CONTENTS: POLYETHYLENE POLYPROPYLENE HDPE EX EX3-88S 2 EX3-188S 3 EX5 (HM9458F) F (FILM GRADE) 5 LDPE LLDPE 289AA 6 HOMOPOLYMER

Transcription

1

2 CONTENTS: POLYETHYLENE HDPE EX EX3-88S 2 EX3-188S 3 EX5 (HM9458F) F (FILM GRADE) 5 LDPE LLDPE 289AA 6 POLYPROPYLENE HOMOPOLYMER Z69S (552R) 7 HP558J 8 Contact 9

3 EX 3-88 License grade code HM 5818 T2N EX 3-80 is a high density polyethylene with 1-butene as co monomer. It is natural, good ESCR, good impact strength, tough and rigid pipe resin. Pipe extrusion PE class Industrial and pressure pipe, gas pipe, drinking water pipe Pressure less pipe, relining, fittings PROPERTIES TEST METHOD UNIT TYPICAL VALUE Mass density (32 C) ISO 8812 g/cm Melt flow rate (895 C/0,5kg) ISO 8822 g/85min 5,.0 Melt flow rate (895 C/38,82kg) ISO 8822 g/85min 83 FRR(38,210) - 32 Stress at yield ISO 032 Mpa 33 Flextural creep modulus (.point,8min) DIN Mpa 905 Tensile modulus (32 C,v=8mm/min,secant) ISO 032 Mpa 105 Stress at break ISO 032 Mpa 20 Elongation at break ISO 032 % >105 Elongation at yield ISO 032 % 1 Softening temperature ISO 252 C 22 Brittle temperature ASTM D C <-15 shore D hardness ISO ESCR in full notch creep test (15 C,32Arcopal) ISO CD h@.45 Mpa 05 Impact strength (32 C) ISO 82918eA Kj/m3 32 S. test (RCP) ISO DIS bar PC >2 Notch test (SCG) ISO DIS Mpa h@.45 >305 1

4 EX 3-88S License grade code HM 5818 T3N EX 3-80S is a high density polyethylene with 1-butene as co monomer. It is natural, excellent ESCR, high impact strength, outstanding hydrostatic strength for PE 80 class. Pipe extrusion PE 80 class Industrial and pressure pipe, gas pipe, drinking water pipe relining, fttings PROPERTIES TEST METHOD UNIT TYPICAL VALUE Mass density (32 C) ISO 8812 g/cm Melt flow rate (895 C/0,5kg) ISO 8822 g/85min 5,.2 Melt flow rate (895 C/38,82kg) ISO 8822 g/85min 85,2 FRR(38,210) - 3. Stress at yield ISO 032 Mpa 33 Flextural creep modulus (.point,8min) DIN Mpa 955 Tensile modulus (32 C,v=8mm/min,secant) ISO 032 Mpa 105 Stress at break ISO 032 Mpa 20 Elongation at break ISO 032 % >8555 Elongation at yield ISO 032 % 85 Softening temperature ISO 252 C 22 Brittle temperature ASTM D C <-15 shore D hardness ISO ESCR in full notch creep test (15 C,32Arcopal) ISO CD h@.45 Mpa 355 Impact strength (32 C) ISO 82918eA Kj/m3 32 S. test (RCP) ISO DIS bar PC >2 Notch test (SCG) ISO DIS Mpa h@.45 >3055 Hydrostatic strength test (15 C) ISO 8822 Mpa h@.42 >0555 2

5 EX 3-188S License grade code HM CRP 188 N EX3-100s is a high density polyethylene with 1-butene as co monomer. It is natural outstanding ESCR, high impact strength, outstanding hydrostatic strength for PE 100 class. Pipe extrusion PE 100 class Industrial and pressure pipe, gas pipe, drinking water pipe relining, fttings PROPERTIES TEST METHOD UNIT TYPICAL VALUE Mass density (32 C) ISO 8812 g/cm Melt flow rate (895 C/0,5kg) ISO 8822 g/85min 5,33 Melt flow rate (895 C/38,82kg) ISO 8822 g/85min 2,3 FRR(38,210) - 32 Stress at yield ISO 032 Mpa 32 Flextural creep modulus (.point,8min) DIN Mpa 8505 Tensile modulus (32 C,v=8mm/min,secant) ISO 032 Mpa 105 Stress at break ISO 032 Mpa 22 Elongation at break ISO 032 % >8555 Elongation at yield ISO 032 % 85 Softening temperature ISO 252 C 2. Brittle temperature ASTM D C <-15 shore D hardness ISO ESCR in full notch creep test (15 C,32Arcopal) ISO CD h@.45 Mpa.55 Impact strength (32 C) ISO 82918eA Kj/m3 30 S. test (RCP) ISO DIS bar PC >35 Notch test (SCG) ISO DIS Mpa h@.45 >8555 Hydrostatic strength test (15 C) ISO 8822 Mpa h@.42 >

