMABLE FOR WELDING OF MILD & 490MPa CLASS HIGH TENSILE STEEL HYUNDAI WELDING CO., LTD.

Rev. 02 SF-71LF. FLUX CORED ARC WELDING CONSUMABLE FOR WELDING OF MILD & 490MPa CLASS HIGH TENSILE STEEL HYUNDAI WELDING CO., LTD. Rev. 02 SF-71LF FLUX CORED ARC WELDING CONSUMABLE FOR WELDING OF MILD & 490MPa CLASS HIGH TENSILE STEEL HYUNDAI WELDING CO., LTD. v Specification (M E491T1-C1A2-CS1) (AWS A5.20 E71T-1C) JIS Z3313 T49J