VALOX Resin 451E Europe-Africa-Middle East: COMMERCIAL

Transcription

1 VALOX 451E is 20% glass reinforced, flame retardant PBT injection moulding resin. MECHANICAL Tensile Stress, yld, Type I, 5 mm/min 110 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 110 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 2 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 2 % ASTM D 638 Tensile Modulus, 5 mm/min 7900 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 154 MPa ASTM D 790 Flexural Stress, brk, 1.3 mm/min, 50 mm span 154 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 6100 MPa ASTM D 790 Tensile Stress, yield, 5 mm/min 110 MPa ISO 527 Tensile Stress, break, 5 mm/min 110 MPa ISO 527 Tensile Strain, yield, 5 mm/min 2 % ISO 527 Tensile Strain, break, 5 mm/min 2 % ISO 527 Tensile Modulus, 1 mm/min 8000 MPa ISO 527 Flexural Stress, yield, 2 mm/min 160 MPa ISO 178 Flexural Stress, break, 2 mm/min 160 MPa ISO 178 Flexural Strain, break, 2 mm/min 3 % ISO 178 Flexural Modulus, 2 mm/min 6600 MPa ISO 178 Hardness, H358/ MPa ISO Hardness, Rockwell R ISO IMPACT Charpy Impact, unnotched, 23 C 30 kj/m² ISO 179/2C Charpy Impact, unnotched, -30 C 28 kj/m² ISO 179/2C 2014 Saudi Basic Industries Corporation (SABIC).

2 IMPACT Izod Impact, unnotched, 23 C 350 J/m ASTM D 4812 Izod Impact, unnotched, -30 C 320 J/m ASTM D 4812 Izod Impact, notched, 23 C 60 J/m ASTM D 256 Izod Impact, notched, 0 C 60 J/m ASTM D 256 Izod Impact, notched, -30 C 60 J/m ASTM D 256 Instrumented Impact Total Energy, 23 C 6 J ASTM D 3763 Izod Impact, unnotched 80*10*4 +23 C 25 kj/m² ISO 180/1U Izod Impact, unnotched 80*10*4-30 C 25 kj/m² ISO 180/1U Izod Impact, notched 80*10*4 +23 C 6 kj/m² ISO 180/1A Izod Impact, notched 80*10*4 0 C 6 kj/m² ISO 180/1A Izod Impact, notched 80*10*4-30 C 6 kj/m² ISO 180/1A Charpy 23 C, V-notch Edgew 80*10*4 sp=62mm 7 kj/m² ISO 179/1eA Charpy Impact, notched, 23 C 7 kj/m² ISO 179/2C Charpy -30 C, V-notch Edgew 80*10*4 sp=62mm 5 kj/m² ISO 179/1eA Charpy Impact, notched, -30 C 7 kj/m² ISO 179/2C Charpy 23 C, Unnotch Edgew 80*10*4 sp=62mm 35 kj/m² ISO 179/1eU Charpy -30 C, Unnotch Edgew 80*10*4 sp=62mm 45 kj/m² ISO 179/1eU THERMAL Vicat Softening Temp, Rate A/ C ASTM D 1525 Vicat Softening Temp, Rate B/ C ASTM D 1525 HDT, 0.45 MPa, 3.2 mm, unannealed 219 C ASTM D 648 HDT, 1.82 MPa, 3.2mm, unannealed 200 C ASTM D 648 CTE, -40 C to 40 C, flow 3.09E-05 1/ C ASTM E 831 CTE, -40 C to 40 C, xflow 9.26E-05 1/ C ASTM E 831

3 THERMAL CTE, -40 C to 40 C, flow 2.61E-05 1/ C ISO CTE, -40 C to 40 C, xflow 6.96E-05 1/ C ISO CTE, 23 C to 150 C, flow 2.38E-05 1/ C ISO CTE, 23 C to 150 C, xflow 1.6E-04 1/ C ISO Ball Pressure Test, 125 C +/- 2 C PASSES - IEC Vicat Softening Temp, Rate A/ C ISO 306 Vicat Softening Temp, Rate B/ C ISO 306 Vicat Softening Temp, Rate B/ C ISO 306 HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 219 C ISO 75/Bf HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 200 C ISO 75/Af Relative Temp Index, Elec 120 C UL 746B Relative Temp Index, Mech w/impact 120 C UL 746B Relative Temp Index, Mech w/o impact 140 C UL 746B PHYSICAL Specific Gravity ASTM D 792 Specific Volume 0.65 cm³/g ASTM D 792 Filler Content 20 % ASTM D 229 Mold Shrinkage on Tensile Bar, flow (2) (5) % SABIC Method Mold Shrinkage, flow, 3.2 mm (5) % SABIC Method Mold Shrinkage on Tensile Bar, xflow (2) (5) % SABIC Method Mold Shrinkage, xflow, 3.2 mm (5) % SABIC Method Melt Flow Rate, 250 C/2.16 kgf 17 g/10 min ASTM D 1238 Melt Flow Rate, 266 C/5.0 kgf 110 g/10 min ASTM D 1238 Density 1.54 g/cm³ ISO 1183 Water Absorption, (23 C/sat) 0.27 % ISO 62 Moisture Absorption (23 C / 50% RH) 0.08 % ISO 62 Melt Volume Rate, MVR at 250 C/2.16 kg 12 cm³/10 min ISO 1133

4 PHYSICAL Melt Volume Rate, MVR at 250 C/5.0 kg 55 cm³/10 min ISO 1133 Melt Volume Rate, MVR at 265 C/5.0 kg 85 cm³/10 min ISO 1133 Melt Viscosity, 260 C, 1500 sec Pa-s ISO ELECTRICAL Volume Resistivity >1.E+15 Ohm-cm ASTM D 257 Volume Resistivity >1.E+15 Ohm-cm IEC Surface Resistivity, ROA >1.E+15 Ohm IEC Dielectric Strength, in oil, 0.8 mm 22 kv/mm IEC Dielectric Strength, in oil, 1.6 mm 21 kv/mm IEC Dielectric Strength, in oil, 3.2 mm 15 kv/mm IEC Relative Permittivity, 1 MHz IEC Dissipation Factor, 50/60 Hz IEC Dissipation Factor, 1 MHz IEC Comparative Tracking Index 175 V IEC Relative Permittivity, 50/60 Hz IEC FLAME CHARACTERISTICS UL Recognized, 94V-0 Flame Class Rating (3) 0.71 mm UL 94 UL Recognized, 94-5VA Rating (3) 2.3 mm UL 94 Glow Wire Flammability Index 960 C, passes at 1 mm IEC Oxygen Index (LOI) 30 % ISO 4589

5 PROCESSING PARAMETERS TYPICAL VALUE Unit Injection Molding Drying Temperature C Drying Time 2-4 hrs Maximum Moisture Content 0.02 % Melt Temperature C Nozzle Temperature C Front - Zone 3 Temperature C Middle - Zone 2 Temperature C Rear - Zone 1 Temperature C Hopper Temperature C Mold Temperature C

6