Bearing grease for high temperatures, especially for line contact. Characteristics Unit Value Test method

Transcription

1 Arcanol LOAD150 Bearing grease for high temperatures, especially for line contact Characteristics Value Test method KP2N-20 DIN to 140 DIN ,94 lithium complex Base oil viscosity at 40 C: [mm²/s] ISO VG 150 DIN Worked penetration: [0,1 mm] DIN ISO 2137 NLGI grade: 2-3 DIN Copper corrosion after 24 h/100 C: [Corr.Grad] /30-RT [mg] vwk50 20 mg /80-RT [mg] vwk50 50 mg F h DIN Edition

2 Arcanol LOAD220 Rolling bearing grease for universal applications, moderate to high load, wide temperature range, good water resistance Characteristics Value Test method KP2/1K-20 DIN to 140 DIN ,9 mixed thickener Base oil viscosity at 40 C: [mm²/s] ISO VG 220 DIN Worked penetration: [0,1 mm] DIN ISO 2137 NLGI grade: 1-2, 2 DIN Copper corrosion after 24 h/120 C: [Corr.Grad] /10-RT [mg] vwk50 35 mg /80-RT [mg] vwk50 35 mg MP - 7,5/80-80 [mg] vwk50 35 mg F h DIN [h] no failure < 100 h Edition

3 Arcanol LOAD400 Bearing grease for universal applications, high dynamic secondary stress, high loads, low starting temperatures, low starting friction over a wide speed range, also for applications with vertical shaft Characteristics Value Test method Temperature range: -40 to 130 C Longtime limit temperature 80 C Density: 0.9 kg/dm³ lithium/calcium Base oil viscosity at 40 C: 400 mm²/s DIN at 100 C: 27 mm²/s DIN Worked penetration: mm DIN ISO 2137 NLGI grade: 2 DIN Drop point: 170 C Water resistance: 1-90 Range Corrosion Emcor Test: with 0.5 % NaCl: Copper corrosion after 24 h/130 C: 1, Running time 500 hours without failure /80-RT vwk50 35 mg MP /10-RT vwk50 35 mg MP - 7.5/80-80 vwk50 35 mg MP - 7.5/80-RT vwk50 35 mg A/1500/ F h DIN no failure < 100 h DIN / Schaeffler Spec. Speed limit n*dm mm/min 400, ,000 properties or warranties cannot be taken over. Edition

4 Arcanol LOAD460 Wind energy main shaft bearings, especially for bearings with pin-cage and other large bearings, high loads, low starting temperatures, wide temperature range, excellent water resistance and corrosion protection, False Brinelling, vibrations Characteristics Value Test method Temperature range: -40 to 130 C Longtime limit temperature 80 C Density: 0.93 kg/dm³ lithium/calcium Base oil viscosity at 40 C: 400 mm²/s DIN at 100 C: 25.8 mm²/s DIN Worked penetration: mm DIN ISO 2137 NLGI grade: 1 DIN Drop point: > 170 C Water resistance: 1-90 Range Corrosion Emcor Test: with 1 % NaCl: Copper corrosion after 24 h/120 C: 1, Running time 500 hours without failure /80-RT vwk50 35 mg MP - 7.5/80/RT vwk50 35 mg A/1500/ F h DIN no failure < 100 h Low temperature torque -30 C Start / Steady-state 1000 / Nmm IP 186 Lowest Isothermal Temperature (FE8) roller bearing hours reached: yes10 C: / 6 mg DIN / Schaeffler Spec. FAG Speed limit n*dm mm/min 400, ,000 properties or warranties cannot be taken over. Edition

5 Arcanol LOAD1000 Very high load, shock load, wide temperature range, good water and corrosion resistance, low to moderate speed Characteristics Value Test method KP2K-20 DIN to 120 DIN ,9 mixed thickener Base oil viscosity at 40 C: [mm²/s] ISO VG 1000 DIN Worked penetration: [0,1 mm] DIN ISO 2137 NLGI grade: 2 DIN Copper corrosion after 24 h/100 C: [Corr.Grad] / [mg] vwk50 35 mg /80-RT [mg] vwk50 35 mg /30-RT [mg] vwk50 35 mg MP - 7,5/80-80 [mg] vwk50 35 mg MP - 75/80-RT [mg] vwk50 35 mg F h DIN [h] no failure < 50 h Edition