MATERIALS JEWELLERY HANDBOOK DIGITAL MANUFACTURING SOLUTIONS

Transcription

1 MATERIALS HANDBOOK JEWELLERY

2 SuperWAX The only DLP printing material that melts like wax. With a melting temperature of 50 C / 122 F SuperWAX is the ideal jewellery casting material to fit within your current jewellery casting process. Super smooth surfaces with no post-processing prior to treeing. Suitable for casting platinum. Layer thickness range from 25 microns. Direct casting in gypsum and phosphate investments. Platinum / gold / silver / non-precious Melts like real wax $355 p/l Investment casting guide BURNOUT GUIDE USING GYPSUM BONDED INVESTMENT 1382 F / 750 C Hold 4 hrs 900 F / 482 C TEMPERATURE 300 F / 149 C 700 F / 371 C Cast Temperature CAST Flask Orientation: Button side down (upside down) Recommended ramp time of approximately 9 F / 5 C per minute 73 F / 23 C Start from Ambient TIME Recommendations: Investment: Kerr Satin Cast 20 using a perforated flask

3 Materials Handbook - Jewellery SuperCAST HD The smoothest parts you ll ever see! Asiga has combined years of direct-casting knowledge and for SuperCAST HD has introduced a unique nano-technology to achieve stunning surface smoothness and detail definition. Direct casting in gypsum investments Durable resin for pre-cast finishing $355 p/l Investment casting guide BURNOUT GUIDE USING GYPSUM BONDED INVESTMENT 1382 F / 750 C Hold 4 hrs TEMPERATURE 900 F / 482 C Cast Temperature 700 F / 371 C CAST 300 F / 149 C Flask Orientation: Button side down (upside down) Recommended ramp time of approximately 9 F / 5 C per minute 73 F / 23 C Start from Ambient TIME Recommendations: Investment: Kerr Satin Cast 20 using a perforated flask

4 SuperCAST v3 SuperCAST v3 is Asiga s highest definition direct-casting material for direct casting in gypsum investments. Fast printing, durable and cast under normal burnout conditions. Direct casting in gypsum investments Fast print speeds $355 p/l Investment casting guide BURNOUT GUIDE USING GYPSUM BONDED INVESTMENT 1382 F / 750 C Hold 4 hrs 900 F / 482 C TEMPERATURE 300 F / 149 C 700 F / 371 C Cast Temperature CAST Flask Orientation: Button side down (upside down) Recommended ramp time of approximately 9 F / 5 C per minute 73 F / 23 C Start from Ambient TIME Recommendations: Investment: Kerr Satin Cast 20 using a perforated flask

5 PlasGRAY Looking for a low cost client validation model? PlasGRAY is the perfect design validation material. Super smooth matte surface finish which offers clear visibility of small details and texture. Also an excellent choice for printing miniature models. Jewellery design validation. RTV moulding Miniature model making $175 p/l Technical Data COLOR TENSILE STRENGTH ELONGATION AT BREAK ELONGATION AT YIELD FLEXURAL STRENGTH FLEXURAL MODULUS HARDNESS (SHORE D) VISCOSITY GLASS TRANSITION TEMPERATURE IZOD NOTCHED-IMPACT DENSITY GRAY 51.1 Mpa 6.58 % 8.40% 86.8 MPa 1910 MPa 82 Shore D 343 mpa s 84 C 4.97 kj/m² g/cm³

6 FusionGRAY A high temperature material for vulcanised rubber moulding. Resistant to temperatures to to 160 C / 320 F. FusionGRAY offers excellent surface detail making it perfect to use as a master model material for mould making. Vulcanised rubber moulds RTV moulds Jewellery design validation. $265 p/l Technical Data COLOR GLASS TRANSITION TEMPERATURE DARK GRAY 160 C / 320 F

7