6 EX 5 License grade code HM 9458 F EX 5 is a high density polyethylene with 1-butene as co monomer. It is good toughness, low gel level, good toor strength, good stiffness and tenacity, high molar mass. Film extrusion Counter bag, carrier bag Wrapping films & sheets PROPERTIES TEST METHOD UNIT TYPICALVALUE Mass density (32 C) ISO 8812 g/cm Melt flow rate (895 C/0,5kg) ISO 8822 g/85min 5,31 Melt flow rate (895 C/38,82kg) ISO 8822 g/85min 1 FRR(38,210) - 39 FN MPC-TEST - <2/<835 Stress at yield ISO 032 Mpa 3. Max. tensile strength MD / TD ISO 032 Mpa.01.5 Stress at break ISO 032 Mpa 20 Tear strength MD / TD ISO m N Max. Elongation MD / TD ISO 032 % Softening temperature ISO 252 C 20 Brittle temperature ASTM D C <-15 shore D hardness ISO Dart drop impact ASTM D 8259 g 335 4

7 7888F (FILM GRADE) 7000 F is a high density polyethylene resin; a product of bi-modal process from mitsui chemicals, Inc. of Japan Recommend film thickness at micron High tensile strength with good dart impact strength, low gel content Good moisture barrier, food contact applicable Good impact resistance and process ability, shopping bag and T-shirt bag Garbage bag, liner bag, enhanced ultra thin film, high stiffness Wide service temperature range, UV resistance PROPERTIES TEST METHOD UNIT TYPICAL VALUE Resin Properties Melt flow rate ASTM D 895 C, 3482 kg g/85 min 545. Density ASTM D 8050 g/cm Melting point ASTM D 3882 C 828 Vicat softening point ASTM D 8030 C 83. Brittleness temperature ASTM D 2.2 C < -25 ESCR ASTM D 05 C hrs, F05 > 8555 Film Properties Tensile strength at yield ASTM D crosshead speed 05mm/min kg/cm3 Tensile strength at break ASTM D crosshead speed 05mm/min kg/cm3 Tensile modulus, 32 secant ASTM D crosshead speed 05mm/min kg/cm3 Elongation at break ASTM D crosshead speed 05mm/min % Elmendorf tear strength ASTM D 8933 g MD: -*, TD: 305* MD: 235*, TD: 285* MD: 1355*, TD: 1555* MD : 3.5*, TD :.05* MD : 2*, TD : 15* Dart impact strength ASTM D 8259 g 829 5

8 289AA LL0209AA & LL0209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. Frozen food bags, liners, carrier bags, garbage bags, agriculture films Lamination and coextruded films, shrink film (for blending with LDPE) Industrial consumer packaging and high clarity film if blended with (10-202) LDPE. PROPERTIES TEST METHOD UNIT TYPICAL VALUE Resin MFI@8951 C, 3482 kg D8321 gr/85min 549 Density D3129 gr/ml Vicat softening point D8030 C 855 Film Tensile strength@yield, MD/TD D221 Mpa Elongation@break, MD/TD D221 % Tensile strength@break, MD/TD D211 Mpa.8123 Tear strength, MD/TD D8933 gr/30mic Impact strength, dart D8259 gr 805 Haze D8552 % 85 Gloss (.01 ) D3.02 Rating 02 6

9 POLYPROPYLENE HOMOPOLYMER Z 69 S (552R) Z 69 S is a high melt flow homopolymer for the production of CF, BCF and staple fibers at medium to high spinning speeds. Z 69 S exhibits excellent anti-gas fading. Low denier staple fibers for nonwoven fabrics for diapers, Medical-sanitary applications and wipes High tenacity continuous filament for straps for backpacks, sport bags, bulk bags and for safety belt upholstery and sportswear Production of bulked continuous filament for carpets. Physical Mechanical Thermal PROPERTIES Melt flow rate (325 C, 3482 kg) Density Flexural modulus Tensile strength yield Elongation at yield Izod Impact Strength (notched) at 321C Hardness Shore D Vicat softening point (941 N) H.D.T. (54.2 Mpa) Accelerated oven ageing in air (forced circulation) at 805 C TEST METHOD ISO 8822 ISO 8812 ISO 821 ISO R 032 ISO R 032 ISO 815 ISO 121 ISO 252/A ISO 20/B ISO.022 UNIT dg / min g/cm2 N/mm3 N/mm3 % kj/m3 points C C hours TYPICAL VALUE

10 HP558J HP550J is a polypropylene homopolymer particularly suitable for the extrusion of sheet for thermoforming, film yarn and monofilament. This grade combines outstanding processability with good mechanical. This product is designed for the production of films that can be converted into stretched tapes for weaving applications. Stiff sheet for high quality thermoformings Packaging for dairy products Film yarn, raffia, tapes, strapping Carpet backings, bags, industrial fabrics, mats and artificials grass Physical Mechanical Thermal PROPERTIES Melt flow rate (325 C, 3482 kg) Density Flexural modulus Tensile strength yield Elongation at yield Izod Impact Strength (notched) at 321C Hardness shore D Vicat softening point (941 N) H.D.T. (54.2 Mpa) Accelerated oven ageing in air (forced circulation) at 805 C TEST METHOD ASTM D8321 ASTM D8050 ASTM D295 ASTM D221 ASTM D221 ASTM D302 ASTM D210 ASTM D8030 ASTM D2.1 ASTM D2583 UNIT g/85min g/cm2 MPa MPa % J/m R Scale C C hours TYPICAL VALUE